Rezin kompozitlerin renk değişimi ve yüzey pürüzlülüğü üzerine farklı bitirme ve polisaj uygulaması ile hızlandırılmış yaşlandırmanın etkilerinin in vitro olarak incelenmesi
Investigation of the effects of different finishing and polishing and accelareted aging on color change and surface roughness of rezin composites in vitro
- Tez No: 819949
- Danışmanlar: PROF. DR. OYA BALA
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental materyaller, Dental restorasyon, Kompozit reçineler, Yapay yaşlandırma, Yüzey pürüzlülüğü, İn vitro, Dental materials, Dental restoration, Composite resins, Artificial aging, Surface roughness, In vitro
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu in vitro çalışmanın amacı, farklı polisaj sistemlerinin ve hızlandırılmış yapay yaşlandırma (HYY) testine maruz bırakılmanın rezin kompozitlerin renk değişikliği ve yüzey pürüzlülüğü üzerine etkisini incelemektir. Yöntem: Çalışmada 8 mm çapında, 2 mm derinliğinde plexiglas kalıplar kullanıldı. Test edilen her rezin kompozit için 60 adet örnek hazırlandı. Takiben, hazırlanan örnekler her rezin kompozit için beş alt gruba ayrıldı. Grup 1'de; örnek yüzeylerine herhangi bir polisaj uygulanmayarak kontrol grubu oluşturuldu. Grup 2'de; Clearfil Twist Dia, Grup 3'de; Pogo, Grup 4'de; Sof-Lex ve Grup 5'de; Super Snap kullanılarak örnek yüzeylerine polisaj uygulaması yapıldı. Daha sonra, rezin kompozit örneklerin renk ölçümleri spektrometre cihazı ile yüzey pürüzlülük ölçümleri ise profilometre cihazı kullanılarak gerçekleştirildi. Takiben, tüm örnekler HYY testine maruz bırakıldıktan sonra, tekrar renk ölçümleri ve yüzey pürüzlülük ölçümleri alındı ve elde edilen değerler kaydedildi. Elde edilen veriler istatistiksel olarak %95 güven aralığında analiz edildi. Bulgular: Tüm polisaj gruplarında, polisaj sonrası, HYY sonrası ve polisaj sonrası ile HYY sonrası renk değişimini gösteren ΔE değerlerinin test edilen rezin kompozitler arasında farklılık gösterdiği görüldü (p<0,05). Test edilen tüm rezin kompozitlerde, polisaj sonrası (G hariç), HYY sonrası ve polisaj sonrası ile HYY sonrası renk değişimini gösteren ΔE değerlerinin polisaj grupları arasında farklılık gösterdiği tespit edildi (p<0,05). Ayrıca, test edilen tüm rezin kompozitlerin her birinden elde edilen yüzey pürüzlülük değerlerinin polisaj grupları arasında farklılık olduğu görüldü (p<0.05). G ve GD haricinde, diğer rezin kompozitlerde kontrol grubunda anlamlı olarak daha düşük yüzey pürüzlülük değerleri elde edildi (p<0.05). Tüm polisaj gruplarında, test edilen rezin kompozitlerin pürüzlülük değerleri arasında anlamlı farklılığın olduğu tespit edildi (p<0.05). HYY sonrasında da rezin kompozitlerin (PE haricinde) yüzey pürüzlülük değerlerinin polisaj grupları arasında farklılık olduğu tespit edildi (p<0.05). Ayrıca, test edilen rezin kompozitlerin pürüzlülük değerlerinin arasında da farklılık olduğu görüldü (p<0.05). Sonuç: Bu çalışmanın sınırları dahilinde, rezin kompozitlerin renk değişimi ve pürüzlülüğünün kullanılacak rezin kompozitin yapısından ve polisaj sisteminin özelliklerinden etkilediği, ancak test edilen rezin kompozitlerin renk değişiminde, yüzey pürüzlülüğünden ziyade rezin kompozitin yapısının daha önemli rol oynadığı söylenebilir.
Özet (Çeviri)
Objectives: The aim of this in vitro study is to examine the effect of different polishing systems and exposure to the accelerated artificial aging (AAA) test on the color change and surface roughness of resin composites. Methods: In the study, plexiglass molds with a diameter of 8 mm and a depth of 2 mm were used. For each resin composite tested, 60 samples were prepared. Subsequently, the prepared samples were divided into five subgroups for each resin composite. In Group 1; The control group was formed by not applying any polishing to the sample surfaces. The sample surfaces were polished with Clearfil Twist Dia (in Group 2), Pogo (in Group 3), Sof-Lex (in Group 4) or Super Snap (in Group 5). Then, the color measurements of the resin composite samples were measured using a spectrometer device and the surface roughness measurements were measured using a profilometer device. Subsequently, after all samples were exposed to the AAA test, color measurements and surface roughness measurements were taken again and the obtained values were recorded. The obtained data were statistically analyzed at 95% confidence interval. Results: In all polishing groups, ΔE values showing the color change after polishing, after AAA, after polishing and AAA were found to differ between the tested resin composites (p<0.05). In all tested resin composites, ΔE values showing the color change after polishing (except G), after AAA, after polishing and after AAA were found to differ between polishing groups (p<0.05). In addition, it was observed that there was a significant difference between the polishing groups in the surface roughness values obtained from each of the tested resin composites (p<0.05). Except for G and GD, other resin composites had significantly lower roughness values in the control group (p<0.05). It was determined that there was a significant difference between the roughness values of the tested resin composites in all polishing groups (p<0.05). It was determined that the surface roughness values of the resin composites (except PE) were also different between the polishing groups after AAA (p<0.05). In addition, it was observed that the roughness values of the tested resin composites were different from each other (p<0.05). Conclusions: Within the limits of this study, it can be said that the color change and roughness of the resin composites are affected by the structure of the resin composite to be used and the properties of the polishing system, but the structure of the resin composite rather than the surface roughness plays a more important role in the color change of the tested resin composites.
Benzer Tezler
- Rezin kompozit yüzeylerinde modelasyon likiti ve adeziv ajan kullanılmasının pürüzlülük renk stabilitesi ve mikrosertlik üzerine etkilerinin incelenmesi
Examination of the effects of modeling liquid and adhesive agents on surface roughness, color stability and microhardness of resin composite surfaces
MERT KARAKAŞ
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiGazi ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. HACER DENİZ ARISU
- Farklı içeceklerde bekletilen restoratif materyallerin yüzey pürüzlülüğü ve renk stabilitesinin değerlendirilmesi
Evaluation of surface roughness and color stability of restorative materials soaked in different beverages
ZEYNEP BİÇER
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiEskişehir Osmangazi ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. BATU CAN YAMAN
- Farklı polisaj sistemlerinin ve yaşlandırmanın tek renk üniversal rezin kompozitlerin yüzey pürüzlülüğü ve renk parametreleri üzerine etkisi
The effect of different polishing systems and aging on surface roughness and color parameters of single-shade universal resin composites
AYŞE İREM YETİŞ
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiGazi ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. OYA BALA
- Farklı solüsyonların tek renkli üniversal kompozit materyallerin renk stabilitesi üzerine etkilerinin ı̇ncelenmesi
Effects of different solutions on the color stability of single-shade universal composite materials
EZGİ ACAR
Doktora
Türkçe
2025
Diş HekimliğiMarmara ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. BİLGE TARÇIN
- Farklı cila pastaları eşliğinde uygulanan polisaj sistemlerinin, üniversal ve akışkan kompozitlerin yüzey pürüzlülüğüne ve renk stabilitesine etkisinin incelenmesi
Investigation of the effects of polishing systems applied with different polishing pastes on the surface roughness and color stability of universal and flowable composites
KERİM SAFA KUL
Diş Hekimliği Uzmanlık
Türkçe
2026
Diş HekimliğiUşak ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
PROF. DR. MUHAMMET KERİM AYAR