Metallographic and mechanical studies on plain carbon and vanadium containing dual phase structural steels
Başlık çevirisi mevcut değil.
- Tez No: 9682
- Danışmanlar: PROF. DR. ERDOĞAN TEKİN
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Metalografi, yapı çeliği, ikili faz sıcaklığı. Bilim dalı sayısal kodu 604.02.07 vi, Karbon, Tavlama, Vanadyum, Çelik-metal, Metallography, structural steel, Intercrltlcal annealing temperature. Scientific code 604.02.07 1v, Carbon, Annealing, Vanadium, Steel-metal
- Yıl: 1990
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
YALIN KARBON VE VANADYUM KATILIMLI ÇİFT FAZLI YAPI ÇELİKLERİNİN METALOGRAFİK VE MEKANİK ÇALIŞMASI BOLVADİN, Hakan Mühendislik Fakültesi Metalürji Müh.Bölümü, Yüksek Lisans Tezi Tez Yöneticisi: Prof.Dr.Erdoğan Tekin 87 sayfa, Mayıs 1990 ÖZET Bu çalışmada ikili bölgeden su verilme, menevişlerine işlemlerinin ve alaşım element eklenmesinin çift fazlı yapı çeliklerinin mekanik ve içyapı özelliklerine olan etkisi incelendi. İçyapı özelliklerinin araştırılmasında optik mikroskop, tarama ve geçirimli elektron mikroskopları kullanıldı. Çelik numunelerine çelik çarpma ve sertlik deneyleri uygulandı.Karbon içerikleri %0.23-%37 arasında değişen yapı çeliklerine 740°C-770°C arasında 30 dakika bekletildikten sonra su ile suverildi. Hacimsel martensit yüzdesinin ikili bölge sıcaklığından büyük ölçüde etkilendiği ve sıcaklıktaki artış sonucunda hacimsel martensit yüzdesinin arttığı gözlendi. Mekanik deney sonuçları çekme, çarpma ve sertlik gibi mekanik özelliklerin hacimsel martensit yüzdesinden etkilendiğini gösterdi. Ayrıca menevişleme işleminin süneklik özelliğini arttırdığı gözlendi.
Özet (Çeviri)
M ET ALLOGRAPHS AND MECHANICAL STUDIES ON PLAIN CARBON AND VANADIUM CONTAINING DUAL PHASE STRUCTURAL STEELS Bolvadin, Hakan Faculty of Engineering Metallurgical Eng.Dept., M.S.Thesis Supervisor: Prof.Dr.Erdoğan Tekin 87 pages. May 1990 ABSTRACT In this study the effect of intercrltical annealing temperature and tempering on the microstructure and mechanical properties of some structural dual phase steels were Investigated. For metal lographic studies optical microscopy, scanning electron microscopy and transmission electron microscopy were used. Mechanical tests including tensile, impact and hardness tests were performed. mStructural steels that have a carbon content between 0.238-0.375? were heat treated at 740°C-770°C for 30 minutes. It was observed that the martensite volume fraction Is greatly Influenced from the Intercrltlcal annealing temperature, It Increases as the Intercrltical annealing temperature Increases. The results of the mechanical tests show that mechanical properties such as hardness, tensile and Impact strength of the specimens are generally affected from the martensite volume fraction. It is also found that tempering improves ductility properties of the specimens.
Benzer Tezler
- Tel çekme işleminde bakırın ve bakır oksit inklüzyonlarının deformasyon davranışı
Deformation behaviour during drawing of copper wires and copper oxide inclusions
MUSTAFA M. ARIKAN
- Nikelli ve nikelsiz altın alaşımlarının geniş bir bileşim aralığında fiziksel, kimyasal, mekanik ve alerjen özelliklerinin belirlenmesi
The Determination of physical, chemical, mechanical and allergen properties of nickel containing and nickel free gold alloys of a wide range
MESUT EMRE
- Ötektik altı Al-Si alaşımlarında 5/1 tibör ön alaşımı ile tane inceltme işleminin sertlik ve mikroyapı üzerindeki etkisinin belirlenmesi
The effects of grain refining conditions using 5/1 tibor alloy upon the microstructure and hardness of hypoevtectic Al-Si alloys
RASİM ERDOĞAN
- Az alaşımlı ve karbon çeliklerinde borlama ile yüzeye kaplanan borürlerin bazı özelliklerinin tesbiti
Determination of some material properties of borides coated on the surfaces of low alloy and carbon steels
CUMA BİNDAL
- Yüksek azot içeren çökeltme ile sertleştirilebilir ostenitik paslanmaz çelikler
Precipitation hardening austenitic stainless steels
GÜLHAN TÜYSÜZ
Yüksek Lisans
Türkçe
1999
Makine Mühendisliğiİstanbul Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. MEHMET DEMİRKOL