Küresel grafitli dökme demirlerin ark kaynak yöntemi ile kaynak edilebilirliğinin ve kaynak sonrası mekanik özelliklerin incelenmesi
The Weldability of ductile cast irons by using arc welding technique and investigation of its mechanical properties
- Tez No: 85915
- Danışmanlar: Y.DOÇ.DR. CEMİL ÇETİNKAYA
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Küresel grafitli dökme demir, jCaynak, Mikro yapı, Ön tavlama, Ark kaynağı, Kaynak yöntemleri, Küresel grafitli dökme demirler, Mekanik özellikler, Mikroyapı, Ductile C I Nodular C.I, Welding, Microstructure, Preheating, Arc welding, Welding methods, Nodular graphite cast irons, Mechanical properties, Pre-annealing
- Yıl: 1999
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metal Eğitimi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Endüstride kullanım alanı gittikçe artmakta olan küresel grafıtli dökme demirlerin (KGDD) kaynak edilebilirliği ve kaynak sonrası mekanik özelliklerinde meydana gelen değişiklikleri araştırmak amacıyla farklı kimyasal bileşime sahip KGDD numunelerine değişik ön tav sıcaklıktan uygulanarak kaynak edilebilirliği incelenmiştir. Ark kaynağında Askaynak firmasının ürettiği E NiFe-Cl örtülü elektrod kullanılmıştır. Kaynak işleminden sonra, mikro yapı (ana malzeme, ısı tesiri altındaki bölge (ITAB), kaynak metali bölgesi) incelemesi yapılmıştır. Kaynak işlemi sonunda malzemelerin çekme dayanımlarının, değişen ön tav sıcaklıklarına bağlı olarak arttığı, ön tav sıcaklığının artışıyla bölgeler arasındaki sertlik değerlerinde değişme görülmüştür. Ön tav sıcaklığının diğer bir etkisi ise sıcaklık artışına bağlı olarak malzemenin ITAB bölgesindeki sertlik değerlerinin azaldığı buna karşılık kaynak metalinin sertliğinde ise artma olduğu gözlenmiştir. Bilim Kodu : 626 1801
Özet (Çeviri)
The use of nodular cast iron is increasing in industrial applications. In this study the weldability and mechanical properties, of welded nodular cast iron were examined. For this reason, in order to investigate properties variations, different nodular cast iron specimens having different composition were welded. Different preheat temperatures were applied to each specimen. When applying arc-welding technique to the specimens E NiFe-Cl type coated electrodes were used. After welding microstructures of the main material, heat affected zone (HAZ) and filler metal zones were examined by optical microscopy. As a result of welding process, tensile stress properties were improved by applying different preheating temperatures. By increasing the preheat temperatures local variations of hardness values on HAZ were attained. The hardness values on HAZ were observed to decrease while it was observed to increase in filler metal zone. Science Code : 6261801
Benzer Tezler
- GGG 40 sınıfı küresel grafitli dökme demirlerin yorulma davranışına tin kaplamanın etkisi
Başlık çevirisi yok
GÖKHAN BAŞMAN
Yüksek Lisans
Türkçe
1998
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
DOÇ. DR. M. KELAMİ ŞEŞEN
- Küresel grafitli dökme demirlerin ostemperleme ısıl işleminin çekme mukavemetine etkisi
Başlık çevirisi yok
M.TOLGA YILMAZ
- Küresel grafitli dökme demirlerin borlanması ve özellikleri
The boriding of some ductile irons and their properties
UĞUR ŞEN
Doktora
Türkçe
1997
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. FEVZİ YILMAZ
- Küresel grafitli dökme demirlerin aşınma davranışları
Wear behaviours of ductile irons
ÖZGÜR ÇELİK
Yüksek Lisans
Türkçe
2001
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. EYÜP SABRİ KAYALI
- Ostemperlenmiş küresel grafitli dökme demirlerin yorulma mukavemeti
Fatique strength of austempered ductile iron
OSMAN ÇÖĞEN
Yüksek Lisans
Türkçe
1996
Makine MühendisliğiEskişehir Osmangazi ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. ORHAN ŞERİF KOMAÇ