Three-dimensional failure analysis of pin jointed composite laminates
Pim bağlantılı kompozit plakaların üç boyutlu yetmezlik analizi
- Tez No: 90962
- Danışmanlar: DOÇ. DR. LEVEND PARNAS
- Tez Türü: Doktora
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Sonlu Eleman Analizi, Kompozit Malzemeler, Yetmezlik Analizi, İlerleyen Hasar Modeli, Temas Analizi, Geometrik olarak doğrusal olmayan poblem. vı, Hasar analizi, Kompozit levhalar, Pim bağlantı, Sonlu elemanlar analizi, Finite Element Analysis, Composite Materials, Failure Analysis, Progressive Damage, Contact Analysis, Geometrical Non- linearity, Damage analysis, Composite plates, Pin joint
- Yıl: 2000
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Kompozit ve metal malzemelerin bağlantı bölgelerindeki kırılma biçimlerini belirleyebilmek amacı ile büyük deplasman teorisi, izotrop ve ortotrop malzeme özellikleri ve transformasyon matrisine dayalı bir temas algoritması içeren üç boyutlu doğrusal olmayan bir sonlu eleman yazılımı geliştirilmiştir. Kompozit plaka içindeki hasarın boyutlarını ve kırılma şeklini, uygulanan yükün bir fonksiyonu olarak belirlemek ve kompozit plakaların ilk yüklemeden kırılmaya kadar geçen sürede tepkilerini üç boyutlu olarak gözleyebilmek için bir hasar ilerleme modeli geliştirilmiştir. Hashin ve en büyük gerilme yetmezlik kriterleri, elyaf - matris kesme yetmezliği ve Ye delaminasyon kriteri ile birlikte kullanılmış, malzeme özellikleri yetmezliğin türüne göre değiştirilmiştir. Yazılımın her bölümü için örnek bir problem çözülmüş ve sonuçlar başarılı bulunmuştur. Hasar ilerleme algoritmasını doğrulamak için ortasında bir delik bulunan [06/906]s kompozit plakaya baskı yükü uygulanmıştır. Hashin yetmezlikkriteri ile elde edilen sonuçların deneysel sonuçlarla tam bir uyum içerisinde olduğu ve ortalama değerlerden % 2.6'ya kadar düşen oranlarda saptığı gözlenmiştir. Ancak en büyük gerilme yetmezlik kriterinin sonuçları başarılı bulunmamıştır. Pim bağlantılı [u6/906]s kompozit plakanın yetmezlik analizi iki farklı geometri kullanılarak yapılmış, hasarın ilerlemesi göz önüne alınarak plakadaki net çekme, ezilme, kesme ve karma yetmezlik durumları değerlendirilmiştir.
Özet (Çeviri)
A three-dimensional, non-linear finite element code including large displacement theory, isotropic and orthotropic material properties and a contact algorithm based on transformation matrix was developed to analyze the failure of composite to metal joints. A progressive damage model was developed to predict the extent and the failure modes of the internal damage in composite laminates as a function of applied load and to stimulate the three-dimensional response of composite laminates from initial loading to final collapse. Hashin and maximum stress failure criteria were used together with the fiber-matrix shear failure and Ye delamination criterion and material properties were degraded according to the mode of failure. A test case was conducted for every part of the code and satisfactory results were obtained. The progressive damage algorithm developed was verified using a clustered cross-ply [06/906]s laminate with a hole under compressive inplane load. The results determined by Hashin failure criterion was found IIIto be in good agreement with the experimental results with a deviation of as low as 2.6 % from the average. However, the results of maximum stress failure criterion was unsatisfactory. Pinned joint failure analysis of same cross-ply [06/906]s laminate was conducted using two different geometries and net-tension, bearing, shear- out and mixed modes of failure of the joined was examined according to the progression of the damage.
Benzer Tezler
- Three-dimensional analysis of composite pinned joints
Başlık çevirisi yok
SİNAN PEKŞEN
Yüksek Lisans
İngilizce
1996
Astronomi ve Uzay BilimleriOrta Doğu Teknik ÜniversitesiHavacılık Mühendisliği Ana Bilim Dalı
DOÇ. DR. MEHMET A. AKGÜN
- 600 MWe gücünde PWR tipi bir nükleer reaktör kalp öndizayn analizi
Başlık çevirisi yok
FARZAD REZAEİ BASHARAT
- TİN kaplama parametrelerinin aşınma davranışı üzerindeki etkisi
The Effect of coating parameters on the wear behaviour of TİN
OĞUZ AKKAŞ
Yüksek Lisans
Türkçe
1998
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMalzeme Mühendisliği Ana Bilim Dalı
PROF. DR. E. SABRİ KAYALI
- IEEE 1149.1 standardı kullanarak test edilebilir lojik devre tasarımı
Testable lojik circit design by using IEEE 1149.1 standard
A.BETÜL TUNCER
Yüksek Lisans
Türkçe
1992
Elektrik ve Elektronik Mühendisliğiİstanbul Teknik ÜniversitesiPROF. DR. AHMET DERVİŞOĞLU
- 3D computer modelling and sliding failure analysis of jointed rock slopes
Eklemli kaya şevlerinin 3 boyutlu bilgisayar modellemesi ve kayma analizi
ADEM ÖCAL
Doktora
İngilizce
2000
Maden Mühendisliği ve MadencilikOrta Doğu Teknik ÜniversitesiMaden Mühendisliği Ana Bilim Dalı
PROF. DR. ABDURRAHİM ÖZGENOĞLU