Validating a test method to evaluate the adhesion force of electrospun nanofiber covered nitinol stents and evaluating the adhesion force of differently treated stents
Elektrospun nanofiber kaplanacak nitinol stentlerde yapışma durumunun değerlendirilmesi için yeni bir test metodu ve yapışmayı artırma yönteminin geliştirilmesi
- Tez No: 911336
- Danışmanlar: PROF. DR. OSMAN BABAARSLAN
- Tez Türü: Yüksek Lisans
- Konular: Tekstil ve Tekstil Mühendisliği, Textile and Textile Engineering
- Anahtar Kelimeler: Nitinol stentler, elektrospun nanolif, adezyon kuvveti, test yöntemi doğrulama, nitinol stents, electrospun nanofiber, adhesion force, test method validation
- Yıl: 2023
- Dil: İngilizce
- Üniversite: Çukurova Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Tekstil Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın temel amacı, örgülü yapılı nitinol stentin yüzeyi ile termoplastik poliüretan (TPU) elektrospun nanolifler arasındaki yapışma kuvveti araştırılmıştır. Ayrıca, farklı işlemlerin adezyon kuvveti üzerindeki etkisi araştırılmış ve adezyonu artıracak bir yöntem bulunmaya çalışılmıştır. TPU nanofiber kaplı stentlerin yapışma kuvvetini ölçmek için öncelikle farklı yüzey malzemeleri ve yapıştırıcılar kullanılarak bir yöntemin doğrulaması yapılmıştır. Bu test yöntemi doğrulamasından sonra, yapışma kuvveti ölçülmüştür. Daha sonra, farklı elektrospinning işlemleri, örgülü yapılar ve işlemler gibi yapışma kuvvetini değerlendirmek için farklı yaklaşımlar izlenmiştir. Doğrulama kısmında, 2D ve 3D yüzeylerin yapışma kuvvetlerinin oldukça tutarlı ve tekrarlanabilir olduğu gözlemlenmiştir. 2D ve 3D yapılı nanofiber kaplı stentler için benzer sonuçlar bulunmuştur. Farklı yaklaşımlar açısından, yatay elektroeğirme kurulumları ve daha yüksek iletme hızlarına sahip örgülü yapılar için daha yüksek yapışma kuvvetleri gözlemlenmiştir. Plazma işleminden sonra adezyon kuvvetleri 2 kat, ısıl işlemden sonra ise 1,5 kat artmıştır. Plazma ve ısıl işlemden sonra stentin ortalama yapışma kuvveti sırasıyla 41.8 cN ve 26.41 cN iken, işlem görmemiş referans stentin yapışma kuvveti 16.75 cN ölçülmüştür.
Özet (Çeviri)
The main objective of this study is to measure the adhesion force between braided structured nitinol stent's surface and thermoplastic polyurethane (TPU) electrospun nanofibers. Further, the influence of different treatments on the adhesion force should be investigated, and a method to enhance adhesion should be found. To measure the adhesion force of TPU nanofiber covered stents, first, a method was validated using different surface materials and adhesives. After that test method validation, the adhesion force is measured. Later, different approaches are followed to evaluate the adhesion force, such as different electrospinning processes, braided structures, and treatments. From the validation part, it has been observed that the adhesion forces of 2D and 3D surfaces are quite coherent and reproducible. Similar results have been found for 2D, and 3D structured nanofiber covered stents. In terms of different approaches, higher adhesion forces have been observed for horizontal electrospinning setups and braided structures with higher forwarding speeds. After plasma treatment, adhesion forces were increased by 2 times, while for heat treatment, it was increased by 1.5 times. The average adhesion force of the stent after plasma and heat treatment was 41.8 cN and 26.41 cN, respectively, while the reference stent without treatment measured 16.75 cN.
Benzer Tezler
- Investigating the effect of additives on the performance of non-stick coating films in composite structures
Kompozit yapılardaki yapışmaz kaplama filmlerinde katkı malzemelerinin performansa etkisinin incelenmesi
JABIR ISMAEILI
Doktora
İngilizce
2025
Kimya MühendisliğiEge ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. BİKEM ÖVEZ
- Toz metalurjı̇sı̇ ı̇le üretı̇len bir takım çelı̇ğinin kutu alüminyumlama yöntemiyle kaplanması
Pack aluminizing of a powder metallurgy tool steel
TARIK SEKBAN
Yüksek Lisans
Türkçe
2025
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MURAT BAYDOĞAN
- Politika duyarlı text-to-SQL ajanının postgresql satır düzeyi güvenlik (RLS) ile uygulamalı değerlendirilmesi
Applied evaluation of the policy-sensitive text-to-SQL agent with postgresql row level security (RLS)
ALI ATIA ALI KOUNDI
Yüksek Lisans
Türkçe
2026
Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve KontrolSakarya ÜniversitesiBilişim Sistemleri Mühendisliği Ana Bilim Dalı
PROF. DR. İSMAİL HAKKI CEDİMOĞLU
- Hastanelerde rol çatışması ve sosyal iklimin örgütsel sapma davranışına etkisi
Effect of role conflict and the social climate in hospitals on organizational deviation behavior
PERİHAN EREN BANA
Doktora
Türkçe
2019
Sağlık Kurumları YönetimiMarmara ÜniversitesiSağlık Yönetimi Ana Bilim Dalı
DOÇ. DR. ŞEVKİ BURAK BEKAROĞLU
- Farklı disiplinler ile ilişkilendirme bağlamında matematiksel modelleme etkinliklerinin geliştirilmesi ve uygulanması: Ortaokul öğrencileri örneklemesi
Development and implementation of mathematical modeling activities in the context of connecting with different disciplines: The sample of middle school students
ZÜLKÜF KILIÇ
Yüksek Lisans
Türkçe
2020
MatematikDicle ÜniversitesiMatematik ve Fen Bilimleri Eğitimi Ana Bilim Dalı
DOÇ. DR. KEMAL ÖZGEN