Yüksek sıcaklık YBa CuO süperiletken sisteminde yittrium yerine yaklaşık yarıçaplı farklı oksitlerin katılması ve yeni sistemin özelliklerinin belirlenmesi
Başlık çevirisi mevcut değil.
- Tez No: 77913
- Danışmanlar: DOÇ. DR. M. EYYÜPHAN YAKINCI
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Süperiletkenlik, Y-Ba-Cu-O sistemi, Katıhal reaksiyon metodu, Süper iletkenler, İtriyum, Superconductivity, Y-Ba-Cu-O System, Solid State Method, Superconductors, Yttrium
- Yıl: 1998
- Dil: Türkçe
- Üniversite: İnönü Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
IV ÖZET: Bu tez çalışmasında, YBa2Cu307.x süperiletken sisteminde, yittrium yerine yaklaşık aynı iyonik yarıçapa sahip olan vanadyum ve kadmiyum oksitleri ayrı ayrı, %20-%100 oranlarında katılmış ve ortaya çıkarılan yeni sistemler 'Katıhal reaksiyonu' metodu ile hazırlanmıştır. Her bir sistem için uygun ısıl işlem sıcaklıkları tesbit edilmiş ve ısıl işlemlerin tamamı oksijen atmosferinde gerçekleştirilmiştir. Hem ısıl işlemler hem de artan katkı oranlarının üretilen sistemler üzerinde meydana getirdikleri değişimler, taramalı elektron mikroskopu (SEM), enerji dağılımlı X-ışınları analizi (EDAX), X-ışınları kırınımı (XRD) ve Direnç-Sıcaklık (R-T) ölçüm metodları ile karakterize edilmiştir. Her iki katkılama sonucunda ortaya çıkan sistemlerin ancak belirli bir iyonik çözürnürlük limitine sahip olduğu, limitler dahilinde her iki sistemin çeşitli sıcaklıklarda süperiletkenlik gösterdiği, limitler aşıldığında ise süperiletkenlikle birlikte metalik özellikten de uzaklaşıldığı ve yarıiletkenlik özelliklerine bir dönüşümün olduğu bulunmuştur. Bu sonuçların netliği deneyler sırasında kullanılan bütün yöntemler ile desteklenmiştir.
Özet (Çeviri)
ABSTRACT: In this study, in YBa2Cu307_x system, instead of Yittrium oxide, Vanadium and cadmium oxides, which have nearly the same ionic radius, were added sperately with ratio of %20-%100 and the new systems obtained have been prepared by solid state method. For each a system, a suitable heat..treatment schedule was developed and all heatings were carried out in Oxygen atmosphere. The changes occurred during the heat treatments and increasing additive ratios were characterized by Scanning Electron Microscope (SEM), Energy Dispersive of X-Ray Analysis (EDAX), X-Ray Diffraction (XRD) and Resistivity-Tempareture (R-T) measurements. It was found that, for both additions, the systems obtained have a significant ionic solution limit, below the limit both system showed superconductivity in various temperatures but, over these limits, superconductivity including the metallic property of samples were disappeared and a transition to semiconductivity was occurred. These results were supported by all analysis method used during the experiments
Benzer Tezler
- Y-Ba-Cu-O sisteminde süperiletkenlik
Başlık çevirisi yok
CABİR TERZİOĞLU
Yüksek Lisans
Türkçe
1992
Fizik ve Fizik MühendisliğiKaradeniz Teknik ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. MUSTAFA ALTUNBAŞ
- Yüksek kritik sıcaklıklı üstüniletken seramik filmlerin elektriksel özellikleri
Başlık çevirisi yok
ATİLLA KILIÇ
Doktora
Türkçe
1993
Fizik ve Fizik MühendisliğiHacettepe ÜniversitesiFizik Ana Bilim Dalı
DOÇ. DR. NECDET BAŞTÜRK
- Y, BaF2 ve Cu'ın beraberce buharlaştırılması ile hazırlanan üstüniletken filmlerin karekterizasyonu
Characterization of Y-Ba-Cu-O superconducting films prepared by coevaporation of Y, BaF2 and Cu
ERDAL KAYNAK
- Gümüş difüzyonunun YBaCuO süperiletkenlerinin yapısal ve süperiletkenlik özelliklerine etkisi
Başlık çevirisi yok
UĞUR KÖLEMEN
Yüksek Lisans
Türkçe
1996
Fizik ve Fizik MühendisliğiKaradeniz Teknik ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. MUSTAFA ALTUNBAŞ
- Turbostratik bor nitrüt'ün kritalizasyon davranışı ve karakterizasyonu
Başlık çevirisi yok
SEDAT ALKOY