İletken polikarbazolün elektrokimyasal sentezi ve karakterizasyonu
Elektrochemical synthesis and characterization of conducting polycarbazole
- Tez No: 85189
- Danışmanlar: DOÇ. DR. ŞADİ ŞEN, PROF. DR. MEHMET SAÇAK
- Tez Türü: Yüksek Lisans
- Konular: Kimya, Chemistry
- Anahtar Kelimeler: Polikarbazol, İletken Polimerler, Elektrokimyasal Polimerizasyon, Sabit Potansiyel Elektrolizi, Elektrokimyasal polimerleşme, Çözünürlük, Polycarbazole, Conducting Polymers, Electrochemical Polymerization, Controlled Potential Electrolysis, Solubility
- Yıl: 1999
- Dil: Türkçe
- Üniversite: Zonguldak Karaelmas Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Kimya Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Bilim Uzmanlığı Tezi İLETKEN POLİKARBAZOLÜN ELEKTROKİMYASAL SENTEZİ VE KARAKTERİZASYONU Hülya MACİT Zonguldak Karaelmas Üniversitesi Fen Bilimleri Enstitüsü Kimya Anabilim Dalı Tez Danışmanı: Doç.Dr. Sadi ŞEN Ortak Danışman: Prof.Dr. Mehmet SAÇAK Eylül 1999, 82 sayfa. Bu çalışmada karbazolün, asetonitril - tetrabütilamonyum tetrafloroborat içinde, Pt elektrot kullanılarak, sabit potansiyel elektroliz yöntemi ile elektrokimyasal olarak polimerleştirilmesi incelendi. Polimer verimi; monomer derişimi, elektroliz potansiyeli ve sıcaklığın arttırılması ile arttı. Değişik koşullarda elde edilen polikarbazol örneklerinin iletkenliklerinin 10“3 S / cm dolayında olduğu belirlendi ve undop işlemi sonucu bu iletkenlik değeri 10”8 S / cm düzeyine düştü. Değişik çözücüler kullanılarak yapılan çözünürlük deneylerinde, polikarbazol çözünürlüğünün önemsiz olduğu gözlendi. Polikarbazolün elektriksel direncinin sıcaklıkla değişimi 30 - 125 °C sıcaklık aralığında incelendi. Polimer karakterizasyonu ayrıca CV, FTIR ve TGA ile yapıldı. inÖZET (devam ediyor)
Özet (Çeviri)
ABSTRACT M. Sc. Thesis ELECTROCHEMICAL SYNTHESIS AND CHARACTERIZATION OF CONDUCTING POLYCARBAZOLE Hülya MACİT Zonguldak Karaelmas University Graduate School of Natural and Applied Sciences Department of Chemistry Thesis Advisor: Assoc.Prof.Dr. Sadi ŞEN Co-advisor: Prof.Dr. Mehmet SAÇAK September 1999, 82 pages. In this work, electrochemical polymerization of carbazole by constant potential electrolysis method in acetonitrile - tetrabütylammonium tetrafluoroborate with Pt electrode has been investigated. Polymer yield has been observed to increase with increasing monomer concentration, electrolysis potential and temperature. The conductivities of polymeric samples obtained under different conditions were measured to be about 10"3 S / cm. After undoping, these values decreased to the level of 10'8 S / cm. Solubilitiy tests in various solvents have revealed that the solubility of polycarbazole is insignificant. The temperature dependence of electrical resistance of polycarbazole between 30 - 125 °C has been examined. Polymer characterizations have been done employing CV, FTIR and TGA techniques.ABSTRACT (continued)
Benzer Tezler
- Metil pirolün karbazol ve etil karbazol ile kimyasal ve elektrokimyasal polimerizasyonlarının karşılaştırmalı olarak incelenmesi
Chemically and electrochemical polymerization of methyl pyrrole with carbazole and ethyl carbazole
MURAT ATEŞ
- Chemical and electrochemical polymerisation of substituted carbozoles in the presence of acrylamide
Sübstitüye karbozollerin akrilamid varlığında kimyasal ve elektrokimyasal polimerizasyonu
ÖZLEM YAVUZ
- An Investigation on floor panel heating by conductive sheet analogy
Başlık çevirisi yok
MEHMET RIFAT MATARACI
- Electrochemical synthesis of conducting polyaniline blends and their use as sensors
Başlık çevirisi yok
SAKIP DOĞAN