Cu-Al-Be ve Cu-Al-Ni alaşımlarının mekanik etkilerle şekil hatırlama özelliklerindeki değişimlerinin incelenmesi
The investigation shape memory properties of Cu-Al-Be and Cu-Al-Ni alloys by mechanical effects
- Tez No: 83903
- Danışmanlar: PROF. DR. MEHMET CEYLAN
- Tez Türü: Doktora
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Cu-Al-Be ve Cu-Al-Ni alaşımları, şekil hatırlama olayı, zor-zorlanma, martensitik dönüşüm, dönüşüm sıcaklıkları, Alaşımlar, Martensit, Şekil hatırlama, Cu-Al-Be and Cu-AI-Ni alloys, shape memory alloys, stress-strain, martensite transformation, transformation temperatures, Alloys, Martensite, Martensitic transformation, Shape memory
- Yıl: 1999
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada incelenen Cu-1 1.8Al-0.47Be ( ağırlık yüzdeli ) alaşımı austenit fazında D03 yapısına, Cu-ll.6Al-0.42Be, Cu-13.5Al-4Ni, Cu-13A1 4Ni ( ağırlık yüzdeli ) alaşımları austenit fazında DO3, martensit fazındal8R yapılara sahiptirler. Bu alaşımlara uygulanan mekanik zor ve zorlanmaların şekil hatırlama davranışlarına etkileri metalografik metotlar ( optik mikroskobu, taramalı elektron mikroskobu ), x-ışını difraksiyonu ve termal analiz metotları ile incelendi Austenit fazda bulunan Cu-ll.8Al-0.47Be alaşımına T > Af sıcaklığında, martensit fazda bulunan Cu-1 1.6Al-0.42Be alaşımına da T < As sıcaklığında 1 13.6 kg/mm2 lik basma zoru uygulandığında şekil hatırlama özelliklerinin kaybolduğu belirlendi Ayrıca T < As sıcaklığında Cu-13.5Al-4Ni ve Cu-13Al-4Ni alaşımlarında şekil hatırlama özelliklerinin uygulanan çekme zoru ile kaybolmadığı tespit edildi Uygulanan çekme ve basma zorlarına bağlı olarak yeni martensit fazların oluştuğu, mevcut martensitler içinde ikizlenmelerin ve yeni çökelti fazlarının oluştuğu belirlendi. Deformasyon derecesine bağlı olarak örgü parametrelerinde küçük değişimlerin meydana gelmesine rağmen a/b oranının V3/2 den küçük olduğu austenit ve martensit fazların uygulanan zorlardan bozulmadığı belirlendi. Diğer taraftan uygulanan zorların ters dönüşüm sıcaklıklarını yükselttiği tespit edildi.
Özet (Çeviri)
In this study, shape memory properties of Cu-ll.8Al-0.47Be, Cu-ll.6Al-0.42Be, Cu-13.5Al-4Ni and Cu-13Al-4Ni alloys have been investigated. Effects of mechanically applied stress on the shape memory behaviour of these alloys were studied by metalographic methods ( optical microscope and scanning electron microscope ), x-ray diffraction and thermal analysis methods. The alloys studied in this work have DO3 structure in the austenite phase and have 18R structure in the martensite phase. But only Cu-ll.8Al-0.47Be alloys was in the austenite phase the other alloys were 18R martensite phase in the room temperature. It was observed that when a compressive stress of 113.6 kg/mm2 is applied to Cu-1 1.8Al-0.47Be alloy at T > Af in austenite phase region and Cu-1 1.6Al-0.42Be alloy at T < As in martensite phase region, the shape memory behaviours disappeared on the other hand, it was found that the shape memory features were not affected if an tensile stress is applied at T < As to the Cu-13.5Al-4Ni and Cu-13Al-4Ni alloys.The new martensites, twinnings, and precipitation phases were formed in the present martensites depending on the applied tensile and compressive stresses. Despite small changes in the lattice parameters with deformations, it was fount that the a/b ratio of martensite structure is less than V3/2 and this ratio was not affected, and austenite-martensite crystal structures were not disturbed by the applied stresses. However, it has been determined that inverse transformation temperatures have a tendency to increase proportional to the applied stresses.
Benzer Tezler
- Otomotiv sektörü için AI-Si-Fe-x alaşımlarının geliştirilmesi
Başlık çevirisi yok
NECİP ÜNLÜ
Doktora
Türkçe
1998
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. NİYAZİ ERUSLU
- Redükleyici ergitme yöntemiyle kobaltlar ve nikelbor ön alaşımlarının DC ARK fırınlarında üretim şartlarının belirlenmesi
Başlık çevirisi yok
İSMAİL KARACAN
- Kobaltın alumina içeren fayalitik curuflardaki çözünürlüğünün incelenmesi
The Salubility of cobalt in alumina containing fayalitic slags
C. BORA DERİN
- Gaz enjeksiyon ve elementel karbon ilavesi yöntemleri ile tic takviyeli alüminyum matrisli kompozit üretimi
Başlık çevirisi yok
IŞIL ÇEVİKER KERTİ
Doktora
Türkçe
1998
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMalzeme Mühendisliği Ana Bilim Dalı
PROF. DR. H. ERMAN TULGAR
- Kaynak edilebilen kobalt ve demir esaslı alaşımların yüksek sıcaklıkdaki aşınma davranışları
High temperature wear behaviour of weldable cobalt and iron based alloys
HALİS ÇELİK