Yüksek fırın cürufu ile birlikte bazik pomza kullanılanalkali ile aktive edilmiş harçların özellikleri
Properties of alkali-activated mortars using blast furnace slag together with basic pumice
- Tez No: 766040
- Danışmanlar: PROF. DR. MUSTAFA SARIDEMİR
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Bazaltik pomza, Cüruf, Harç, Mekanik özellikler, Mikroyapı, Sodyum hidroksit, Sodyum silikat, Yüksek sıcaklık, Basaltic pumice, Slag, Mortar, Mechanical properties, Microstructure, Sodium hydroxide, Sodium silicate, High temperature
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Niğde Ömer Halisdemir Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: İnşaat Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Yapı Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tezde, ortam sıcaklığı ve yüksek sıcaklıklar uygulanan alkali ile aktifleştirilmiş öğütülmüş bazaltik pomza (ÖBP) ve öğütülmüş yüksek fırın cüruflu (ÖYFC) harçların uzun vadeli mekanik ve mikroyapısal özellikleri üzerine Na konsantrasyonu, buhar kürü ve fırın kürü koşullarının etkileri araştırılmıştır. Alkali ile aktifleştirilmiş harçlarda, bağlayıcı malzeme olarak %50 ÖBP+%50 ÖYFC kullanılmıştır. Bu malzemeleri bağlamak için karışımlarda, farklı Na konsantrasyonlarında aktivatör olarak sadece katı sodyum hidroksit (Na(OH)) ve sıvı sodyum silikat (Na2SiO3) ile birlikte katı Na(OH) kullanılmıştır. Ortam ve yüksek sıcaklıklara maruz kalan alkali ile aktifleştirilmiş ÖBP+ÖYFC harçların birim ağırlık, ultrases geçiş hızı, eğilme dayanımı ve basınç dayanımı değerleri tespit edilmiştir ve sadece çimento ile üretilen kontrol harcının değerleri ile karşılaştırılmıştır. Ayrıca ortam ve yüksek sıcaklıklara maruz kalan alkali ile aktifleştirilmiş ÖBP+ÖYFC harçların üzerinde XRD, SEM ve EDAX analizleri yapılmıştır. Sonuçlar, özellikle sıvı Na2SiO3 ile birlikte katı Na(OH) kullanılan alkali ile aktifleştirilmiş ÖBP+ÖYFC harçlarından kontrol harçlarına göre daha yüksek dayanım değerlerinin elde edilebileceğini göstermiştir. Ayrıca, sonuçlar, kontrol harçlarının maruz kaldığı sıcaklık arttıkça dayanım değerlerinin giderek azaldığını, ancak alkali aktifleştirilmiş ÖBP+ÖYFC harçlarının 450 ºC sıcaklığa kadar dayanım değerlerinin giderek arttığını ve daha sonraki yüksek sıcaklıklarda giderek azaldığını göstermiştir.
Özet (Çeviri)
In this thesis, the influences of Na concentration, steam and oven curing conditions on the long/short-term mechanical and microstructural properties of alkali activated ground basaltic pumice (GBP) and ground blast furnace slag (GBFS) mortars exposed to ambient and elevated temperatures are investigated. In the alkali activated mortars, 50%GBP+50%GBFS are employed as binder materials. To bind the materials, only solid sodium hydroxide (Na(OH)) and liquid sodium silicate (Na2SiO3) together with solid Na(OH) as activators are used at different Na concentration in the mixtures. The unit weight, ultrasonic pulse velocity, flexural strength and compressive strength of the alkali activated GBP+GBFS mortars subjected to ambient and elevated temperatures are determined and compared with the values of the control mortar produced only with cement. Besides, XRD, SEM and EDAX analyses are conducted on the alkali activated GBP+GBFS mortars subjected to ambient and elevated temperatures. The experimental results have indicated that the higher strength values can be attained from alkali activated GBP+GBFS mortars using liquid Na2SiO3 together with solid Na(OH) compared to the control mortars. Moreover, the experimental results have indicated that the strength values gradually reduce as the temperature subjected to the control mortars rises, but the strength values of alkali activated GBP+GBFS mortars up to 450 ºC temperature gradually rise, and reduce gradually at later elevated temperatures.
Benzer Tezler
- Alkali ile aktive edilmiş hafif betonların özelliklerinin araştırılması
Investigation of the properties of alkali-activated lightweight concretes
SERHAT ÇELİKTEN
Doktora
Türkçe
2019
İnşaat MühendisliğiNiğde Ömer Halisdemir Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA SARIDEMİR
- Bazı yapı malzemelerinde radyasyon perdeleme özelliklerinin belirlenmesi
Determination of radiation shielding properties in some building materials
İBRAHİM ALKILINÇ
Yüksek Lisans
Türkçe
2023
İnşaat MühendisliğiKahramanmaraş İstiklal ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. ADNAN KÜÇÜKÖNDER
- Bazik oksijen fırını cürufunun yapay agrega olarak esnek üstyapılarda alt temel ve temel tabakalarında kullanılabilirliğinin incelenmesi
Study of the usability of the basic oxygen furnace slag in terms of artificial aggregate as lower foundation and foundation layers in flexible superstructures
HİKMET ERGİN
Yüksek Lisans
Türkçe
2017
Ulaşımİstanbul Teknik Üniversitesiİnşaat Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. ŞÜKRÜYE İYİNAM
- Demir-çelik endüstrisindeki katı atıklardan çinko'nun uzaklaştırılması
Zinc removal from solid wastes in iron and steel industry
MUSTAFA KARĞILI
- Erdemir sinterinin özelliklerine harman bileşiminin (özellikle BOF cürufunun) etkisi
The Effects of blend contents on the properties of Erdemir's sinter
ABDULKERİM MUMCU