Some aspects of chromium and silicon-aluminide coatings on 321 stainless steel alloy
321 paslanmaz çelik alaşim üzeri̇ne krom ve silikon-alüminid kaplamalarin bazi özelli̇kleri̇
- Tez No: 832021
- Danışmanlar: Prof. Dr. MOYAD A. MOHAMMED
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Paslanmaz çelik, Yüzey kaplama, Yüzey kaplama yöntemleri, Stainless steel, Surface coating, Surface coating methods
- Yıl: 1994
- Dil: İngilizce
- Üniversite: Unıversıty Of Mosul (جامعة الموصل)
- Enstitü: Yurtdışı Enstitü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Fizik Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Al alımını belirlemek ve ticari alaşım, 321 paslanmaz çelik üzerinde 800 ve 1000 oC'de üretilen alüminid, Cr-aluminid ve Si-alüminid kaplamayı karakterize etmek için deneysel çalışmalar yapılmıştır. Kaplanmış numuneler, onların performanslarını belirlemek için 1000 oC'de 500 saate kadar havada oksitlenmiştir. Al alımı, 1000 oC'de alüminid, Cr-alüminid ve Si-alüminid kaplamalar için sırasıyla 0.025, 0.016 ve 0.01 mg2.cm-4.sec-1 olan KP değerleri ile 800 ve 1000 oC'de parabolik bir ilişki izler. 800 oC'de üretilen kaplamalar, esas olarak, demirin Al açısından zengin intermetalik faz(lar)ına dayalı bir tabaka kaplama üretmek için Al'ın içe doğru difüzyonu ile oluşturulmuştur ve daha uzun bir işlem süresinde kararlı bir FeAl'e indirgenir. 1000 oC'de, sırasıyla alüminid, Si-alüminid ve Cr-alüminid için Al açısından zengin katı çözelti, Al açısından zengin FeAl, Fe2Al5 bazında çift katmanlı bir dış kaplama üretildi. İlk iki sistemde, dış katman, Al'ın baskın olarak içeriye doğru difüzyonu ile az miktarda Fe'nin karşı akım difüzyonu ile oluşturulurken Cr-alüminid sistemlerinde, dış katman, esas olarak Fe'nin bir miktar karşı akım difüzyonu ile dışa doğru difüzyonu ile oluşturulmuştur. Al'in karşı akım difüzyonunun Fe'nin dışa doğru difüzyonu, Fe açısından zengin intermetalik faz(lar)ın iç tabaka oluşumundaki ana süreçtir. Fe'nin dışa doğru difüzyonu da kaplama bozulmasına yol açar.
Özet (Çeviri)
Experimental studies have been made to determine the Al uptake, and characterize the aluminide, Cr- aluminide and Si- aluminide coating produce on commercial alloy, 321 stainless steel at 800 and 1000 oC. The coated specimens have been oxidized in air for up to 500h at 1000 oC in order to ascertain their performance. The Al uptake follows a parabolic relationship at 800 and 1000 oC with KP values being 0.025, 0.016, and 0.01 mg2.cm-4.sec-1 for the aluminide, Cr-aluminide, and Si- aluminide coatings at 1000 oC respectively. The coatings produced at 800 oC were formed mainly by inward diffusion of Al to produce one layer coating based on Al-rich intermetallic phase(s) of iron and degraded to a stable FeAl on a longer time of treatment. At 1000 oC a double layer coating were produced the outer layer based on Al-rich solid- solution, Al-rich FeAl, Fe2Al5 for the aluminide, Si- aluminide, and Cr- aluminide respectively. In the first two systems, the outer layer was formed by predominant inward diffusion of Al with a small amount of counter-current diffusion of Fe, but in Cr-aluminide systems, the outer layer was formed by mainly outward diffusion of Fe with an amount of counter-current diffusion of Al. Outward diffusion of Fe is the main process in the inner layer formation of Fe-rich intermetallic phase(s). The outward diffusion of Fe also leads to coating degradation
Benzer Tezler
- Ulaş Sağlık Ocağı merkezinde nüfusun bazı niteliklerine ve konutların durumuna ilişkin bir çalışma
An Investigation carried out at the Ulaş Public Health Centre concerning some characteristics of the population and housing conditions in the district of Ulaş
EROL ŞANLI
Doktora
Türkçe
1985
Halk SağlığıCumhuriyet ÜniversitesiHalk Sağlığı Ana Bilim Dalı
DOÇ. DR. SERVET ÖZGÜR
- İzmir'de bazı yolların kapatılarak yaya bölgeleri oluşturma da kent peyzajını geliştirme açısından yeniden planlanması üzerinde araştırmalar
Başlık çevirisi yok
BAHAR TÜRKYILMAZ
Yüksek Lisans
Türkçe
1985
Şehircilik ve Bölge PlanlamaEge ÜniversitesiŞehir ve Bölge Planlama Ana Bilim Dalı
- Bazı esterlerin kinetik incelenmesi ve termodinamik parametrelerin belirlenmesi
Kinetic study and detesmination of thermodnamic parameters of some esters
İBRAHİM TAŞ
Yüksek Lisans
Türkçe
1986
Kimya MühendisliğiUludağ ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MUSTAFA CEBE
- Çoklu amaçların çözümlemesinde amaç programlaması ile genelleştirilmiş ters yaklaşımı ve yem sanayiinde bir uygulama
Goal programming and generalieed inverse approaches in the multi-objective analysis and application in feed industry
HASAN BAL