Farklı yüzey işlemleri uygulanan seramiklerin termal yaşlandırma sonrası bağlanma dayanımının değerlendirilmesi
Effects of surface treatments on the SHEAR bond strength of ceramics after thermal aging
- Tez No: 769497
- Danışmanlar: PROF. DR. ASUDE DİLEK NALBANT
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental bonding, Dental porselen, Dental stres analizi, Yapay yaşlandırma, Yüzey işleme tekniği, Dental bonding, Dental porcelain, Dental stress analysis, Artificial aging, Surface handling technique
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Gazi Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmasının amacı yüzey işlemi uygulamalarının seramiklerin (feldspatik seramik, rezin matriks infiltre cam seramik, rezin nanoseramik) siman bağlanma dayanımına etkisini ve meydana gelen başarısızlık tiplerini değerlendirmektir. Çalışmada Vitablock Mark II, Vita Enamic ve GC Cerasmart materyallerinden 14*12*2 mm boyutunda 30'ar adet örnek hazırlanmıştır (n=90). Örnekler uygulanan yüzey işlemlerine göre 3 alt gruba ayrılmıştır (n=30). Birinci gruptaki örneklere %10'luk HF asit; ikinci gruptaki örneklere Al2O3 ile kumlama; üçüncü gruptaki örneklere ise tribokimyasal silika ile kumlama uygulanmıştır. Yüzey işlemi uygulaması sonrasında tüm örneklerin yüzey pürüzlülüğü ölçümleri yapılmıştır. Örneklerin işlem yüzeyine silan ve dual-cure rezin siman uygulanmıştır. Tüm örneklere suda bekletme (24 saat 37 °C) ve termal yaşlandırma (5 000, 5°C-55 °C) uygulanmıştır. Seramik örnekler makaslama bağlanma dayanımı testine tabi tutulmuş ve meydana gelen başarısızlık tipleri değerlendirilmiştir. Tüm örneklerin yüzey pürüzlülüğü (Ra) ve makaslama bağlanma dayanımı (SBS) değerleri Levene-Tukey HSD ve Tamhane's testi kullanılarak analiz edilmiştir. Seramik gruplar ile başarısızlık tipleri arasındaki ilişki ise Ki-Kare analizi ile değerlendirilmiştir. Çalışmanın sonucunda, ayrı ayrı hem seramikler (P=0,037) hem de yüzey işleminin (P<0,001) yüzey pürüzlülüğüne etkisinin anlamlı olduğu bulunmuştur. Seramik grupları (P=0,013) ve yüzey işlemi uygulamasının (P<0,001) SBS üzerindeki etkisi istatistiksel olarak anlamlı bulunmuştur. Başarısızlık tipleri ile seramik gruplar (P=0,951) ve yüzey işlemleri arasında istatistiksel olarak anlamlı bir ilişki bulunmamıştır (P=0,024).
Özet (Çeviri)
The aim of this study is to evaluate the effect of surface treatment methods on the shear bond strength of ceramics (feldspathic ceramic, resin matrix infiltrated glass ceramic, resin nanoceramic) and the failure types that occur. Samples (14*12*2 mm) were prepared from Vitablocs Mark II, Vita Enamic and GC Cerasmart blocks (n=90). The samples were divided into 3 subgroups according to the surface treatment method (n=30). Group 1: 10% HF acid; Group 2: Sandblasting with Al2O3; Group 3: Sandblasting with tribochemical silica. After surface treatment, surface roughness measurements of all samples were made. Silane and dual-cure resin cement were applied to the surface of the samples. All samples were soaked in water (37 °C for 24 hours) and thermal aged (5 000 cycles, 5°C-55 °C). Shear bond strength test was applied to ceramic samples and failure types were evaluated. Surface roughness (Ra) and shear bond strength (SBS) values of all samples were analyzed using Levene-Tukey HSD and Tamhane's test. The relationship between ceramic groups and failure types was evaluated by Chi-Square analysis. As a result of the study, it was found that the effect of both ceramics (P=0.037) and surface treatment (P<0.001) on the surface roughness was significant. The effect of ceramic groups (P=0.013) and surface treatment (P<0.001) on SBS was found to be statistically significant. There was no statistically significant relationship between failure types of ceramic groups (P=0.951) and surface treatments (P=0.024).
Benzer Tezler
- Farklı yüzey işlemleri uygulanan lityum disilikat seramiklerin tamir materyaline bağlanma dayanımının değerlendirilmesi
Evaluation of the shear bond strength between repair material and lithium disilicate ceramics subjected to different surface treatments
BURCU YILDIRIM
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiGazi ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. CEMAL AYDIN
- Farklı yüzey işlemleri uygulanan zirkonya seramiğe üç farklı rezin simanın bağlanmasının incelenmesi
Investigation of bond strength of three different resin cements to zirconia ceramics which different surface treatments are applied
MERYEM GÜLCE SUBAŞI
Doktora
Türkçe
2011
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ÖZGÜR İNAN
- Lityum disilikat cam seramiklerde farklı primer uygulamasının termal yaşlandırma sonrası makaslama bağlanma dayanımına etkisi
Effect of shear bond strenght of glass ceramic treated different primers after termal cycling
BÜŞRA NUR AZGIN
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. OĞUZ ERASLAN
- CAD/CAM hibrit materyalleri ile adeziv rezin siman arasındaki bağlanma dayanımına farklı yüzey hazırlıklarının etkisi
Effect of different surface treatments on bond strength of resin cement to CAD/CAM hybrid materials
MATANAT GADIRLI
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiBezm-İ Alem Vakıf ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. BURCU DİKER
DOÇ. DR. ŞULE TUĞBA DENİZ
- Çeşitli yüzey işlemleri uygulanan Rezin Matriks seramiklerin rezin siman kullanılarak dişe bağlantılarının in-vitro olarak incelenmesi
In-vitro evaluation of shear bond strength of Resin Matrixceramics with different surface treatment methods
ELİF MELİKE AKARCA
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiHacettepe ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. RAGİBE ŞENAY CANAY