Determination and preparation of rheological behaviour of fine strontium titanate powder suspensions
Strontium titanat seramik tozlarının hazırlanması ve reolojik uygulamalarının incelenmesi
- Tez No: 85241
- Danışmanlar: PROF. DR. MUHSİN ÇİFTÇİOĞLU, YRD. DOÇ. DR. MUSTAFA GÜDEN
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Mühendislik Bilimleri, Chemistry, Engineering Sciences
- Anahtar Kelimeler: Pechini yöntemi, Reoloji, Seramik tozları, Sol-jel yöntemi, Pechini method, Rheology, Ceramic powders, Sol-gel method
- Yıl: 1999
- Dil: İngilizce
- Üniversite: İzmir Yüksek Teknoloji Enstitüsü
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Malzeme Bilimi ve Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
oz Bu projede, strontium titanate tozu sol-gel ve Pechini metodları kullanılarak yapılmıştır. Sol-gel metodunda, tozlar Ti02 solu ve Sr(N03>2 solüsyonu karıştırılarak üretilmiştir. Sr(N03)2 solüsyonunun eklenmesinden sonra çökelme gözlenmiştir. Her iki yöntemle de ikişer toz üretilmiştir. Sol-gel metodunda, asit:alkol oranı değiştirilmiştir. Pechini metodunda, sitric acitin % 50 si poliakrilik asit ile değiştirilmiştir. Tozların karakterizasyonları termal gravimetrik analiz (TGA) cihazı, Fourier değişimli infrared spektra (FTIR), XRD, taramalı elektron mikroskopu (SEM) ve optik mikroskop kullanılarak yapıldı. TGA verilerine dayanarak, sol-gel tozu için kalsinasyon sıcaklığı 650 °C olarak seçilmiştir. XRD sonuçları, bu sıcaklığın SrTiC>3 fazının tamamı ile oluşması için yeterli olmadığını göstermiş, ancak FTIR spektralarında nitrat ve organik piklerine rastlanmamıştır. Sinterleme çalışmaları, sol-gel tozunda çok kuvvetli topaklanmalar olduğunu göstermiştir. Sol-gel tozlarının relatif yoğunlukları sinterlemeden sonra dahi çok düşüktür. Pechini tozları daha zayıf topaklanmalara sahiptir ve sinterlemeden sonra daha yüksek relatif yoğunluklar göstermiştir. Pechini tozlarının çapları 0.2-0.5 um arasında bulunmuştur. Üretilen toz değişik yüzdelerde, pirinç yağının içinde dağıtılarak, katı yüzdesinin reolojik davranış üzerindeki etkisi araştırıldı. Bunun için bir rheometre kullanıldı. Farklı kayma gerilimlerinde ve hacimsel toz fraksiyonlarında çalışmalar yapılmıştır. Kararlı olmayan süspansiyonlar kayma gerilimi arttıkça viskozitede azalma göstermiştir, bu da topaklanmalara işaret eder. Ancak yüzey aktif maddesi eklendikten sonra, süspansiyonlar kararlı hale gelmiş ve dilatant ya da Newtonian davranış göstermişlerdir. Katı yüzdesindeki artış, kararlı haldeki süspansiyonlar için viskozitede çok büyük değişiklik yapmamıştır.
Özet (Çeviri)
ABSTRACT In this project, strontium titanate powders were prepared by using sol- gel and Pechini methods. In sol-gel method, the powders were prepared by mixing the TİO2 sol and Sr(NC>3)2 solution. Precipitation was observed after the addition of Sr(N03)2 solution. Two powders were prepared by each method. In sol-gel method, acid:alcohol ratio was changed. In Pechini method, 50% of citric acid was substituted with polyacrylic acid. The characterization of the powders were performed by Fourier Transform Infrared Spectrophotometer (FTIR), Thermogravimetric Analyzer (TGA), Scanning Electron Microscope (SEM), X-Ray Diffraction and Optical Microscope. The calcination temperature of 650 °C was chosen for sol-gel powder according to TGA data. XRD pattern showed that this temperature was not high enough to form complete SrTi03 phase, but no peaks related to nitrates or organic groups was observed in FTIR spectra. Sintering studies indicated that the agglomeration of sol-gel powder was very strong because the relative densities were very small. Pechini powders had weaker agglomerates and sintered to higher densities. The diameters of the Pechini powders were found as in the range of 0.2-0.5 um. The powders were dispersed in white oil and the rheological behaviour of these dispersions was studied by a rheometer. Several runs at different shear rates, and volume fractions were done. The suspensions without surfactant showed shear-thinning behavior, which indicates that the suspensions were flocculated. The addition of surfactant in certain amount produced stabilized suspensions. The stabilized suspensions showed Newtonian or Dilatant behaviour. The increase in the solids loading did not show significant change in the viscosity of stabilized suspension.
Benzer Tezler
- Preparation and characterization of alumina powders and suspensions
Alümina tozları ve süspansiyonlarının hazırlanması ve karakterizasyonu
AYLİN MÜYESSER ŞAKAR
Yüksek Lisans
İngilizce
2000
Metalurji Mühendisliğiİzmir Yüksek Teknoloji EnstitüsüPROF.DR. MUHSİN ÇİFTÇİOĞLU
Y.DOÇ.DR. HÜRRİYET POLAT
- Tarihi eserlerde kullanılan CaSO4 harç ve sıvalarının incelenmesi
Investigation of historical CaSO4 mortars and plasters
ESRA Z. UZGİL
- Tatil köylerindeki genel kullanım ve rekreasyon alanlarının planlama ilkeleri
The Planning principles of general utility and recreation areas in holiday village
MUALLA KANCIOĞLU
- Türkiye'de karayolu etüd ve proje çalışmalarında uygulanabilecek fotogrametrik değerlendirme modeli ve öneriler
Photogrammetric restitution model on studies of highway location survey and their projects in Turkey and some recommendations
FERRUH YILDIZ
- A Case study for credit ratings of a gas cycled power plant financed by project finance in Turkey
Türkiye'de proje finansmanı ile finanse edilen bir gaz çevrim enerji santralinin kredi derecelendirmesi (reyting) ile ilgili bir vaka çalışması
OĞUZ KAAN KİZİROĞLU
Yüksek Lisans
İngilizce
2000
İnşaat MühendisliğiOrta Doğu Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. METİN ARIKAN