Production and structural, magnetic and caloric characterization of bonded magnetocaloric material with high thermal conductivity plastic
Yüksek termal iletkenliğe sahip malzeme ile bağlı manyetokalorik malzemenin üretilmesi ve yapısal, manyetik ve kalorik karakterizasyonu
- Tez No: 845906
- Danışmanlar: DOÇ. DR. EYÜP DUMAN
- Tez Türü: Yüksek Lisans
- Konular: Enerji, Mühendislik Bilimleri, Energy, Engineering Sciences
- Anahtar Kelimeler: Manyetokalorik etki (MKE), Termal iletkenlik, Magnetocaloric effect (MCE), Thermal conductivity
- Yıl: 2023
- Dil: İngilizce
- Üniversite: Ankara Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Enerji Sistemleri Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tez kapsamında manyetokalorik malzemeler ile bağlı malzemeler arasındaki termal iletkenlik problemi üzerinde çalışılmıştır. TCPoly firması tarafından geliştirilen yüksek termal iletkenlik özelliklerine sahip TCPoly termoplastiği ile mikron boyutunda Gd tozu karıştırılarak numuneler hazırlanmıştır. Karıştırma işlemi TCPoly malzemesinin erime sıcaklığı olan 250-280 oC'de gerçekleştirilmiştir. Hazırlanan numunelerin TCPoly konsantrasyonu ağırlıkça % 0-15 olarak belirlenmiştir. Bu değerler, bağlayıcı malzeme bileşiminin literatür çalışmalarından seçilmiştir. Ağırlıkça 5%, 10% ve 15% TCPoly içeren numunelerin mikroyapısı Taramalı Elektron Mikroskobu (SEM) ile incelenmiştir. Hazırlanan bağlı manyetokalorik numunelerin manyetik özellikleri, titreşimli numune manyetometri cihazı kullanılarak ölçülmüştür. Numunelerin manyetizasyonunun sıcaklık ve manyetik alan bağımlılığı, 2T'ye kadar uygulamalı alanlarda 270-310 K sıcaklık aralığında ölçülendirilmiştir. Bu ölçümlerden alınan datalara göre adyabatik entropi değişimi SM, Maxwell denklemi kullanılarak hesaplanmıştır. Yüksek ısısal iletkenlipe sahip TCPoly termoplastiği ile karıştırılmış olan manyetokalorik numunelerin farklı bileşiminin, manyetizasyonu, manyetik entropi değişimi, araştırılmıştır. Artan TCPoly içeriği ile numunelerin maksimum entropi değişiminin beklendiği gibi azaldığı gözlemlenmiştir. Buna rağmen elde edilen TCPoly termoplastiğe bağlı manyetokalorik malzemelerin, manyetik soğutucu teknolojisinde kullanılabileceği gösterilmiştir.
Özet (Çeviri)
In this thesis, the thermal conductivity problem between magnetocaloric materials and bonded materials has been studied. Samples were prepared by mixing TCPoly thermoplastic with high thermal conductivity properties developed by TCPoly and micron-sized Gd powder. The mixing process was carried out at 250-280 oC, which is the melting temperature of the TCPoly material. TCPoly concentration of the prepared samples was determined as 0-15% by weight. These values were selected from literature studies of binder material composition. The microstructure of the samples containing 5%, 10% and 15% TCPoly by weight was examined by Scanning Electron Microscopy (SEM). The magnetic properties of the prepared bonded magnetocaloric samples were measured using a vibrating sample magnetometry device. The temperature and magnetic field dependence of the magnetization of the samples was measured in the temperature range of 270-310 K in applied fields up to 2T. According to the data obtained from these measurements, the adiabatic entropy change SM was calculated by using the Maxwell equation. The magnetization and magnetic entropy change of the different composition of the magnetocaloric samples were investigated. It was observed that the maximum entropy change of the samples decreased with increasing TCPoly content as expected. However it was shown that, the magnetocaloric material bonded with TCPoly thermoplastic may be used in magnetic cooler technology.
Benzer Tezler
- Kütahya-Gediz yöresi kömürlerindeki kükürdün uzaklaştırılması
Desulfurization of high sulfur Kütahya-Gediz coal
UĞUR DEMİR
Doktora
Türkçe
2011
Maden Mühendisliği ve MadencilikDumlupınar ÜniversitesiMaden Mühendisliği Ana Bilim Dalı
PROF. DR. AHMET AYDIN
- Sol-jel yöntemi ile hazırlanan La1-xMgxMn1-yCoyO3 bileşiklerinin yapısal ve manyetik özelliklerinin incelenmesi
Investigation of structural and magnetic properties of La1-xMgxMn1-yCoyO3 compounds prepared by sol-gel method
AHMET ÇETİN
Yüksek Lisans
Türkçe
2009
Fizik ve Fizik MühendisliğiMuğla ÜniversitesiFizik Ana Bilim Dalı
YRD. DOÇ. DR. ERGÜN TAŞARKUYU
- Bi2S3@Fe3O4 nano kompozitlerin üretilmesi, yapısal ve manyetik özelliklerinin incelenmesi
Production of Bi2S3@Fe3O4 nano composites investigation of structural and magnetic properties
RAMAZAN KARAÇAM
Yüksek Lisans
Türkçe
2020
Fizik ve Fizik MühendisliğiKırklareli ÜniversitesiFizik Ana Bilim Dalı
DR. ÖĞR. ÜYESİ MÜMİN MEHMET KOÇ
DR. NURDAN KURNAZ YETİM
- NiFeCu/Cu ve NiCu filmlerinin elektrodepozisyon tekniği ile üretimi, yapısal ve magnetik özelliklerinin incelenmesi
Production of NiFeCu/Cu and NiCu films by electrodeposition technique, investigation of structural and magnetic properties
UMUT SARAÇ
Doktora
Türkçe
2011
Fizik ve Fizik MühendisliğiEskişehir Osmangazi ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. M. CELALETTİN BAYKUL
- ZnO tabanlı seyreltik manyetik yarıiletkenlerin üretimi ve bazı yapısal, optik ve manyetik özelliklerinin incelenmesi
The production and investigation of some structural, optical and magnetic properties of ZnO-based diluted magnetic semiconductors
SALİH YILMAZ
Doktora
Türkçe
2013
Fizik ve Fizik MühendisliğiKaradeniz Teknik ÜniversitesiFizik Ana Bilim Dalı
DOÇ. DR. EMİN BACAKSIZ