Ceş 0,50 olan yapı çeliğinin kaynak kabiliyetinin incelenmesi
The welding ability of steels having 0,5 C in their structures
- Tez No: 93539
- Danışmanlar: YRD. DOÇ. DR. BEHÇET GÜLENÇ
- Tez Türü: Yüksek Lisans
- Konular: Eğitim ve Öğretim, Metalurji Mühendisliği, Education and Training, Metallurgical Engineering
- Anahtar Kelimeler: Orta karbonlu çeliklerin kaynağı, kaynak metali. mikroyapı. Sayla Adedi : 152, Ark kaynağı, Isıl işlem, Kaynak banyosu, Kaynak kabiliyeti, Çelik-metal, Welding of steels with middle-carbon, welding metal, microstructure. Page Numbers : 152 Adviser : Yrd.Doç.Dr.Behçet GÜLENÇ, Arc welding, Heat treatment, Weld puddle, Welding ability, Steel-metal
- Yıl: 2000
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Ceş 0,50 OLAN YAPI ÇELİĞİNİN KAYNAK KABİLİYETİNİN İNCELENMESİ (YÜKSEK LİSANS TEZİ) İsmail BAYRAM GAZİ ÜNİVERSİTESİ FEN BİLİMLERİ ENSTİTÜSÜ MART 2000 ÖZET Bu çalışmada 0,50 karbonlu çeliğin ısıl işlem metodu uygulanılarak bazik elektrotlar kullanımı ile kaynaklanabilirliği mikroyapı ve mekanik özellikleri bakımından araştırılmış ve incelenmiştir. Deneyde kullanılan elektrotlar 250°C"de 2 saat kurutulduktan sonra, 125°C'de tutularak 4 saat süresinde tüketildi. Kaynaklı yapının (metalin) akma, çekme, uzama - % -, çentik darbe dayanımı ve sertlik değerleri saptanmıştır. Kaynak işlemine göre ısı arttıkça kaynaklanabilirliğin arttığının gözlemlendiğini olumlu sonuçlar vermiştir. Optik mikroskop ile yapılan mikroyapı çalışmalarında ısıya bağıl olarak 0.5 karbonlu çeliğin tanecik yapısı incelenmiştir. Bilim kodu : 225.04.01
Özet (Çeviri)
11 THE WELDING ABILITY OF STEELS HAVING 0,5C INTHEÎîr STRUCTURES (HIGH LICENSE THESIS) Ismail BAYRAM GAZİ UNIVERSITY INSTITUTE OF SCIENCE AND TECHNOLOGY MARCH 2000 ABSTRACT In this study, the ability of having been welded of steell having 0,5 C in its structure had been researched and examined with the help of“bazik electrodes”by using the method of thermal operation interms of microstructure and mechanic characteristics. After keeping the electrodes used in the experiment under the heat of 250°C for 2 hours, they had been used up for 4 hours under the heat of 150°C. The leaking, pulling, getting longer, notch stroke resistance and hardness values of welded structure were determined. According to the operation of welding we can see increase in the ability of having been welded as the heat increases. Also the mechanic characteristics of welded structures had given the positive results in the experiment. Moreover, in microstructure studies made by optic microscobe, particle structure of steel with 0.5 according to the heating was ewamined. Science Code : 225.04.01
Benzer Tezler
- Bazı makarnalık buğday çeşitlerinin (triticum turgidum var. durum L.) Bursa koşullarında verim ve adaptasyon yeteneği üzerinde araştırmaları
Başlık çevirisi yok
MEHMET AYÇİÇEK
Yüksek Lisans
Türkçe
1989
ZiraatUludağ ÜniversitesiTarla Bitkileri Ana Bilim Dalı
PROF. DR. NEVZAT YÜRÜR
- Alain Robbe-Grillet et la litterature objective: Les Gommes (1953), le Voyeur (1955) et la Jalousie (1957)
Alain Robbe-Grillet ve nesnel edebiyat: Silgiler (1953), Gözetleyici (1955), Kıskançlık/perde (1957)
NAZİK GÜLBEYAZ
Yüksek Lisans
Fransızca
2000
Fransız Dili ve EdebiyatıÇukurova ÜniversitesiFransız Dili ve Edebiyatı Ana Bilim Dalı
PROF. DR. EROL KAYRA
- Fosfojipsiyumdan mikrobiyel proses ile hidrojen sülfür (H2S) eldesi
Microbial conversion of hydrous calcium sulfate to hydrogen sulfide
CÜNEYT GÖKTUĞ DELALOĞLU
- Ege bölgesi keçi liflerinin bazı önemli fiziksel, kimyasal özellikleri ve değerlendirme imkanları
Başlık çevirisi yok
NİLÜFER ERDEM
Doktora
Türkçe
1985
Tekstil ve Tekstil MühendisliğiEge ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
PROF. DR. GÜLSEREN YAZICIOĞLU
- Trakya Bölgesi şaraplık üzüm üretim ekonomisi ve pazarlaması üzerine bir araştırma
Başlık çevirisi yok
NALAN YÜKSEL DELİCE