Maksillofasiyal protezlerin yapımında kullanılan silikonların polimerizasyon ve üç boyutlu yazıcı yöntemleri ile üretilmiş farklı rezin altyapı malzemelerine bağlantı dayanımının incelenmesi
Peel bond strength of silicones used in extraoral maxillofacial prostheses from different resin substructures
- Tez No: 911338
- Danışmanlar: DR. ÖĞR. ÜYESİ TUĞGEN MERSİN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Maksillofasiyal protez, silikon elastomerler, dijital teknoloji, yapay yaşlandırma, soyulma testi, Maxillofacial prosthesis, silicone elastomers, digital technology, artificial aging, peel test
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Sağlık Bilimleri Üniversitesi
- Enstitü: Gülhane Diş Hekimliği Fakültesi (ankara)
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Ekstraoral maksillofasiyal protezler, proteze rijit destek sağlayan akrilik altyapının üzerini kaplayan, yumuşak doku görünümünde silikon elastomerlerden oluşur. Silikon elastomer-altyapı arasındaki bağlantı protezin başarısında önemlidir. Çalışmada farklı polimerizasyon ve üç boyutlu yazıcı(3B) ile üretilmiş yedi rezin altyapının silikon elastomere bağlantısı, yapay yaşlandırmanın etkisi incelendi. Altyapı üretiminde güncel dijital malzemelerin konvansiyonel malzemelere alternatif kullanımının araştırılması amaçlandı. Gereç ve Yöntem: Örneklerin hazırlanmasında kimyasal polimerize şeffaf akrilik rezin(KPSA), ısı ile polimerize şeffaf(IPSA) ve pembe akrilik rezin(IPPA), 3B cerrahi kılavuz rezini(CKR), kaide rezini(KR), polieterketonketon(PEKK), polietereterketon(PEEK) olmak üzere 7 farklı altyapı malzemesi, silikon elastomer kullanıldı. Her altyapı malzemesinden 10 adet, toplam 70 örnek ASTM-D903-98 standartlarına göre hazırlanarak yarısına soyulma testi yapıldı. Diğer yarısına yapay yaşlandırma sonrası soyulma testi yapıldı. Ölçülen bağlantı dayanımı verisi iki yönlü varyans analizi ve post hoc Bonferroni testi ile değerlendirildi. Bağlantı yüzeyleri konfokal mikroskopta incelendi. Bulgular: Soyulma testi sonrası ortalama bağlantı dayanımı (N/mm) örneklerde sırasıyla IPSA (7,1600), IPPA (6,5108), KR (6,4294), KPSA (5,7826), CKR (5,3783), PEEK (0,9556), PEKK (0,1912), YCKR (3,1828), YKR (2,7568), YIPPA (2,3062), YIPSA (0,2658), YKPSA (0,1336), YPEEK (0,0797), YPEKK (0,0532) ölçüldü. Bağlantı yüzeylerinde adeziv, karışık, koheziv başarısızlık gözlendi. İki yönlü varyans analizi sonucuna göre farklı altyapı kullanımının, yapay yaşlandırma uygulanmasının ve bu ikisi arasındaki etkileşimin bağlantı dayanımına etkisi anlamlı bulundu(sırasıyla p<0.001, p<0.001, p<0.001). Bağlantı dayanımı KPSA, IPSA, IPPA, CKR, KR gruplarında benzer bulundu(p>0.05). PEEK, PEKK gruplarında benzer(p>0.05) ancak diğer gruplara göre istatistiksel olarak anlamlı düzeyde düşüktü(p<0.05). Bağlantı dayanımı YCKR, YKR gruplarında YKPSA, YIPSA, YPEKK, YPEEK gruplarından anlamlı düzeyde yüksek ölçüldü(p<0.05). PEKK, PEEK dışındaki altyapı türlerinde yapay yaşlandırmanın bağlantı dayanımını düşürdüğü görüldü(p<0.05). Sonuç: Silikon elastomer-altyapı bağlantısı altyapının farklı polimerizasyon veya 3B üretilmesinden ve yapay yaşlandırma uygulanmasından etkilendi. 3B üretilen CKR ve KR'nin maksillofasiyal protezlerde altyapı malzemesi olarak kullanımı avantaj sağlayabilir. 3B üretilen PEEK ve PEKK'in maksillofasiyal protezlerde altyapı olarak kullanılabilmeleri için bağlantı dayanımını geliştirmeye yönelik ileri çalışmalara ihtiyaç vardır.
Özet (Çeviri)
Aim: Extraoral maxillofacial prostheses consist of a rigid acrylic substructure providing support to the silicone elastomer. The bond between the silicone elastomer and the substructure is critical for success. In this study, the bond strength between silicone elastomer and seven resin substructures, produced with different polymerisation and three-dimensional printing (3D) methods, and the effect of artificial aging were investigated. It was aimed to investigate the use of current digital materials as an alternative to conventional materials in substructure production. Materials and Method: Seven different substructure materials, including chemically polymerised clear acrylic resin(KPSA), heat polymerised clear acrylic resin(IPSA) and pink acrylic resin(IPPA), 3D surgical guide resin (CKR), Denture base resin(KR), polyetheretherketone (PEKK), polyetheretheretherketone (PEEK) and silicone elastomer were used to prepare samples. A total of 70 samples, 10 of each material, were prepared according to ASTM-D903-98 standards and peel test was performed on half of them. The other half was subjected to peel test following artificial aging. The calculated peel bond strength data were analysed by two-way analysis of variance and post hoc Bonferroni test. The bond surfaces were examined under confocal microscope. Results: The mean bond strength(N/mm) after the peel test was measured in the samples as IPSA (7.1600), IPPA (6.5108), KR (6.4294), KPSA (5.7826), CKR (5, 3783), PEEK (0.9556), PEKK (0.1912), YCKR (3.1828), YKR (2.7568), YIPPA (2.3062), YIPSA (0.2658), YKPSA (0.1336), YPEEK (0.0797), YPEKK (0.0532). Adhesive, mixed, cohesive failures were observed on the bonding surfaces. According to the results of two-way analysis of variance, the effect of using different substructures, applying artificial aging and the interaction between these two were found to be significant(p<0.001, p<0.001, p<0.001, p<0.001, respectively). The bond strength was similar in KPSA, IPSA, IPPA, CKR, KR groups(p>0.05). It was similar in PEEK, PEKK groups(p>0.05) but statistically significantly lower than the other groups(p<0.05). Bond strength was significantly higher in YCKR, YKR groups than YKPSA, YIPSA, YPEKK, YPEEK groups(p<0.05). Artificial aging decreased the bond strength in all substructure types except PEKK, PEEK(p<0.05). Conclusion: The silicone elastomer-substructure bond was affected by the fabrication of the substructure using different polymerization or 3D printing methods and the application of artificial aging. The use of 3D fabricated CKR and KR as substructure materials in maxillofacial prostheses may provide advantages. Further studies are needed to improve the bond strength of 3D fabricated PEEK and PEKK to use them as substructures in maxillofacial prostheses.
Benzer Tezler
- Yüksek performanslı polimerlerin maksillofasiyal silikon ile bağlantı dayanımının incelenmesi
Investigation of the bond strength between hi̇gh performance polymers and maxillofacial silicone
BENAN İLAYDA KARAMAN
Doktora
Türkçe
2021
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. MELTEM ÖZDEMİR KARATAŞ
DR. ÖĞR. ÜYESİ BURÇ İHSAN GENÇEL
- Ultraviyole koruyucu ilavesinin farklı maksillofasiyal silikonların mekanik özellikleri üzerine etkisi
Effect of ultraviolet protective addition on the mechanical properties of different maxillofacial silicones
NECLA KILIÇKAYA
Doktora
Türkçe
2021
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. SEÇİL NEMLİ
- Farklı nanopartikül ilavelerinin çene yüz protezlerinde kullanılan silikon elastomerin mekanik ve mikrobiyolojik özelliklerine etkilerinin araştırılması
Investigation of mechanical and microbiological effects of different nanoparticle additions on maxillo facial prostheses
GAMZE KARAMAN
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiFırat ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ EYYÜP ALTINTAŞ
- Postmenopozal osteoporoz hastalarında bifosfonatların mandibular radyomorfometrik indekslere ve kemik yoğunluğuna etkisi
The effect of bisphosphonates on mandibular radiomorphometric indeces and bone density in post-menopausal osteoporosis patients
SİNAN ATEŞ
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiDicle ÜniversitesiAğız, Diş ve Çene Cerrahisi Ana Bilim Dalı
PROF. DR. BELGİN GÜLSÜN
- Erzurum merkez ili ilkokul çocuklarında görülen dento-facial ve maxillo-facial anomalilerin görülme sıklıklarının incelenmesi
Başlık çevirisi yok
ZEYNEP ECE BİLGEN