Farklı aşındırma ve kumlama protokollerinin fiberle güçlendirilmiş kompozit materyalinin eğilme dayanımına etkisi
Effect of different grinding and air-abrasion protocols on the flexural strength of fiber-reinforced composite material
- Tez No: 974283
- Danışmanlar: DOÇ. DR. YENER OKUTAN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD/CAM, Hava aşındırma, Mikroskopi-elektron taramalı, Protetik diş tedavisi, Yapay yaşlandırma, Yüzey pürüzlülüğü, İki eksenli eğilme, CAD/CAM, Air abrasion, Microscopy-electron scanning, Prosthetic dental treatment, Artificial aging, Surface roughness, Biaxial bending
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Aydın Adnan Menderes Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı farklı tungsten karbit frezler kullanılarak gerçekleştirilen aşındırma ile farklı tane boyutlarına ve basınç seviyelerine sahip kumlama işlemlerinin fiberle güçlendirilmiş kompozit materyalin yüzey pürüzlülüğü (Ra) ve eğilme dayanımı üzerindeki etkisini değerlendirmektir. Gereç ve Yöntem: Toplam 150 disk şekilli örnek CAD/CAM kullanılarak üretildi. Örnekler kırmızı (K) ve mavi (M) bantlı tungsten karbit frez ile aşındırılmasına, 50 ve 110 µm alüminyum oksit ile 1,5 ve 2 bar basınç altında kumlanmasına ve bu işlemlerin kombine uygulanmasına göre 15 gruba ayrıldı: Kontrol, (50-1,5), (50-2), (110-1,5), (110-2), K, M, (K50-1,5), (K50-2), (K110-1,5), (K110-2), (M50-1,5), (M50-2), (M110-1,5), (M110-2). Örneklerin tümü 5000 termal siklus uygulanarak yaşlandırıldı. Ra değerleri bir profilometre kullanılarak ölçüldü. Her gruptan ilave birer örnek taramalı elektron mikroskobu ile incelendi. Biaksiyel eğilme dayanımı verileri üniversal test cihazı kullanılarak elde edildi. İstatistiksel analizler için tek yönlü ANOVA, Tukey HSD, Tamhane T2 testleri ve Weibull analizi uygulandı. Bulgular: Kontrol, K ve M gruplarının Ra değerleri istatistiksel olarak benzerdir (p>0,05). Kumlama yapılan tüm gruplarda kumlama yapılmayan gruplara göre önemli derecede yüksek Ra değerleri bulunmuştur (p<0,05). Kumlama uygulanmayan gruplar, 110 µm ile kumlama yapılan gruplara göre daha yüksek eğilme dayanımı değerleri göstermiştir (p<0,05). Kontrol, K ve M grupları arasında eğilme dayanımı açısından anlamlı fark yoktur (p>0,05). Sonuçlar: Fiberle güçlendirilmiş kompozit materyali için yüzey işlemi olarak tungsten karbit frezle aşındırma ve 50 µm alüminyum oksit ile kumlama önerilebilir. 110 µm alüminyum oksit ile yapılan kumlama işlemi fiberle güçlendirilmiş kompozit materyalin mekanik özelliklerini olumsuz etkileyebilir.
Özet (Çeviri)
Aim: The aim of this study was to evaluate the effects of grinding performed with different tungsten carbide burs and air-abrasion with different particle sizes and pressure levels on the surface roughness (Ra) and flexural strength of a fiber-reinforced composite material. Materials and Methods: A total of 150 disc-shaped specimens were fabricated using CAD/CAM. The samples were divided into 15 groups according to grinding with red (R) and blue (B) band tungsten carbide bur, air-abrasion with 50 and 110 µm aluminum oxide at 1.5 and 2 bar pressure, and the combined application of these procedures: Control, (50-1.5), (50-2), (110-1.5), (110-2), R, B, (R50-1.5), (R50-2), (R110-1.5), (R110-2), (B50-1.5), (B50-2), (B110-1.5), (B110-2). All specimens were aged by 5,000 thermal cycles. Ra was measured using a profilometer. One additional specimen per group was examined under a scanning electron microscope. Biaxial flexural strength data were obtained using a universal testing machine. One-way ANOVA, Tukey HSD, Tamhane T2 tests, and Weibull analysis were performed for statistical analyses. Results: The Ra values of control, R, and B groups were statistically similar (p>0.05). All groups subjected to air-abrasion showed significantly higher Ra values compared to non-air-abraded groups (p<0.05). Non-air-abraded specimens demonstrated significantly higher flexural strength than those air-abraded with 110 µm particles (p<0.05). No statistically significant differences in flexural strength were observed among the control, R, and B groups (p>0.05). Conclusion: Grinding with tungsten carbide burs and air-abrasion with 50 µm aluminum oxide particles may be recommended as surface treatment for fiber-reinforced composite material. Air-abrasion with 110 µm aluminum oxide particles may adversely affect the mechanical properties of fiber-reinforced composite material.
Benzer Tezler
- Rezin kompozit restorasyon tamirinde farklı tedavi protokollerinin uygulanmasının makaslama bağlanma dayanımı üzerine etkisi
The effect of application of different treatment protocols on shear bond strength in resin composite restoration repair
AYŞENUR ÇELİK
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiGazi ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. OYA BALA
- İmmediat dentin kapama ve geçici uygulama teknikleri sonrası farklı yüzey temizleme protokollerinin bağlanma dayanımına etkisinin in vitro değerlendirilmesi
In vitro evaluation of the effect of different surface cleaning protocols on bond strenght after immediate dentin sealing and temporary application techniques
SİMAY KOCAAĞA
Doktora
Türkçe
2025
Diş HekimliğiMarmara ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. YILMAZ UMUT ASLAN
- Farklı kumlama prosedürlerinin zirkonya ve rezin bazlı CAD/CAM materyallerinin aşınma ve yüzey özellikleri üzerine etkisi
The effect of different sandblasting procedures on the wear and surface properties of zirconia and resin based CAD/CAM materials
SEVAL BAŞPINAR ALPER
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiKocaeli ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. NESLİHAN TEKÇE
- Farklı tip dolgu malzemeli yapıştırıcılar ile yapıştırılan alüminyum alaşım ve karbon fiber kompozitlerin mekanik özelliklerinin belirlenmesi
Determination of the mechanical properties of aluminum alloy and carbon fiber composites bonded with different types of sealant adhesives
BURCU ÖZTÜRK
Yüksek Lisans
Türkçe
2021
Makine MühendisliğiKafkas ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ BENEK HAMAMCI
- Farklı yüzey işlemlerinin ve yapay yaşlandırmanın y-tzp zirkonya seramiklerin faz dönüşümüne ve eğilme dayanımına etkisi
Effect of different surface treatments and artificial aging on the phase transformation and flexural strength of y-tzp zirconia ceramics
YENER OKUTAN
Doktora
Türkçe
2015
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. MÜNİR TOLGA YÜCEL