Farklı hibrit abutmentlar üzerine hazırlanan farklı kalınlıklardaki zirkonya ile güçlendirilmiş lityum silikat cam seramiklerin optik özelliklerinin in vitro olarak incelenmesi
In vitro investigation of optical properties of zirconia reinforced lithium silicate glass ceramics with different thicknesses prepared on different hybrid abutments
- Tez No: 834625
- Danışmanlar: DR. ÖĞR. ÜYESİ CUMHUR KORKMAZ
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental destekler, Dental materyaller, Dental porselen, Diş renk değişikliği, Lityum silikat, Optik özellikler, Zirkonyum oksit, İn vitro, Dental abutments, Dental materials, Dental porcelain, Tooth discoloration, Lithium silicate, Optical properties, Zirconium oxide, In vitro
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Sağlık Bilimleri Üniversitesi
- Enstitü: Hamidiye Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı; farklı materyaller ile hazırlanan hibrit abutment örneklerinin, farklı kalınlıklardaki zirkonya ile güçlendirilmiş lityum silikat seramik (ZLS) kuronlar ile oluşturduğu optik özelliklerin, spektrofotometrik analizler ile in vitro olarak incelenip karşılaştırılmasıdır. Gereç ve Yöntem: Titanyum altyapıların (12x14x1,0 mm) üzerine, lityum disilikat (LDS), hibrit seramik (PICN), polietereterketon (PEEK) ve zirkonya (Zr) materyallerinden hazırlanan kesitler (12x14x0,7 mm; n=10) yerleştirilerek 80 adet hibrit abutment örneği elde edildi. Kontrol grupları olarak 20 adet Zr örnek (12x14x1,8 mm) hazırlandı. Tüm abutment tasarımlarının üzerine, ZLS materyalinden iki farklı kalınlıkta (1,0 mm ve 1,5 mm) kuron örnekleri hazırlandı. Oluşturulan hibrit abutment-kuron konfigürasyonlarının spektrofotometrik analizleri yapıldı ve CIEDE2000 (ΔE00) formülü yardımıyla renk değişimi hesaplandı. Parametrelerin normal dağılıma uygunluğu Kolmogorov-Smirnov ve Shapiro Wilks testleri ile istatistiksel olarak değerlendirilmiştir. Materyal ve kalınlık etkileşiminin L*, C*, h* ve ∆E00 üzerindeki etkisi Two-way ANOVA testi ile değerlendirilmiş, post hoc analizlerde Tukey HSD test kullanılmıştır (p˂0,05). Bulgular: Hibrit abutmentları oluşturan materyallerin türünün ve üst yapı restorasyon kalınlığının; final restorasyonun L*, C*, h* ve ∆E00 üzerinde anlamlı etkisi olduğu görüldü (p˂0,05). 1,0 mm ZLS kuron gruplarındaki ΔE00 değerleri en düşükten yükseğe doğru; Z1 (Zr; ΔE00=1,88), L1 (LDS; ΔE00=2,29), V1 (PICN; ΔE00=2,36), P1 (PEEK; ΔE00=3,04) şeklinde sıralandı. 1,5 mm ZLS kuron gruplarındaki ΔE00 değerleri ise; Z2 (Zr; ΔE00=1,34), L2 (LDS; ΔE00=1,37), V2 (PICN; ΔE00=1,37), P2 (PEEK; ΔE00=2,87) şeklinde sıralandı. Bütün gruplardaki renk değişimi algılanabilirlik eşiğinin üzerindedir (ΔE00>0,8). Z2, V2 ve L2'nin ΔE00 değerinin kabul edilebilirlik eşiğinin altında olduğu tespit edildi (ΔE00<1,8). Sonuç: Farklı optik özelliklere sahip altyapı materyalleri üzerine yerleştirilen ZLS kuronların, kalınlıklarının artırılması ile kabul edilebilir estetik sonuçlara ulaşılabilir. Ancak PEEK ile oluşturulan hibrit abutmentlar, kabul edilebilirlik eşiğinin üzerinde gösterdiği sonuçlardan dolayı estetik olarak önerilmemektedir(ΔE00>1,8).
Özet (Çeviri)
Aim: The aim of this study is to examine and compare the optical properties of hybrid abutment samples prepared with different materials with zirconia-reinforced lithium silicate ceramic (ZLS) crowns of different thicknesses in vitro with spectrophotometric analyzes. Materials and Methods: 80 hybrid abutment specimens were obtained by placing sections (12x14x0.7 mm; n=10) prepared from lithium disilicate (LDS), hybrid ceramic (PICN), polyetheretherketone (PEEK) and zirconia (Zr) materials on titanium substructures (12x14x1.0 mm). 20 Zr specimens (12x14x1.8 mm) were prepared representing ceramic abutments. Then, crown samples of two different thicknesses (1.0 mm and 1.5 mm) were prepared from ZLS blocks. Hybrid abutment-crown configurations were created by placing these samples on the hybrid abutment and control groups samples. Spectrophotometric analyzes of the hybrid abutment-crown configurations were made and the color change was calculated with the help of the CIEDE2000 (ΔE00) formula. The suitability of the parameters to the normal distribution was evaluated statistically by Kolmogorov-Smirnov and Shapiro Wilks tests. The effect of material and thickness interaction on L, C, h and ∆E00 was evaluated with Two-way ANOVA test, Tukey HSD test was used in post hoc analyzes (p˂0.05). Results: It was observed that the type of abutment material and the thickness of the superstructure material were significant over L, C, h parameters ∆E00 value (p˂0.05). The ΔE00 values in the 1.0 mm ZLS crown groups, from lowest to highest, are Z1 (Zr; ΔE00=1.88), L1 (LDC; ΔE00=2.29), V1 (PICN; ΔE00=2.36), P1 (PEEK; ΔE00=3.04) sorted. The ΔE00 values in the 1.5 mm ZLS crown groups are Z2 (Zr; ΔE00=1.34), L2 (LDC; ΔE00=1.37), V2 (PICN; ΔE00=1.36), P2 (PEEK; ΔE00=2.87). The color change in all groups is above the perceptibility threshold (ΔE00>0.8). It was determined that the ΔE00 value of Z2, V2 and L2 was at a acceptability threshold (ΔE00<1.8). Conclusion: Acceptable aesthetic results can be achieved by increasing the thickness of ZLS crowns on coping materials with different optical properties. However, hybrid abutments created with PEEK are not recommended aesthetically due to results above the acceptability threshold (ΔE00>1.8).
Benzer Tezler
- Farklı hibrit abutmant prototiplerinin tam seramik kronların optik özellikleri üzerindeki etkilerinin in-vitro olarak değerlendirilmesi
In vitro evaluation of the effects of different hybrid abutment prototypes on optical properties of all ceramic crowns
YASEMİN AKBAŞ
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiBolu Abant İzzet Baysal ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ HAMİYET KILINÇ
- Dişsiz maxilla posterior bölgede implant üstü protetik tedavi yöntemlerinin implant ve çevresindeki kemik üzerinde oluşturduğu stresin sonlu elemanlaranalizi yöntemiyle karşılaştırılması
Comparison of the stress on the implant and surrounding bone with the finite ewlement analysis method of the prosthesis treatment methods on the implant in the edentulous maxilla posterior
YAKUP KAPTI
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. NURAN YANIKOĞLU
- “All-on-Four”hibrid protezler için farklı tekniklerle üretilen PEEK altyapının mekanik dayanım ve stres analizlerinin karşılaştırılması
Comparison of mechanical strength and stress analysis of PEEK framework manufactured with different techniques for“All-on-Four”hybrid prosthesis
MUSTAFA GÜRKAN
Doktora
Türkçe
2022
Diş HekimliğiEge ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. TOMURCUK ÖVÜL KÜMBÜLOĞLU
- Farklı yüzey işlemleri ve farklı siman tiplerinin, prefabrike plastik döküm şablonları kullanılarak hazırlanan implant üstü delikli kuronların retansiyonuna etkisi
The effect of surface treatment and cement type on the retention of cement-screw retained crowns
ÖZGE ASIM
Doktora
Türkçe
2023
Diş Hekimliğiİstanbul ÜniversitesiDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
PROF. DR. ONUR GEÇKİLİ
- Titanyum altyapı üzerinde kullanılan seramik abutmentların bağlantısına farklı universal adeziv sistemlerin etkisi
The effect of different universal adhesive systems on the bonding of ceramic abutments and titanium bases
HÜSNİYE YILDIRIM
Diş Hekimliği Uzmanlık
Türkçe
2020
Diş HekimliğiOrdu ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ AYÇA TULGA