Farklı asitleme ve kumlama protokollerinin hibrit CAD/CAM materyalinin eğilme dayanımına ve rezin siman bağlantısına etkisi

Effect of different etching and air-abrasion protocols on flexural strength and resin cement bonding of hybrid CAD/CAM material

PDF İndir

  1. Tez No: 767316
  2. Yazar: HÜSEYİN ŞEKER
  3. Danışmanlar: DOÇ. DR. YENER OKUTAN
  4. Tez Türü: Diş Hekimliği Uzmanlık
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: CAD/CAM, Dental bonding, Dental materyaller, Dental stres analizi, Dental çimentolar, Eğilme dayanımı, Kompozit reçineler, Yüzey işleme tekniği, Yüzey pürüzlülüğü, CAD/CAM, Dental bonding, Dental materials, Dental stress analysis, Dental cements, Bending strength, Composite resins, Surface handling technique, Surface roughness
  7. Yıl: 2022
  8. Dil: Türkçe
  9. Üniversite: Aydın Adnan Menderes Üniversitesi
  10. Enstitü: Diş Hekimliği Fakültesi
  11. Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Amaç: Bu çalışmanın amacı hidroflorik asit (HF), kendinden asitli seramik primeri (MEP) ve kumlama protokollerinin hibrit CAD/CAM materyalinin yüzey pürüzlülüğü (Ra), eğilme dayanımı ve rezin siman bağlantısına etkisini değerlendirmektir. Gereç ve Yöntem: Toplamda 130 bar şekilli ve 130 dikdörtgen şekilli örnek düşük hızda elmas separe kullanılarak hibrit materyalden (Cerasmart 270) su soğutması altında kesilerek elde edildi. Örnekler yapılan yüzey işlemlerine göre 13 alt gruba ayrıldı: Kontrol (K), 60 sn HF (HF60), 90 sn HF (HF90), 120 sn HF (HF120), 60 sn MEP (MEP60), 90 sn MEP (MEP90), 120 sn MEP (MEP120), 10 sn kumlama (Kum10), 15 sn kumlama (Kum15), 20 sn kumlama (Kum20), kumlama sonrası HF (Kum+HF), kumlama sonrası MEP (Kum+MEP), HF sonrası MEP (HF+MEP). Ra değerleri bir profilometre kullanılarak ölçüldü. Her gruptan birer örnek atomik kuvvet mikroskobu ve taramalı elektron mikroskobu ile incelendi. Eğilme dayanımı ve rezin bağlanma dayanımı verileri üniversal test cihazı kullanılarak elde edildi. Başarısızlık tipleri stereomikroskop ile incelendi. İstatistiksel analizler için 1-yönlü ANOVA, Tukey HSD ve Tamhane T2 testleri uygulandı. Bulgular: En yüksek Ra değerleri ve en düşük eğilme dayanımı değerleri kumlama gruplarında bulunmuştur (P<0,05). HF ve MEP gruplarının eğilme dayanımı değerleri kontrol grubu ile istatistiksel olarak benzerdir (P>0,05). MEP gruplarının rezin bağlanma dayanımı değerleri aynı sürelerde HF asit uygulanan gruplara göre daha yüksektir. Farklı sürelerde uygulanan asitleme protokollerinden sonra rezin bağlanma dayanımı değerlerinde önemli farklılıklar görülmüştür (P<0,05). Sonuçlar: MEP uygulaması hibrit CAD/CAM materyali için tercih edilebilir bir yüzey işlemi olabilir. Kumlama işlemi hibrit materyalin mekanik özelliklerini olumsuz etkileyebilir.

Özet (Çeviri)

Aim: The aim of this study was to evaluate the effect of hydrofluoric acid (HF), self etching ceramic primer (MEP) and air-abrasion protocols on the surface roughness (Ra), flexural strength, and resin cement bonding of hybrid CAD/CAM material. Materials and Methods: A total of 130 bar-shaped and 130 rectangular-shaped specimens were obtained by cutting from a hybrid material (Cerasmart 270) using a low-speed diamond saw under water cooling. The specimens were divided into 13 subgroups according to surface treatments applied: Control (C), HF for 60 s (HF60), HF for 90 s (HF90), HF for 120 s (HF120), MEP for 60 s (MEP60), MEP for 90 s (MEP90), MEP for 120 s (MEP120), air-abrasion for 10 s (A10), air-abrasion for 15 s (A15), air-abrasion for 20 s (A20), air-abrasion followed by HF (A+HF), air-abrasion followed by MEP (A+MEP), HF followed by MEP (HF+MEP). Ra values were measured by using a profilometer. One specimen per group was examined under atomic force microscope and scanning electron microscope. Flexural strength and resin bond strength data were obtained by using a universal test device. Failure types were evaluated by a stereomicroscope. One-way ANOVA, Tukey's HSD, and Tamhane's T2 tests were performed for statistical analyses. Results: The highest Ra and the lowest flexural strength values were found in air-abrasion groups (P<0.05). Flexural strength values of HF and MEP groups were statistically similar to that of control group (P>0.05). Resin bond strength values of MEP groups were higher than those of HF groups treated with same durations. Significant differences in resin bond strength values were observed after etching protocols with different durations (P<0.05). Conclusion: MEP application can be a preferable surface treatment for hybrid CAD/CAM material. Air-abrasion may adversely affect the mechanical properties of the hybrid material.

Benzer Tezler

  1. Tez No

    797676

    Sinterleme öncesi ve sonrası farklı yüzey şekillendirme işlemlerinin monolitik zirkonya-rezin siman bağlantı dayanıklılığına etkilerinin incelenmesi

    Investigation of the effects of different surface treatment processes before and after sintering on the strength of monolithic zirconia-resin cement bonding

    YASAMIN RASHID MAHMOOD

    Doktora

    Türkçe

    Türkçe

    2023

    Diş Hekimliğiİstanbul Medipol Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. HALUK BARIŞ KARA

  2. Tez No

    568107

    Farklı yüzey şartlandırma işlemleri uygulanmış fiberle güçlendirilmiş kompozit post ve kök kanal dentini arasındaki bağlanma dayanımının itme bağlanma dayanımı testi ile değerlendirilmesi

    Evaluation of the the bond strength between different surface treatments applied fiber reinforced composite post and root canal dentine wi̇th pust out test

    TURAN SEKMEN

    Doktora

    Türkçe

    Türkçe

    2019

    Diş HekimliğiAkdeniz Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. ÖMER KIRMALI

  3. Tez No

    703552

    Dental seramik ve PEKK'nin bağlanma dayanımına farklı yüzey işlemlerinin etkisinin değerlendirilmesi

    Evaluation of the effect of different surface treatments on bond strength of dental ceramic and PEKK

    BAHAR TEKLİ

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2021

    Diş HekimliğiGazi Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF. DR. GÜLFEM ERGÜN

  4. Tez No

    744992

    Çeliklerde soğuk haddeleme öncesi yüzey tufalının giderilmesinde kuru buz püskürtme, yaş ve kuru kumlama yöntemlerinin incelenmesi

    Investigation of dry ice blasting, wet and dry sandblasting methods for removing of surface scale before cold rolling of steels

    MEHMET UÇKAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2022

    Makine MühendisliğiKocaeli Üniversitesi

    Makine Mühendisliği Ana Bilim Dalı

    DR. ÖĞR. ÜYESİ ERSİN ASIM GÜVEN

  5. Tez No

    99572

    Yüzey işlemleri ve silan/ bonding ajanı uygulamalarının porselen yapay diş-protez kaidesi bağlantısına olan etkinlikleri

    Effects of surface treatment and silane/ bonding agents on bond strength of denture base resin to porcelain denture teeth

    YEŞİM ERDEM ERMİŞ

    Doktora

    Türkçe

    Türkçe

    2001

    Diş Hekimliğiİstanbul Üniversitesi

    Protetik Diş Tedavisi Ana Bilim Dalı

    PROF.DR. HALUK KESKİN

Geri Dön