Katılaşma sırasında uygulanan mekanik titreşimin A356 alüminyumun mikroyapı ve mekanik özelliklerine etkisinin incelenmesi
Investigation of the effect of mechanical vibration applied during solidification on the microstructure and mechanical properties of A356 aluminum
- Tez No: 899891
- Danışmanlar: PROF. DR. RECEP ÇALIN, DR. ÖĞR. ÜYESİ NACİ ARDA TANIŞ
- Tez Türü: Yüksek Lisans
- Konular: Savunma ve Savunma Teknolojileri, Metalurji Mühendisliği, Defense and Defense Technologies, Metallurgical Engineering
- Anahtar Kelimeler: Alüminyum, Aluminum
- Yıl: 2024
- Dil: Türkçe
- Üniversite: Kırıkkale Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Savunma Teknolojileri Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Alüminyum alaşımlar, ağırlık ve mekanik özelliklerinden kaynaklı olarak savunma sanayi, otomotiv endüstrisi, tesisat ekipmanları, sağlık teknolojileri gibi birçok farklı uzmanlık alanında tercih edilmektedir. Sektörlerin hem teknolojik anlamda hem de büyüklük anlamda gelişmesi ile birlikte alüminyum ve alaşımlarına talep artmaktadır. Alüminyum ürün üretiminde geleneksel bir metot olan döküm ile imalat, farklı geometrideki ürünlerin üretilmesinde kullanılmaktadır. Diğer tüm malzemelerde olduğu gibi alüminyum malzemeler için de kullanım isterlerine göre mekanik özelliklerinde iyileştirmeler gerekebilmektedir. Alüminyum malzemelerin mekanik özelliklerini iyileştirmek için kimyasal kompozisyonlarında yapılacak iyileştirmelerin yanı sıra üretim sırası ve sonrasında da bazı operasyonlar yapılabilmektedir. Bu çalışmada, bir Al-Si alaşımı olan A356 alüminyum alaşıma katılaşma sırasında mekanik titreşim uygulanmıştır. Farklı titreşim seviyelerinde gerçekleştirilen katılaştırmanın yanı sıra titreşimsiz katılaştırmada gerçekleştirilmiştir. Üretim sonrasında, gözeneklilik testi, dentrit kolları arası mesafenin ölçümü için mikroyapı incelemesi, aşınma verilerinin elde edilebilmesi için aşınma testi, sertlik değerlerinin ölçümü için sertlik testi, aşınma katsayılarının tespiti için ise aşınma katsayısı hesabı gerçekleştirilmiş; SEM görüntülemesi ve EDS analizlerine de yer verilmiştir. İncelemeler sonucunda, gözeneklilik testi, aşınma dayanımı ve aşınma katsayısı hesabında titreşimin belli bir seviyeye kadar olumlu etkisi gözlemlenmiş; belli bir seviyeden sonra negatif durum gözlemlenmiştir. Dentrit kolları arası mesafe ise her titreşim seviyesinde azalmış; sertlik ise her titreşim seviyesinde artış göstermiştir.
Özet (Çeviri)
Aluminum alloys are preferred in many different areas of expertise such as the defense industry, automotive industry, plumbing equipment and health technologies due to their weight and mechanical properties. As the sectors develop both technologically and in size, the demand for aluminum and its alloys increases. Manufacturing by casting, which is a traditional method in aluminum product production, is used to produce products of different geometries. As with all other materials, improvements in the mechanical properties of aluminum materials may be required depending on the usage requirements. In order to improve the mechanical properties of aluminum materials, in addition to improvements in their chemical composition, some operations can be performed during and after production. In this study, mechanical vibration was applied to A356 aluminum alloy, an Al-Si alloy, during solidification. In addition to solidification at different vibration levels, vibration-free solidification was also carried out. After production, porosity test, microstructure examination to measure the distance between dendrite arms, wear test to obtain wear data, hardness test to measure hardness values, and wear coefficient calculation to determine wear coefficients were performed; SEM imaging and EDS analyzes are also included. As a result of the examinations, a positive effect of vibration was observed up to a certain level in porosity test, wear resistance and wear coefficient calculations; after a certain level, a negative situation was observed. The distance between dendrite arms decreased at each vibration level; The hardness increased at each vibration level.
Benzer Tezler
- Improving the thermal conductivity of fiber-reinforced concrete panels for exterior facades with phase change materials
Diş cepheler için elyaf takviyeli beton panellerin ısı ı̇letkenliğinin faz değiştiren malzemelerle ı̇yileştirilmesi
YALDA SAFARALIPOUR
Doktora
İngilizce
2023
Enerjiİstanbul Teknik ÜniversitesiMimarlık Ana Bilim Dalı
PROF. DR. MUSTAFA ERKAN KARAGÜLER
- Alüminyum silisyum ötektik alaşımının mikroyapı ve mekanik özelliklerinin elektrik alana bağlılığının incelenmesi
Investigation of microstructure and mechanical properties dependences on static electrical field in the aluminium silicon eutectic alloy
SEMİH BİRİNCİ
Yüksek Lisans
Türkçe
2020
Metalurji MühendisliğiYıldız Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. NECMETTİN MARAŞLI
- Eş kanallı açısal ekstrüzyon işleminin Zn-60Al ve Zn-60Al-2Cu alaşımlarının yapısal mekanik ve aşınma özelliklerine etkisi
Effect of equal channel angular extrusion process on microstructural, mechanical and wear properties of Zn-60Al and Zn-60Al-2Cu alloys
ONUR SARAY
Yüksek Lisans
Türkçe
2007
Makine MühendisliğiKaradeniz Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. GENÇAĞA PÜRÇEK
- Kobalt bazlı haynes 188 süperalaşımında lazer kesim sonrasında oluşan recast tabakasının karakterizasyonu ve mekanik özelliklere etkisi
Characterization of recast layer formed on haynes 188 cobalt based superalloy by laser beam machining and effect on mechanical properties
AYBERK YENİCE
Yüksek Lisans
Türkçe
2022
Mühendislik Bilimleriİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ CEVAT FAHİR ARISOY
- Al-%5,7 Zn-%2,6 Mg-%1,7 Cu alaşımının kum, metal kalıp ve sıkıştırma döküm yöntemlerinde mikroyapı ve mekanik özelliklerinin incelenmesi
Investigation of microstructure and mechanical properties of cast Al-%5,7 Zn-%2,6 Mg-%1,7 Cu alloy obtained with sand, gravity and squeeze casting process
ŞÜKRAN KOCAASLAN
Yüksek Lisans
Türkçe
2004
Teknik EğitimGazi ÜniversitesiMetal Eğitimi Ana Bilim Dalı
Y.DOÇ.DR. KADİR KOCATEPE