Pota cürufu ve silika bazlı sentetik cüruf kullanılarak oluşturulan cürufların MgO-C tuğlaları üzerindeki korozyon profillerinin incelenmesi
Examination of penetration behavior of MgO-C refractory bricks used in steel ladles slag zone against different quality steel slags
- Tez No: 761806
- Danışmanlar: DR. ÖĞR. ÜYESİ SERDAR ASLAN
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Cüruf, Penetrasyon, Refrakter, Termal genleşme, Tuğla, Çelik, Çelik üretimi, Slag, Penetration, Refractory, Thermal expansion, Brick, Steel, Steel production
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Sakarya Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, Kardemiş AŞ. Pota fırınlarında üretilen on farklı çelik kalitesine ait cürufun, çelik potası cüruf bölgesinde kullanılan MgO-C refrakter tuğlalara olan etkilerinin incelenmesi hedeflenmiştir. Bu doğrultuda, refrakter tuğlalardan kroze oluşturulmuş ve cüruf numuneleri içerilerine doldurularak“Cüruf – Refrakter Penetrasyon Testi”uygulanmıştır. Penetrasyon testi sonuçları; makro, taramalı elektron mikroskobu ve görüntü işleme yöntemleri ile irdelenmiştir. Çalışma kapsamında hazırlanan refrakter krozelerin içerisine cüruf doldurulmuş ve fırına şarj edilmiştir. Krozeler, 3 saatte 1600 °C sıcaklığa ulaşılmış ve pota fırınlarında yaklaşık işlem sıcaklığı olan 1600 °C'de 2 saat bekletilerek etkileşim sağlanmıştır. Cüruf – Refrakter korozyon testinin tamamlanmasının ardından, etkileşim alanında korozyon alanının hesaplanması amaçlanmıştır. Bu doğrultuda, cüruf-refrakter etkileşim bölgelerinde penetrasyon görülen bölgelerden alınmış SEM görüntüsü üzerinden“ImageJ”programı yardımı ile analizler gerçekleştirilmiştir. MgO-C refrakter krozeler ile cüruf numuneleri arasındaki etkileşimin anlaşılması amacıyla ergitme sonrasında taramalı elektron mikroskobu kullanılarak, cüruf – refrakter etkileşim alanlarında noktasal, alansal ve çizgisel mikro-kimyasal analizler yapılmıştır. EDS nokta analizlerinden, refrakterin MgO ve C esaslı olduğu, kullanılan cürufların ise Mg, Si, Al, Ca elementlerini içerdiği belirlenmiştir. Cüruf penetrasyonunun etkin bir şekilde gerçekleştiği 6,7 ve 8 numaralı numuneler haricinde cürufun refrakter malzemeye nüfuz edemediği görülmüştür. Korozyonun gerçekleştiği bölgelerde, cüruftan refraktere Ca difüzyonu, refrakterden cürufa ise Mg ve C difüzyonlarının olduğu tespit edilmiştir. Bu doğrultuda, SEM görüntülerinde etkin bir korozyonun görülmediği numunelerde dahi etkileşimin gerçekleştiği sonucuna varılmıştır.
Özet (Çeviri)
In this study, It is aimed to investigate the effects of slag belonging to ten different steel grades produced in Kardemiş A.Ş. ladle furnaces on MgO-C refractory bricks used in the steel ladle slag region. In this direction, a cross-section was formed from refractory bricks and slag samples were filled in and the“Slag - Refractory Penetration Test”was applied. The penetration test results were examined by macro, scanning electron microscopy and image processing methods. The slag was filled into the refractory crucibles prepared within the scope of the study and charged into the oven. The crucibles reached a temperature of 1600 °C in 3 hours and the interaction was achieved by holding them for 2 hours at 1600 °C, which is the approximate process temperature in ladle furnaces. After the completion of the slag – Refractory corrosion test, it is aimed to calculate the corrosion area in the interaction area. In this direction, analyzes were carried out with the help of the“ImageJ”program using the SEM image taken from the areas where penetration was observed in the slag-refractory interaction zones. In order to Decipher the interaction between MgO-C refractory crozes and slag samples, point, spatial and linear microchemical analyses were performed in the slag–refractory interaction areas using scanning electron microscopy after melting. From the EDS point analysis, it was determined that the refractory is based on MgO and C, and the slags used to contain the elements Mg, Si, Al, and Ca. It has been observed that slag cannot penetrate the refractory material, except for samples 6,7 and 8, where slag penetration occurs effectively. In the regions where corrosion occurs, Ca diffusion from the slag to the refractory, and Mg and C diffusion from the refractory to the slag have been found. Accordingly, it was concluded that the interaction occurred even in samples where no effective corrosion was observed in SEM images
Benzer Tezler
- Laboratuvar tipi elektrik ark fırını tasarımı ve e-atıktan öğütülebilir alaşım üretimi
Design of laboratory scale electrical arc furnace and production of grindable alloy from e-waste
RIDVAN ORMAN
Yüksek Lisans
Türkçe
2019
Mühendislik Bilimleriİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. SERVET İBRAHİM TİMUR
- Preliminary studies in the production of FeV from fuel oil slag formed in power plants
Fuel oil termik santral cürufundan FeV üretimi ön çalışmaları
GÜNEŞ YAKUPOĞLU
Yüksek Lisans
İngilizce
2009
Metalurji MühendisliğiMarmara ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ERSAN KALAFATOĞLU
YRD. DOÇ. DR. SEVAL GENÇ
- Sürekli döküm tandişlerindeki cüruf ile refrakter etkileşimleri
Slag and refractory interactions in continuous casting tundishes
İSMAİL ŞİŞLİ
Yüksek Lisans
Türkçe
2016
Seramik MühendisliğiKarabük ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. ALİ GÜNGÖR
- Farklı silisyum kaynakları ilave edilmiş pota cürufu tabanlıgeopolimer harçların mekanik ve durabilite özelliklerininincelenmesi
Investigation of the mechanical and durability properties of ladle slag-based geopolymer mortars incorporating different silicon sources
DİLARA BOYNUEYRİ
Doktora
Türkçe
2026
Makine MühendisliğiBartın ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA SABRİ GÖK
- Birincil ve ikincil hammaddelerden yapı kimyasallarında kullanılmak üzere jeopolimer üretimi
Geopolymer production from primary and secondary raw materials for use in construction chemicals
MELTEM İPEKÇİ TERZİOĞLU
Doktora
Türkçe
2025
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. FİLİZ ŞAHİN