The effect of glazing and thermocycling on the surface roughness and microhardness of different CAD/CAM milled ceramic laminate veneers with SEM observations
Glaze ve termosiklüsün CAD/CAM ile frezelenmiş farklı seramik laminelerin yüzey pürüzlülüğü ve mikrosertliğine etkisi SEM gözlemleriyle beraber
- Tez No: 846337
- Danışmanlar: DR. ÖĞR. ÜYESİ MUSTAFA ERSOY
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: CAD/CAM, Yüzey pürüzlülüğü, Mikro sertlik, Glaze, Termosiklüs, Dental materyaller, Dental porselen, Diş kaplamaları, Frezeleme, Laminatlar, Lamine malzeme, Mikrosertlik, Mikroskopi-elektron taramalı, CAD/CAM, Surface roughness, Microhardness, Glaze, Thermocycling, Dental materials, Dental porcelain, Dental veneers, Milling, Laminates, Laminated materials, Microscopy-electron scanning
- Yıl: 2023
- Dil: İngilizce
- Üniversite: Yeditepe Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu in vitro çalışmanın amacı, glazür ve termosiklüs işlemlerinin dört farklı seramik CAD/CAM materyallerinin yüzey pürüzlülüğü ve mikrosertlik değerleri üzerine etkisini değerlendirmektir. Gereç ve Yöntemler: Eğitim modelinin plastik maksiller birinci kesici dişi Omnicam tarayıcı (Cerec, Sirona) ile tarandıktan sonra CAD/CAM laminate veneer şekilli 80 tane CAD/CAM sistemi (inLab MC XL Cerec, Sirona) ile üretildi. Bu çalışmada dört farklı CAD/CAM seramik materyalleri değerlendirildi: Lityum disilikat (IPS e.max CAD, Ivoclar), Lösit takviyeli seramik (IPS Empress CAD), Feldspatik seramik (Cerec, Sirona) ve Nanopartikül dolgulu reçine seramik (Cerasmart), GC). 80 numuneden 4 grup (her grupta 20 numune, n=20) iki alt gruba (10 numune, n=10) ayrıldı: Glazürlü ve glazürsüz. Tüm örnekler 10.000 termosiklüs işlemine tabi tutuldu. Yüzey pürüzlülüğü ve mikrosertlik değerleri üç aşamada elde edilmiştir: Frezeleme sonrası (Başlangıç), Glazür sonrası ve termosiklüs sonrası. Her gruptan (Frezeleme sonrası (Başlangıç), termosiklüs sonrası) her materyalin sem görüntüleri (100 × 250 × 500 x 1000 büyütme) elde edilmiştir. Bulgular: Başlangıç yüzey pürüzlülüğü ortalamaları açısından materyaller arasında istatistiksel olarak anlamlı bir fark vardır. Emax grubunun başlangıçtaki yüzey pürüzlülüğü Empress'inkinden önemli ölçüde daha yüksekti. CS ve Cerec grupları (p<0,05). Glaze'li yüzey değerlendirildiğinde, yaşlandırma sonrası mikrosertlik değerleri ortalamaları açısından materyaller arasında istatistiksel olarak anlamlı bir fark bulunmuştur (p<0,05). Emax grubunun glaze sonrası mikrosertliği CS, Empress ve Cerec gruplarına göre anlamlı derecede yüksekti (p<0.05). Glaze'li yüzey değerlendirildiğinde termosiklüs sonrası mikrosertlik değerlerinin ortalamaları açısından materyaller arasında istatistiksel olarak anlamlı bir fark bulunmuştur (p<0,05) Emax grubunun termosiklüs sonrası mikrosertlik değerleri CS, Empress ve Cerec gruplarına göre anlamlı derecede yüksekti (p<0.05). CS materyalinin yüzeyini değerlendirirken; başlangıçta, glaze sonrası ve termosiklüs sonrası ortalama mikrosertlik değerleri arasında istatistiksel olarak anlamlı bir fark vardır (p:0,000; p<0,05). Başlangıç yüzey pürüzlülüğünün glaze sonrası ve termosiklüs sonrası istatistiksel olarak anlamlı düzeyde daha yüksek olduğu belirlendi (p1:0.000; p2:0.000; p<0.05). Emax materyalinin yüzeyini değerlendirirken; başlangıç yüzey pürüzlülüğünün glaze ve termosiklüs sonrası istatistiksel olarak anlamlı düzeyde daha yüksek olduğu belirlendi (p<0,05). Glaze sonrası mikrosertlik düzeyi Termosiklüs sonrasına göre istatistiksel olarak anlamlı derecede yüksekti (p<0.05). Empress materyalinin yüzeyini değerlendirirken; başlangıç yüzey pürüzlülüğünün glaze ve termosiklüs sonrası istatistiksel olarak anlamlı düzeyde daha yüksek olduğu belirlendi (p<0,05). Glaze sonrası ve termosiklüs sonrası mikrosertlik düzeyleri arasında istatistiksel olarak anlamlı bir fark bulunmadı (p:0,074; p>0,05). Cerec materyalinin yüzeyini değerlendirirken; başlangıç yüzey pürüzlülüğünün glaze ve termosiklüs sonrası istatistiksel olarak anlamlı düzeyde daha yüksek olduğu belirlendi (p<0,05). Glaze sonrası ve termosiklüs sonrası mikrosertlik seviyeleri arasında istatistiksel olarak anlamlı bir fark yoktu (p>0,05) Yüzeye glaze uygulanmadığında Emax grubunun başlangıç mikrosertlik değerleri CS, Empress ve Cerec gruplarına göre anlamlı derecede yüksekti (p<0.05). Yüzeye glaze uygulanmadığında Emax grubunun termosiklüs sonrası mikrosertlik değerleri CS, Empress ve Cerec gruplarına göre anlamlı derecede yüksekti (p<0.05). CS materyali yüzeyini değerlendirirken; Termosiklüs sonrası mikrosertlik değerleri istatistiksel olarak başlangıctaki değerlere göre anlamlı derecede düşük bulunmuştur (p:0,000; p<0,05). Empress materyalinin yüzeyini değerlendirirken; Termosiklüs sonrası mikrosertliğin istatistiksel olarak başlangıçtaki değerlere göre anlamlı düzeyde daha düşük olduğu bulundu (p<0.05). Emax materyalinin yüzeyini değerlendirirken; Termosiklüs sonrası mikrosertlik değerlerinin istatistiksel olarak başlangıçtaki değerlere göre anlamlı düzeyde daha düşük olduğu bulundu (p<0.05). Sonuç: Örneklerin yüzeyine glaze uygulamasının tüm örneklerin yüzey pürüzlülük değerlerini önemli ölçüde etkilediği sonucuna varılmıştır. Yüzey pürüzlülük değerlerinin azalması yüzeylerin düzgünlüğünün artmasına neden olur. Glaze, CAD/CAM ile üretilen lamineler örneklerinin yüzey pürüzlülüğü ve mikrosertlik değerlerini azaltır. Kompozit içerikli CAD/CAM örnekleri cam seramiklere göre termosiklüs sonrası yüzey pürüzlülük değerlerinin artmasına daha yatkındır. Termosiklüsün yüzey pürüzlülük değerleri üzerinde mikrosertlik değerlerine göre daha fazla etkisi vardır. Bu çalışma, araştırmacıların ve klinisyenlerin kliniklerde kullanılacak CAD/CAM malzemelerinin yüzey kalitesini ve özelliklerini daha iyi anlamaları amacıyla yapılmıştır. Bu çalışma, klinisyen ve araştırmacıların CAD/CAM sistemlerinde kullanılacak materyallarin yüzey özelliklerini değerlendirerek daha kaliteli, daha sağlıklı ve daha uzun ömürlü restorasyonlar üretebilmelerini sağlamak amacıyla yapılmıştır.
Özet (Çeviri)
The Purpose: The aim of this in-vitro study was to evaluate the effect of glaze and thermocycling to the surface roughness and microhardness values of four different ceramic CAD/CAM materials. Material & Methods: CAD / CAM laminate veneer shaped 80 samples were milled with CAD/CAM system (inLab MC XL Cerec, Sirona) after scan of plastic maxillary first incisor tooth of educational model with Omnicam scanner (Cerec, Sirona). Four different CAD/CAM ceramic materials were tested in this study: Lithium disilicate (IPS E.max CAD, Ivoclar), Leucite reinforced ceramic (IPS Empress CAD), Feldspathic ceramic (Cerec, Sirona) and a Nanoparticle-filled resin ceramic (Cerasmart, GC) (CS). Four groups from 80 samples (20 samples for each group, n=20) were allocated to two subgroups (10 samples, n=10): Glazed and non-glazed. All specimens were subjected to 10.000 thermo cycles. Surface roughness and Vickers hardness values were obtained in three stages: After milling (Initial), after glazing, after thermocycling. Sem images (100x, 250x, 500x, 1000x magnifications) of each material were obtained from every group (After milling (Initial), after thermocycling). Results: There is a statistically significant difference between materials in terms of initial surface roughness averages. The initial surface roughness of the Emax group was significantly higher than that of the Empress. CS, and Cerec groups (p<0.05). When evaluating the glazed surface, there was a statistically significant difference between the materials in terms of post-glazing microhardness averages (p<0.05). The microhardness of the Emax group after glaze was significantly higher than that of the CS, Empress and Cerec groups (p<0.05). When evaluating the glazed surface, there is a statistically significant difference between the materials in terms of microhardness averages after the thermo cycle (p<0.05) The post-thermo-cycle microhardness of the Emax group was significantly higher than that of the CS, Empress and Cerec groups (p<0.05). When evaluating the surface of CS material; there is a statistically significant difference between the mean microhardness at baseline, after glazing and after thermo cycle (p:0.000; p<0.05). Initial surface roughness was found to be statistically significantly higher after glaze and after thermo cycle (p1:0.000; p2:0.000; p<0.05). When evaluating the surface of Emax material; initial surface roughness was found to be statistically significantly higher after glaze and after thermo cycle (p<0.05). Microhardness level after glazing was statistically significantly higher than after Thermo cycle (p<0.05). When evaluating the surface of Empress material; initial surface roughness was found to be statistically significantly higher after glaze and after thermo cycle (p<0.05). There was no statistically significant difference between microhardness levels after glazing and after thermo cycle (p:0.074; p>0.05). When evaluating the surface of Cerec material; initial surface roughness was found to be statistically significantly higher after glaze and after thermo cycle (p<0.05). There was no statistically significant difference between microhardness levels after glazing and after thermo cycle (p>0.05) When glaze is not applied to the surface, the initial microhardness of the Emax group was significantly higher than that of the CS, Empress and Cerec groups (p<0.05). When glaze is not applied to the surface, the post-thermo-cycle microhardness of the Emax group was significantly higher than that of the CS, Empress and Cerec groups (p<0.05). When evaluating surface of CS material; microhardness after thermo cycle was found to be statistically significantly lower from baseline (p:0.000; p<0.05). When evaluating surface of Empress material; microhardness after thermo cycle was found to be statistically significantly lower from baseline (p<0.05). When evaluating surface of Emax material; microhardness after thermo cycle was found to be statistically significantly lower from baseline (p<0.05). Conclusion: It was concluded that application of the glazed layer on the surface of the samples significantly affects the surface roughness values of all samples. Reduction of the surface roughness values lead to increase the smoothness of the surfaces. Glazing decreases the surface roughness and microhardness values of CAD/CAM milled laminate veneer samples. Compared to glass ceramics, composite CAD/CAM material is more prone to increase of surface roughness values after aging. Thermocycling has more influence on surface roughness values than microhardness values. This study was conducted for researchers and clinicians to better understand the surface quality and properties of CAD/CAM materials to be used in clinics. This study was conducted to enable clinicians and researchers to evaluate the surface properties of materials to be used in CAD/CAM systems and to produce better quality, healthier and longer lasting restorations.
Benzer Tezler
- CAD-CAM tam seramik materyallerin renk, translusensi ve pürüzlülükleri üzerine polisaj ve glaze ışlemlerinin etkisinin değerlendirilmesi
Evaluation of the effect of polishing and glaze techniques on the color, translucency and surface roughness of CAD-CAM all-ceramic materials
SENA KAMACI ERGÜL
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiHacettepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. SÜLEYMAN CUMHUR ALTINTAŞ
- Tek katmanlı ve çok katmanlı monolitik zirkonya seramiklerin renk stabilitelerinin ve translusensi özelliklerinin değerlendirilmesi
Evaluation of color stabilities and translucency properties of monolayer and multilayer monolithic zirconia ceramics
EDA DÖĞÜŞCÜ
Doktora
Türkçe
2023
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ÖZGÜL KARACAER
- Farklı yüzey bitim işlemleri ve kahve termal siklusunun lityum disilikat esaslı CAD-cam cam seramiklerin renk stabilitesi ve yarı saydamlığı üzerine etkisinin incelenmesi
Investigation of the effects of different surface finishing procedures and coffee thermocycling on color stability and translucency of lithium disilicate based CAD-cam glass-ceramics
ABDULHALUK SAVAŞ
Doktora
Türkçe
2024
Diş HekimliğiNecmettin Erbakan ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ALİ RIZA TUNÇDEMİR
- Farklı zirkonya sistemlerinde glazür ve termal siklus uygulamalarından sonra kırılganlık ve mikrosertlik değişimleri
A comparative study of biaxial flexural strength and vickers microhardness of different zirconia materials after glazing and thermal cycling
ESRA SALİHOĞLU
Doktora
Türkçe
2009
Diş HekimliğiYeditepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ENDER KAZAZOĞLU
- Mikrodalga ile yapılan glaze işleminin farklı üstyapı porselenlerinin yüzey özelliklerine ve renk stabilitesine etkisinin incelenmesi
Investıgatıon of the effect of mıcrowave glazıng on the surface propertıes and color stabılıty of varıous porcelaıns
FATMA AYŞE ŞANAL
Doktora
Türkçe
2011
Diş HekimliğiOndokuz Mayıs ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. DR. MURAT KURT