Mekanik alaşımlama ile üretilen nanoyapılı Al-Cu-Ni-Si alaşım tozlarının mikroyapısal ve termal karakterizasyonu
Microstructural and thermal characterization of nano-structured Al-Cu-Ni-Si alloy powders produced by mechanical alloying
- Tez No: 820516
- Danışmanlar: DOÇ. DR. MUSTAFA OKUMUŞ
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Diferensiyel termal analiz, Mekanik alaşımlama, Mikrosertlik, Differential thermal analysis, Mechanical alloying, Microhardness
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Batman Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tez çalışmasında eşit atomik oranda AlCuNiSi orta entropili alaşımları farklı öğütme sürelerinde mekanik alaşımlama tekniği ile nanoyapılı toz olarak üretildi. Üretilen orta entropili nanoyapılı tozlarının mikroyapısal karakterizasyonu X-ışını kırınımı (XRD) ve taramalı elektron mikroskobu/enerji dağıtıcı X-ışını (SEM/EDX) analizleri ile yapıldı ve ayrıca termal karakterizasyonu diferansiyel termal analiz (DTA) ile yapıldı. XRD sonuçları mekaniksel alaşımlama sonucunda 50-140 saat öğütmelerde intermetalik Al2Cu, AlNi, AlNi3 ve fcc yapılı Cu bazlı katı çözelti fazlarının oluştuğunu gösterdi. Ayrıca XRD sonuçlarına göre öğütme süresi arttıkça alaşım tozlarında tane boyutunda küçülme olmuştur. 140 saat mekaniksel öğütme sonucunda kristal boyutunun yaklaşık 3nm, kafes geriniminin %1,15 ve diskolasyon yoğunluğu 0,11x10^18/m2 olduğu bulundu. SEM/EDX analizleri öğütme süresi arttıkça alaşım tozlarında parçalanma, kırılma, topaklaşma ve kaynaklaşmalar olduğunu, ve buna bağlı olarak partikül boyutunun küçüldüğünü ve daha homojen bir yapı oluştuğunu gösterdi. DTA sonuçları sürekli ısıtma esnasında 750-800 oC sıcaklık aralığında faz dönüşümü ve kristalleşmeleri işaret eden bir dizi endotermik pikler göstermiştir. Elde edilen sonuçlara göre 140 saat öğütme ile üretilen AlCuNiSi alaşımın mikroyapısal özelliklerinin bu çalışmada üretilen diğer tüm alaşımların mikroyapısal özelliklerinden daha üstün olduğu anlaşılmıştır.
Özet (Çeviri)
In this thesis, AlCuNiSi medium entropy alloys with equal atomic ratio were produced as nanostructured powder by mechanical alloying technique at different milling times. Microstructural characterization of the produced mid-entropy nanostructured powders was performed by X-ray diffraction (XRD) and scanning electron microscopy/energy dispersive X-ray (SEM/EDX) analyzes, and also thermal characterization was performed by differential thermal analysis (DTA). XRD results showed that as a result of mechanical alloying, intermetallic Al2Cu, AlNi, AlNi3 and fcc structure Cu based solid solution phases were formed during milling for 50-140 h. In addition, according to the XRD results, as the milling time increased, the particle size of the alloy powders decreased. After 140 h of mechanical milling, it was found that the crystallite size was approximately 3nm, the lattice strain was 1.15%, and the discollation density was 0.11x10^18/m2. SEM/EDX analyzes showed that as the milling time increased, fragmentation, breakage, aggregation and cold-welds occurred in the alloy powders, and accordingly the particle size decreased and a more homogeneous structure was formed. DTA results showed a series of endothermic peaks indicating phase transformation and crystallization during continuous heating at a temperature range of 750-800 oC. According to the results obtained, it was understood that the microstructural properties of the AlCuNiSi alloy produced by milling for 140 h were superior to the microstructural properties of all other alloys produced in this study.
Benzer Tezler
- Kobalt esaslı nanoyapılı heusler alaşımların üretimi, yapısal ve morfolojik özelliklerinin incelenmesi, radyasyon zırhlama karakteristiklerinin belirlenmesi
Production of cobalt based nano-structure heusler alloys, investigation of their structural and morphological properties, determination of radiation shielding characteristics
EMİNE NARMANLI HAN
Doktora
Türkçe
2024
Fizik ve Fizik MühendisliğiAtatürk ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. ELİF BOYDAŞ
- Mekanik alaşımlanmış intermetalik toz ve sinter Ti-47-5Al-3Cr alaşımının analitik elektron mikroskop ve x-ışınları teknikleri ile karakterizasyonu
Analytical election microscope and x-ray diffraction characterization of mechanically alloyd intermetallic Ti-47-5Al-3Cr powder and sinter
ARDA GENÇ
- Nanoyapılı metalik alaşımlar
Nanostructured metallic alloys
BARIŞ AVAR
Doktora
Türkçe
2012
Fizik ve Fizik MühendisliğiKahramanmaraş Sütçü İmam ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. MUSA GÖĞEBAKAN
- Titanyum (Ti) katkılı AlCoCuNi yüksek entropili alaşımların mekaniksel alaşımlama ile üretilmesi ve karakterizasyonu
Production and characterization of titanium (Ti) doped AlCoCuNi high entropy alloys by mechanical alloying
FEYZULLAH KAYA
Yüksek Lisans
Türkçe
2021
Makine MühendisliğiBatman ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. MUSTAFA OKUMUŞ
- FeNiCoCu yüksek entropili alaşımlarının ultrasonik sprey piroliz tekniği ile üretimi ve karakterizasyonu
Production and characterization of FeNiCoCu high entropy alloys via ultrasonic spray pyrolysis method
BURAK KÜÇÜKELYAS
Yüksek Lisans
Türkçe
2018
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. SEBAHATTİN GÜRMEN