Endodontik tedavi sonrası farklı materyal ve tekniklerle yapılan restorasyonların dişin kırılma dayanımına etkisi: İn vitro çalışma
The effect of restorations made with different materials and techniques after endodontic treatment on fracture strength: In vitro study
- Tez No: 803492
- Danışmanlar: PROF. DR. ALİ RIZA ÇETİN
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental restorasyon, Dental stres analizi, Endodonti, Kompozit malzemeler, Kompozit reçineler, Dental restoration, Dental stress analysis, Endodontics, Composite materials, Composite resins
- Yıl: 2023
- Dil: Türkçe
- Üniversite: Selçuk Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı: endodontik tedavi görmüş MOD kaviteli molar dişlerin farklı materyal ve teknik kullanılarak yapılan restorasyonlarının kırılma dayanımlarını ve tiplerini karşılaştırmaktır. 84 adet çekilmiş sağlam mandibular azı dişi rastgele 7 gruba (n = 12) ayrıldı. Grup 1'e herhangi bir preparasyon veya restorasyon yapılmadı. Grup 2-7 arasındaki dişlere MOD kavite preparasyonu , ve giriş kavitesi açılarak tek kon tekniği kullanılarak kök kanal tedavisi uygulandı. Restorasyon yapılacak gruplardaki dişlere aynı üniversal adeziv sistem kullanılarak restorasyona hazırlandı. Grup 2, Grup 3 ve Grup 5'teki dişler sırasıyla nano-hibrit kompozit (Clearfil Majesty™ posterior), mikro-hibrit kompozit(Nova Compo HS) ve mikro-hibrit kompozit (Essentia Universal) kullanılarak tabakalama tekniği ile restore edildi. Grup 4'teki dişler, bulk fill kompozit (3M™ Filtek One Bulk Fill) kullanılarak tek tabaka restore edildi. Grup 6 ve Grup 7'deki dişler, pulpa odasına ve dentin yerine fiberle güçlendirilmiş kompozit (everX Posterior) veya kısa fiberle güçlendirilmiş kompozit (everX Flow) onların üzerine de mine yerine mikro-hibrit kompozit (Essentia Universal) kullanılarak restore edildi. Bitim ve parlatma işlemlerinden sonra, her gruba 1 yıl yaşlandırmaya denk olan termal döngü ile yaşlandırma işlemi uygulandı. Daha sonra her dişe kırılıncaya kadar, üniversal kırma testi cihazında, oklüzal yüzeyine dik 5 mm çaplı bilye uçlu aparat kullanarak ve baş hızı 1 mm/dk olacak şekilde kuvvet uygulandı. Kırılma dayanımı verileri Newton cinsinden kaydedildi ve sonuçlar istatistiksel olarak SPSS 22 programında Friedman'nın İki Yönlü Varyans Analizi Testi kullanılarak değerlendirildi. Kırılma dayanımı değerlerinin ortalaması: Grup 1: 2854,9 ± 906,9 N, Grup 2: 1917,3 ± 277,4 N, Grup 3: 2216,7 ± 500,5 N, Grup 4: 2062 ± 405,3 N, Grup 5: 2124,6 ± 592,9 N, Grup 6: 12164,1 ± 591,7 N, Grup 7: 2049,5 ± 381,8 N olarak bulundu. Grup 1 en yüksek ve Grup 2 en düşük kırılma dayanım değeri gösterdi. Grup 1 ile, Grup 3 hariç diğer Gruplar arasında istatistiksel olarak anlamlı fark olduğu gözlendi. Grup 3 ise, sadece Grup 2'den istatistiksel olarak anlamlı daha yüksek kırılma dayanım değeri gösterdi (p> 0.05). Bu çalışmadaki hiçbir restorasyon grubu sağlam dişlerin kırılma değerini geri kazandıramadı. Bununla birlikte, Grup 3 (Nova Compo HS) kırılma dayanımı değerlerini en çok artıran grup olduğu için endodontik tedavi görmüş dişlerde restorasyon materyali olarak kullanımı önerilebilir.Bu çalışmada fiberle güçlendirilmiş kompozitlerde meydana gelen kırıkların diğer kompozit gruplarına göre daha kolay restore edilebilir kırıklar olduğu görüldü.
Özet (Çeviri)
The aim of this study is to compare the fracture strength and types of restorations of endodontically treated MOD cavity molars using different materials and techniques. 84 extracted intact mandibular molars were randomly divided into 7 groups (n = 12). Group 1 did not undergo any preparation or restoration. Root canal treatment was applied to the teeth in groups 2-7 using MOD cavity preparation and single cone technique by opening the access cavity. The teeth in the groups to be restored were prepared for restoration using the same universal adhesive system. The teeth in Group 2, Group 3 and Group 5 were restored by layering technique using nano-hybrid composite (Clearfil Majesty™ posterior), micro-hybrid composite (Nova Compo HS) and micro-hybrid composite (Essentia Universal), respectively. The teeth in group 4 were restored in a single layer using bulk fill composite (3M™ Filtek One Bulk Fill). Fiber reinforced composite (everX Posterior) or short fiber reinforced composite (everX Flow) was applied to the pulp chamber and dentin instead of teeth in Group 6 and Group 7. On these composites, micro-hybrid composite (Essentia Universal) was used instead of enamel. After finishing and polishing, aging was applied to each group by thermal cycling, which is equivalent to aging for 1 year. Then, force was applied to each tooth until it broke, using smashing head with a ball tip with a diameter of 5 mm perpendicular to the occlusal surface in a universal fracture test device, with a cross-head speed of 1 mm/min. Fracture strength data were recorded in Newtons and the results were statistically evaluated using Friedman's Two-Way Analysis of Variance Test in SPSS 22 program. Mean breaking strength values: Group 1: 2854.9 ± 906.9 N, Group 2: 1917.3 ± 277.4 N, Group 3: 2216.7 ± 500.5 N, Group 4: 2062 ± 405.3 N , Group 5: 2124.6 ± 592.9 N, Group 6: 12164.1 ± 591.7 N, Group 7: 2049.5 ± 381.8 N. Group 1 showed the highest and Group 2 showed the lowest breaking strength value. It was observed that there was a statistically significant difference between Group 1 and the other Groups except Group 3. Group 3, on the other hand, showed a statistically significantly higher fracture strength value than only Group 2 (p> 0.05). Non- restorated group in this study was able to restore the fracture value of intact teeth. However, since Group 3 (Nova Compo HS) is the group that increases the fracture strength values the most, it can be recommended to be used as a restoration material in endodontically treated teeth. In this study, it was observed that fractures in fiber reinforced composites were more repairable than other composite groups.
Benzer Tezler
- Tüberkül kaplama tekniğinin mezyo-okluzo-distal kaviteli kanal tedavili dişlere uygulanan restorasyonların kırılma dayanımı üzerindeki etkisi
Effect of cuspal coverage on the fracture strength ofthe restorations of endodontically treated teeth withmod cavities
HALE BAŞGÜL
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş Hekimliğiİzmir Katip Çelebi ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. BİLAL YAŞA
- Farklı kök kanal doldurma teknikleri uygulanarak doldurulan oval yapılı kök kanallarının farklı retreatment prosedürleri sonrası kök kanallarında kalan kanal dolgusu miktarının ve uzaklaştırma sürelerinin karşılaştırılması
Comparison of the amount of residual filling and removal time after different retreatment procedures of oval root canals obturated with different root canal filling methods
ALPER İLKER
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiOrdu ÜniversitesiEndodonti Ana Bilim Dalı
YRD. DOÇ. DR. EVREN SARIYILMAZ
- İki kök kanal patı kullanılarak farklı kök kanal dolgu yöntemlerinin endodontik tedavi görmüş köklerin kırılma direncine olan etkisinin incelenmesi
Evaluation of the effect of different root canal obturation techniques using two root canal sealers on the fracture resistance of endodontically treated roots
İBRAHİM ERSOY
Doktora
Türkçe
2013
Diş HekimliğiAtatürk ÜniversitesiEndodonti Ana Bilim Dalı
DOÇ. DR. MEHMET SİNAN EVCİL
- Farklı seviyelerde kök kanal kalsifikasyonu olan dişlerde rehberli endodonti tekniği kullanılarak açılan giriş kavitelerinin geleneksel giriş kaviteleriyle karşılaştırılması
Comparison of access cavities prepared using the guided endodontc technique and conventional access in teeth with different levels of root canal calcification
NAGİHAN KARA ŞİMŞEK
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiOrdu ÜniversitesiEndodonti Ana Bilim Dalı
DOÇ. DR. LEYLA BENAN AYRANCI
- Kanal dolgu tekniklerinin ve kanal dolgu patlarının apikalden taşan debris ve kanal dolgusunun sökülebilirliğindeki rolleri
Başlık çevirisi yok
DENİZ BENDER
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiHacettepe ÜniversitesiEndodonti Ana Bilim Dalı
DOÇ. DR. EMEL UZUNOĞLU ÖZYÜREK