Isı presleme tekniği ve adeziv sistemlerin PEEK dayanakların titanyum ve krom-kobalt tabanlarla bağlantı dayanımına etkisi
Effect of heat-pressing technique and adhesive systems on the bond strength of PEEK abutments with titanium and chromium-cobalt bases
- Tez No: 971920
- Danışmanlar: PROF. DR. VOLKAN ŞAHİN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental destekler, Dental protez-implant destekli, Sıcak presleme, Çekme dayanım testi, Dental abutments, Dental prosthesis-implant supported, Hot pressing, Tensile strength test
- Yıl: 2025
- Dil: Türkçe
- Üniversite: Kırıkkale Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı farklı adeziv sistemlerin ve ısı ile presleme tekniğinin PEEK dayanakların titanyum ve krom-kobalt tabanlarla arasındaki bağlanma dayanımına etkisinin değerlendirilmesidir. Bu çalışmada, 90 adet PEEK hibrit dayanak kullanılmıştır. Hibrit dayanaklar, taban materyallerine göre iki gruba ayrılmıştır: titanyum (Ti-base) dayanaklar (n =45) ve krom-kobalt (Cr-Co base) dayanaklar (n = 45). Titanyum dayanaklar üretici firma tarafından sağlanmış olup; çapları 4,5 mm, dişeti yüksekliği 1 mm ve boyu 5 mm'dir. Cr-Co dayanaklar, üretici firma tarafından sağlanan titanyum dayanaklara ait dijital tasarım dosyaları temel alınarak, dayanakların yüzeylerine 0,3 mm genişliğinde ve 0,15 mm derinliğinde gözenekler eklenerek tasarlanmıştır ve eklemeli yöntem ile üretilmiştir. Toplam 60 adet PEEK dayanak, her biri 11 × 6 × 6 mm boyutlarında olacak şekilde frezeleme yöntemi ile BİOHPP bloklardan üretilmiştir. Bu örnekler, kullanılan taban materyaline (titanyum ve Cr-Co) ve uygulanan primer ile rezin siman kombinasyonuna (MKZ primer-DTK adeziv ve Monobond Plus-Multilink Hybrid Abutment) göre dört gruba ayrılmıştır (n = 15). Buna ek olarak, ısı ile presleme tekniği kullanılarak üretilen 30 adet PEEK dayanak, titanyum ve Cr-Co tabanlarla birleştirilmiştir (n = 15). Tüm örneklere evrensel test cihazı ile 1 mm/dk hızında çekme testi uygulanmıştır; elde edilen bağlanma dayanımı değerleri MegaPascal (MPa) cinsinden kaydedilmiştir. Gruplar arasındaki istatistiksel farkları değerlendirmek amacıyla iki yönlü robust ANOVA testi uygulanmış, anlamlı fark gözlenen durumlarda Bonferroni düzeltmesi ile ikili karşılaştırmalar yapılmıştır. İki yönlü robust ANOVA testine göre, kullanılan yöntem (p<0,001) ve yöntem–taban etkileşimi (p<0,001) bağlanma dayanımı üzerinde anlamlı bir etki göstermiştir. Isı ile presleme tekniği (109,35 MPa (65,33–218,6)), rezin siman kullanılan gruplara (MKZ–DTK: 28,25 MPa (18,65–66,84); MB-ML: 29,57 MPa (21,01–63,27)) (p<0,001) kıyasla daha yüksek bağlanma dayanımı değerleri göstermiştir. En yüksek bağlanma dayanımı, Cr-Co taban ile ısı ile presleme tekniğinin birlikte kullanıldığı grupta elde edilmiştir (124,46 MPa (85,41–218,6)) (p<0,001). Siman kullanılan gruplarda, titanyum dayanaklar ile elde edilen bağlanma dayanımı (MKZ-DTK 35,41 MPa (19,02–66,84); MB-ML 34,71 MPa (22,44–63,27)), Cr-Co dayanaklara (MKZ-DTK 26,2 MPa (18,65–32,5); MB-ML 28,17 MPa (21,01–41,62)) göre daha yüksek bulunmuştur. Bağlantı başarısızlıkları, siman kullanılan gruplarda genellikle PEEK dayanaklar ile siman arasında görülürken, Cr-Co presleme grubunda 12 örnekte koheziv, 3 örnekte ise karma kopma tipi gözlenmiştir.
Özet (Çeviri)
The aim of this study is to evaluate the effect of different adhesive techniques and heat pressing technique on the bonding strength between PEEK abutments and titanium and chromium-cobalt (Cr-Co) bases. In this study, 90 hybrid abutments were used. Hybrid abutments were divided into two groups according to their base materials: titanium (titanium-base) abutments (n = 45) and cobalt-chromium (Cr-Co base) abutments (n = 45). Titanium abutments are provided by the manufacturer (Dentcon, Turkey) and have a diameter of 4.5 mm, a gingival height of 1 mm, and length of 5 mm. Cr-Co abutments are designed based on digital design files provided by the manufacturer for titanium abutments, with 0.3 mm wide and 0.15 mm deep pores added to the surface of the titanium base abutments, and are produced using the additive manufacturing method (SLM). A total of 60 PEEK abutments, each measuring 11 × 6 × 6 mm, were produced from BioHPP blocks using a milling method. These samples were divided into four groups based on the base material used (titanium and Cr-Co) and the primer and resin cement combination applied (MKZ-DTK and Monobond Plus-Multilink Hybrid Abutment) (n = 15). In addition, 30 PEEK abutments produced using a heat pressing technique were combined with titanium and Cr-Co bases (n = 15). All samples were subjected to a tensile test using a universal testing machine at a crosshead speed of 1 mm/min; the resulting bond strength values were recorded in MegaPascal (MPa). A two-way robust ANOVA test was applied to evaluate the statistical differences between the groups, and pairwise comparisons were made with Bonferroni correction. According to the two-way robust ANOVA test, the method used (p<0,001) and the method-base interaction (p<0,001) had a significant effect on the bond strength. The heat pressing technique (109,35 MPa (65,33–218,6)) demonstrated higher bond strength values compared to the groups using resin cement (MKZ–DTK: 28,25 MPa (18,65–66,84); MB-ML: 29,57 MPa (21,01–63,27)) (p<0,001). The highest bond strength was observed in the group where the heat pressing technique was used in combination with a Cr-Co base (124,46 MPa (85,41–218,6)) (p<0,001). In the groups where cement was used, the bond strength obtained with titanium abutments (MKZ-DTK 35,41 MPa (19,02–66,84); MB-ML 34,71 MPa (22,44–63,27)) was found to be higher than that obtained with Cr-Co abutments (MKZ-DTK 26,2 MPa (18,65–32,5); MB-ML 28,17 MPa (21,01–41,62)). Bonding failures occurred between the cement and PEEK abutments in the groups where cement was used, while cohesive failure was observed in 12 samples and mixed failure in 3 samples in the Cr-Co injection group.
Benzer Tezler
- Zirkonyum dioksit alt yapı üzerine uygulanan farklı yüzey işlemlerinin ve tekrarlanan fırınlamanın üst yapı porseleninin bağlanma dayanımına etkisinin in-vitro olarak incelenmesi
In-vitro evaluation of the effect of different surface treatments and repeated firing on their bond strength to two veneer ceramics to zirconia
SİNEM SAVRAN ÇAKIR
Doktora
Türkçe
2011
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. BÜLENT ŞERMET
- İzolasyon malzemesi geliştirilmesi ve ısıl iletkenlik ölçümü
Insulation material development and thermal conductivity measurement
AHMET KORKMAZ
Yüksek Lisans
Türkçe
2021
Metalurji MühendisliğiYıldız Teknik ÜniversitesiGemi İnşaatı ve Gemi Makineleri Mühendisliği Ana Bilim Dalı
DOÇ. DR. YÜKSEL PALACI
DR. ÖĞR. ÜYESİ HAYDAR BAYAR
- Elmas katkılı kompozit frez üretimi ve mekanik özelliklerinin belirlenmesi
Fabrication and mechanical characterization of diamond-reinforced composite burs
EMİN ORHUN BAŞTEKELİ
Doktora
Türkçe
2025
Makine Mühendisliğiİstanbul Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ HACI ABDULLAH TAŞDEMİR
- Nadir toprak element katkılı ekonomik Beta-SiAlON fosfor tozlarının sentezi ve karakterizasyonu
The synthesis and characterization of rare-earth doped cost effective Beta-SiAlON phosphor powders
PELİN ÇAĞIM TOKAT
Yüksek Lisans
Türkçe
2015
Seramik MühendisliğiDumlupınar ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. HİLMİ YURDAKUL
PROF. DR. SERVET TURAN
- Toz metalürjisi yöntemi ile AA6061/TiB2/grafen hibrid kompozit malzemelerin üretimi, mikroyapı ve mekanik özelliklerinin araştırılması
Production of AA6061/TiB2/graphene hybrid composite materials by powder metallurgy method and investigation of microstructure and mechanical properties
EYÜP KUTAY ÇAKIROĞLU
Yüksek Lisans
Türkçe
2023
Metalurji MühendisliğiGazi ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. RAMAZAN ÇITAK