Production of intermetallic reinforced metal matrix composites via in-situ reactions
İntermetaliklerle takviye edilmiş metal matrisli kompozitlerin yerinde reaksiyon yoluyla üretimi
- Tez No: 75972
- Danışmanlar: PROF. DR. TAYFUR ÖZTÜRK
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: arametallerle takviye edilmiş kompozhler, yerinde reaksiyonlar, arametal seçim mekanizması, hacimsel uyumsuzluk, serbest oluşma enerjisi, Kompozit malzemeler, Kompozitler, Metaller, Sıcak presleme, intermetallic reinforced composites, in-shu reactions, intermetallic selection mechanism, volume mismatch, free energy of formation, growth kinetics rv, Composite materials, Composites, Metals, Hot pressing
- Yıl: 1998
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
öz INTERMETALİKLERLE TAKVİYE EDİLMİŞ METAL MATRİSLİ KOMPOZİTLERİN YERİNDE REAKSİYON YOLUYLA ÜRETİMİ Önal Kıvılcım Yüksek Lisans, Metaluıji ve Malzeme Mühendisliği Bölümü Tez Yöneticisi: Prof Dr. Tayfur Öztürk Haziran 1998, 63 sayfa Bu çalışmada yerinde reaksiyonlar yoluyla arametallerle takviye edilmiş metal matrisli kompozit malzemelerin üretim olanakları incelenmiştir. Bu amaçla, tabakalı Al-Fe(Y) ve Al-Ti levhalar sıcak presleme yöntemiyle üretilmiştir. Haddelenen tabakalı yapılar, 550-6 10°C aralığında farklı sıcaklıklarda uzun süreli ısıl işleme tabi tutulmuştur. Bulgular, Al-Fe(y) numunelerinde Al3Fe ve AlsFe2 intermetaliklerinin; Al-Ti numunelerinde ise AI3Tİ ve AI23Tİ9 yapılarının oluştuğunu göstermektedir. Çalışma, Al-Fe(y) plakalardaki büyümenin“d = 580.85 106 exp<232'nrı) t034 ”bağıntısıyla, Al-Ti laminantlardaki büyümenin ise“d = 1571.84 exp <nn2n) t*29 ”bağıntısıyla uyumlu olduğunu göstermektedir. Burada, d arametal kalınlığını (cm), T sıcaklığı (K), R evrensel gaz sabitini, t reaksiyon süresini (s) ifade etmektedir.Bu çalışmada aynı zamanda, arametal seçme mekanizması hacimsel uyumsuzluk ve mtermetaliklerin serbest oluşma enerjisi açılarından incelenmiştir. Bu bağlamda, hacimsel uyumsuzluğun arametal seçiminde etkin bir mekanizma olduğu, arametal serbest oluşma enerjisinin ise seçim mekanizmasında etkili rol oynamadığı izlenimi edinilmiştir. Çalışma, Al-Fe(y) ve Al-Ti'da takviye âzının makul sûreler içerisinde tümüyle arametallere dönüşmesi için, takviye fazın çok ince olarak (~ 10 um) kullanılması gerektiğim göstermektedir. Aynı amaca tabakalı yapılarla erişilebileceği gibi, uygun boyuttaki toz seçimi ile de ulaşılabileceği sonucuna varılmıştır.
Özet (Çeviri)
ABSTRACT PRODUCTION OF INTERMETALLIC REINFORCED METAL MATRIX COMPOSITES VIA IN-SITU REACTIONS önaL Kıvılcım M.S., Department of Metallurgical and Materials Engineering Supervisor: Prof Dr. Tayfur öztürk June 1998, 63 pages This study examines the possibility of producing intermetallic reinforced metal matrix composites via in-situ reactions. For this purpose, multilayers of Al-Fe(y) and Al-Ti are produced by hot-pressing. Products are then deformed by rolling and subjected to prolonged heat treatments at temperatures between 550-6 10°C. Reaction products are identified as A^Fe and Al5Fe2 in Al-Fe(y) composites, and as Al3Ti and AI23Tİ9 in Al-Ti composites. The growth kinetics is described as“d = 580.85 106 exp<2nim) t0M ”for Al-Fe(y) laminates, and as“ d = 1571.84 exp ”(12732/r) t0M " for Al-Ti laminates, where d (in cm) is the thickness of the growth layer, T (in K) the heat treatment temperature, and t (in seconds) the duration of heat treatment. In this study, also the intermetallic selection mechanism is investigated from the viewpoint of volume mismatch and free energy of formatioa Volume mismatch inappears to be an effective mechanism in intermetallic selection, while free energy of formation does not seem to play a role in this respect. This study shows that so as to convert all reinforcing phase into intermetallics within reasonable production cycles, very thin reinforcing layers need to be used. It also seems likely that this production method may be applied to powders of proper size.
Benzer Tezler
- Gaz enjeksiyon ve elementel karbon ilavesi yöntemleri ile tic takviyeli alüminyum matrisli kompozit üretimi
Başlık çevirisi yok
IŞIL ÇEVİKER KERTİ
Doktora
Türkçe
1998
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMalzeme Mühendisliği Ana Bilim Dalı
PROF. DR. H. ERMAN TULGAR
- In-situ production of TiC particulate reinforced AL metal matrix composite
Yerinde üretilen titanyum karbür parçacıkları ile takviye edilmiş alüminyum esaslı kompozit üretimi
TUFAN SEZENÖZ
Yüksek Lisans
İngilizce
1997
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. ALİ KALKANLI
- Al-TiCp kompozitlerinin Al-Ti eriyikleri içinde grafit çözündürülerek üretilmesi
In-situ processing of TiC-Al composites by reacting graphite with Al-Ti melts
A. MURAT KARAAĞAÇ
- Microstructural and phase studies of titanium carbide particulate reinforced aluminium matrix composities
Titanyüm karbür parçacıkları ile takviye edilmiş alüminyum esaslı kompozitlerde iç yapı ve faz çalışması
AYŞEGÜL ŞAHİN
Yüksek Lisans
İngilizce
1996
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. FİLİZ SARIOĞLU
- Alümina fiber takviyeli Al-si metal matriksli kompozitlerin üretimi ve mikroyapı-özellik ilişkilerinin incelenmesi
production of alumina fiber reinforced Al-si metal matrix composites and the investigation of their microstructure-propetry relation ships
HATEM AKBULUT