CAD-CAM sistemi ile üretilen implant üstü köprü restorasyonlarda bükülme ve kırılma dayanımına konnektör tasarımının etkisi

The effect of connector design on flexural and fracturestrength in implant-supported bridge restorationsmanufactured with CAd-CAM system

PDF İndir

  1. Tez No: 808910
  2. Yazar: BESTE ÇETİN
  3. Danışmanlar: DOÇ. DR. ÖZGE PARLAR ÖZ
  4. Tez Türü: Diş Hekimliği Uzmanlık
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: monolitik zirkonya, lityum disilikat, ti-base abutment, konnektör, dayanım, CAD/CAM, Dental destekler, Dental implantasyon, Dental protezler, Dental restorasyon, Dental stres analizi, Protezler ve implantlar, Zirkonyum, monolithic zirconia, lithium disilicate, ti-base abutment, connector, strength, CAD/CAM, Dental abutments, Dental implantation, Dental prosthesis, Dental restoration, Dental stress analysis, Prostheses and implants, Zirconium
  7. Yıl: 2023
  8. Dil: Türkçe
  9. Üniversite: Gaziantep Üniversitesi
  10. Enstitü: Diş Hekimliği Fakültesi
  11. Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Bu çalışmanın amacı ti-base dayanaklar üzerine CAD-CAM sistemi kullanılarak üretilen üç üyeli monolitik zirkonya (VITA YZ ST) ve lityum disilikat esaslı (e.max Press) restorasyonların farklı konnektör kesit alanlarındaki kırılma ve bükülme dayanımlarını in-vitro olarak araştırmaktır. 12 adet implant analoğu ikişerli olacak şekilde akrilik modeller içine yerleştirildi. Analoglar üzerine ti-base dayanaklar torklandıktan sonra dijital ölçüleri alındı. Köprü dizaynı; maksiller kanin ve 2. premolar dayanak, 1. premolar ise gövde olacak şekilde planlandı. Toplam grupta 42 adet örnek hazırlandı materyal çeşidine göre 2 gruba (n=21) ayrıldı, sonrasında her grup konnektör kesit alanına göre 3 alt gruba ayrıldı (n=7) (monolitik zirkonya için 9 mm 2 , 12 mm 2 , 15 mm 2 ; lityum disilikat için 12 mm 2 , 16 mm 2 , 20 mm 2 ). Örneklere 5-55 °C sıcaklıkta 5000 döngü termal siklus uygulandı. Hazırlanan örnekler universal test cihazında kırılma dayanım testine tabi tutuldu. Sonuçlar formülize edilerek bükülme dayanım verilerine ulaşıldı. İki bağımsız grup arasında farklılık olup olmadığı Mann Whitney U, ikiden fazla bağımsız grup arasında farklılık olup olmadığı ise Kruskal Wallis Testi ile incelendi (p=0.05). Ortalama kırılma ve bükülme dayanım değerleri monolitik zirkonya örneklerde sırasıyla; 1207.21 N (9 mm 2 ), 1594.59 N (12 mm 2 ), 2074.67 N (15 mm 2 ) ve 99.77 MPa (9 mm 2 ), 107.16 MPa (12 mm 2 ), 113.32 MPa (15 mm2), lityum disilikat esaslı örneklerde ise sırasıyla; 500.84 N (12 mm 2 ), 685.75 N (16 mm 2 ), 859.94 N (20 mm 2 ) ve 33.66 MPa (12 mm 2 ), 37.46 MPa (16 mm 2 ), 37.61 MPa (20 mm 2 ) bulunmuştur. Monolitik zirkonya materyalinin kırılma ve bükülme dayanımı lityum disilikat materyalinden istatistiksel olarak anlamlı derecede daha fazladır (p<0,05). Sonuç olarak konnektör kesit alanının artması dayanımı anlamlı derecede arttırmaktadır (p<0,05). Posterior bölgede monolitik zirkonya köprüler kesinlikle tavsiye edilirken lityum disilikat köprüler de yeterli konnektör kesit alanına sahip ise tavsiye edilebilir.

Özet (Çeviri)

The aim of this in-vitro study is to investigate the fracture and flexural strength of three- unit implant supported fixed dental prostheses (monolithic zirconia (VITA YZ ST) and lithium disilicate-based (e.max Press)) restorations at different connector cross-sectional area, produced on ti-base abutments using the CAD-CAM system. 12 implant analogues were placed in acrylic models in pairs. After the ti-base abutments were torqued on the analogs, their digital impressions were taken. Bridge design was planned; maxillary canine and 2nd premolar as abutment and 1st premolar as pontic. In the total group, 42 samples were manufactured and divided into 2 groups (n=21) according to the material type, then each group was divided into 3 subgroups (n=7) according to the connector cross-sectional area (9 mm 2 , 12 mm 2 , 15 mm 2 for monolithic zirconia; for lithium disilicate 12 mm 2 , 16 mm 2 , 20 mm 2 ). A thermal cycle of 5000 cycles was applied to the samples at a temperature of 5-55 °C. Prepared specimens were subjected to fracture strength test at a universal test machine. The results were formulated and flexural strength data were obtained. Differences between two independent groups were analyzed using Mann Whitney U, and whether there was a difference between more than two independent groups using the Kruskal Wallis Test (p=0.05). Average fracture and flexural strength values in monolithic zirconia samples are respectively; 1207.21 N (9 mm 2 ), 1594.59 N (12 mm 2 ), 2074.67 N (15 mm 2 ) and 99.77 MPa (9 mm 2 ), 107.16 MPa (12 mm 2 ), 113.32 MPa (15 mm 2 ) in lithium disilicate based samples; 500.84 N (12 mm 2 ), 685.75 N (16 mm 2 ), 859.94 N (20 mm 2 ) and 33.66 MPa (12 mm 2 ), 37.46 MPa (16 mm 2 ), 37.61 MPa (20 mm 2 ). The fracture and flexural strength of monolithic zirconia material was statistically significantly higher than that of lithium disilicate material (p<0.05). As a result, increasing the connector cross-sectional area increases the strength significantly (p<0.05). In the posterior region, monolithic zirconia bridges are strongly recommended, while lithium disilicate bridges can be recommended if they have sufficient connector cross-sectional area.

Benzer Tezler

  1. Tez No

    365382

    Farklı CAD/CAM blokları kullanılarak restore edilen implant üstü kronlarda termal siklusun kırılma dayanımına etkisi

    Thermal cycle effect on fracture strength of implant supported crowns restorated with different CAD/CAM blocks

    BURCU MUTAF

    Doktora

    Türkçe

    Türkçe

    2014

    Diş HekimliğiCumhuriyet Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. DERYA ÖZDEMİR DOĞAN

  2. Tez No

    674728

    Farklı tekniklerle üretilmiş implant üstü dayanak ve kronların in-vitro olarak karşılaştırılması

    In-vitro comparison of implant-supported single crowns and abutments manifactured with different techniques

    İREM ÇÖTERT MERCAN

    Doktora

    Türkçe

    Türkçe

    2021

    Diş HekimliğiEge Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. MÜBİN SITKI ULUSOY

  3. Tez No

    443780

    CAD/CAM sistemi ile üretilen cam seramik köprü restorasyonlarda üye sayısının ve konnektör tasarımının kırılma dayanımı üzerine etkisi

    Effect of connector design and unit number on fracture strength of CAD/CAM glass ceramic bridges

    KADER TATAR

    Doktora

    Türkçe

    Türkçe

    2016

    Diş HekimliğiYüzüncü Yıl Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. GÜRCAN ESKİTAŞÇIOĞLU

  4. Tez No

    453903

    İmplant destekli sabit protezlerde CAM/CAM sistemleri ile üretilen destek ve üst yapı restorasyonlarının sonlu elemanlar stres analiz yöntemi ve kırılma direnci testi ile karşılaştırmalı olarak incelenmesi

    The comparatively investigation of abutment and crown restorations produced by CAD/CAM systems in implant supported fixed prostheses using the finite element stress analysis method and fracture resistance test

    NAZİRE ESRA BAĞDATLI

    Doktora

    Türkçe

    Türkçe

    2016

    Diş HekimliğiAnkara Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. AHMET ERSAN ERSOY

  5. Tez No

    388518

    CAD/CAM sistemi ile üretilmiş farklı yapıdaki seramik kronlarda siman film aralığı değişiminin renk ve dayanım üzerine etkisi

    The effect of the cement film thickness on colour and strentgh in different all ceramic crowns fabricated with CAD/CAM system

    ABDURRAHMAN ŞAHİNBAŞ

    Doktora

    Türkçe

    Türkçe

    2015

    Diş HekimliğiYüzüncü Yıl Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. GÜRCAN ESKİTAŞCİOĞLU

Geri Dön