Rezin içerikli restoratif materyallerin pürüzlülüğünün, su emilimi ve suda çözünürlüklerinin in vitro olarak incelenmesi
In vitro investigation of the roughness, water absorption and water solubility of resin containing restorative materials
- Tez No: 741850
- Danışmanlar: DOÇ. DR. AYŞE DÜNDAR
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: suda çözünürlük, su emilimi, yüzey pürüzlülüğü, sitrik asit, Dental materyaller, Dental restorasyon, Kompozit reçineler, Nitrik asit, Pürüzlülük, Reçine, Çözünürlük, İn vitro, water solubility, sorption, surface roughness, citric acid, Dental materials, Dental restoration, Composite resins, Nitric acid, Roughness, Resin, Solubility, In vitro
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Akdeniz Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Restoratif Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı, farklı rezin materyallerin asit ortamda pürüzlülüğünü, su emilimini ve suda çözünürlüklerini incelemektir. Yöntem: Çalışmada, 1 adet yüksek viskoziteli Bulk Fill kompozit (Filtek Bulk Fill Posterior Restorative), 1 adet mikrohibrit kompozit (Charisma® Smart), 1 adet nanohibrit indirekt posterior kompozit (GradiaTM Plus indirekt kompozit ) ve 1 adet ışıkla sertleşen rezin modifiye cam iyonomer (RIVA resin modifiye cam iyonomer ) kullanılarak 4 mm çap ve 4 mm kalınlıkta toplam 80 adet örnek hazırlandı. Çözünürlük ve su emilimi değerlerini saptamak için, örneklerin başlangıç ağırlıkları mikrogram (μg) cinsinden kaydedildi (M1). Başlangıç yüzey pürüzlülük ölçümleri profilometre (Surftest SJ-201, Mitutoyo, Tokyo, Japonya) ile yapıldı, ilk ölçülen yüzey pürüzlülük değerleri Ra1 olarak kaydedildi. Örnekler (n=10) 2 farklı solüsyonda (distile su, sitrik asit) 40 gün bekletildi, ardından örneklerin solüsyonlarda bekleme sonrası ağırlıkları mikrogram (μg) cinsinden kaydedildi (M2). Tekrar profilometre ile ikinci yüzey pürüzlülük değerleri belirlendi (Ra2). Örnekler desikatörde bekletilip ağırlık sabitlendiğinde, değerler M3 olarak kaydedildi. Çözünürlük ve suda emilim düzeyleri ISO 4049:2009 standartlarına göre hesaplandı. İstatistiksel analiz, Tek yönlü ANOVA ve Tukey HSD çoklu karşılaştırmaları kullanılarak yapılmıştır (p=0.05). Bulgular: Yüzey pürüzlülük değişimi ve su emilim değerleri karşılaştırıldığında CİS grupları kompozit gruplarına göre daha yüksek yüzey pürüzlülüğü ve su emilimi değerleri göstermiştir (p<0,05). Gruplar arasında suda çözünürlük açısından anlamlı farklılıklar olduğu bulunmuştur (p<0,05). CİS-SA grubu en yüksek suda çözünürlük değeri göstermiştir ve bu çözünürlük değeri diğer tüm gruplardan istatistiksel olarak farklı bulunmuştur. Sonuç: Bekleme ortamı çalışmamızda test edilen gruplar arasında sadece cam iyonomer siman grubunda yüzey pürüzlülüğü, su emilimi ve çözünürlüğünde anlamlı bir artışa sebep olmuştur. En fazla su emilimi, çözünürlük ve yüzey pürüzlülüğü değişimi CİS-SA grubunda görülmüştür. Bekleme ortamı kompozit rezin grupları arasında su emilimi ve yüzey pürüzlülüğü değişimi açısından herhangi bir fark yaratmamıştır. Kompozit grupları arasında bekleme ortamı kompozitlerin çözünürlüğünde anlamlı bir farka sebep olmamıştır.
Özet (Çeviri)
Objective: This study was aimed to evaluate on water sorption, solubility and surface roughness of resin based restorative Method: In this study, a Bulk-fill (Filtek Bulk Fill Posterior Restorative), microhybrid (Charisma® Smart), a nanohybrid indirect resin composites (GradiaTM Plus indirect composite) and a light cure resin modified glass ionomer cement (RIVA resin modified glass ionomer cement) were used and 80 samples of 4 mm diameter and 4 mm thickness were prepared. To determine the water sorption and solubility values, the initial weights of the samples were noted in micrograms (μg) (M1). The initial surface roughness (SR) of all samples was measured with a profilometer (Surftest SJ-201, Mitutoyo, Tokyo, Japan) and was expressed in μm as Ra1. The samples (n=10) were immersed into 2 different solutions (distilled water, citric acid) for 40 days, then the weights of the samples after standing in the solutions were noted in micrograms (μg) (M2). Repeated SR measurements were performed at 40 days storage time (Ra2). Thereafter, the specimens were stored in the desiccator and reweighed until a constant dry mass (M3) was attained. Water sorbtion and solubility (μg/mm3) were calculated based on ISO 4049:2009 standards. Statistical analysis was performed using the One-way ANOVA and Tukey HSD multiple comparisons (p=0.05). Results: CIS groups showed higher surface roughness and water absorption values than composite groups (p<0.05). It was found that there were significant differences between the groups in terms of water solubility (p<0.05). CIS-SA group showed the highest water solubility value and this solubility value was statistically different from all other groups. Conclusion: Among the tested groups in storage medium, only the glass ionomer cement group showed a significant increase in surface roughness, water absorption and solubility. The greatest change in water absorption, solubility and surface roughness was observed in the CIS-SA group. The waiting environment did not make any difference between the composite resin groups in terms of water absorption and surface roughness change. The storage medium did not cause a significant difference in the solubility of the composites between the composite groups.
Benzer Tezler
- Cam iyonomer içerikli farklı restoratif materyallerin yüzey özelliklerinin biyofilm oluşumuna etkisi
Effects of surface characteristic of glass ionomer based different restorative materials on biofilm formation
ÖZLEM SEÇKİN
Diş Hekimliği Uzmanlık
Türkçe
2018
Diş HekimliğiSüleyman Demirel ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ÖZGE KAM HEPDENİZ
- Fluorid içeren rezin esaslı olan ve olmayan üç farklı cam iyonomer siman ve bir akışkan kompozit rezin materyalinin iki farklı rezin esaslı nano içerikli glaze materyali ile kaplanmasının, materyallerin fluorid salınım değerleri, yüzey pürüzlülüğü ve yüzey sertliği özelliklerine olan etkilerinin karşılaştırılması
To investigate the effect of the usage of two different nano-filled and resin based surface coatings on the fluoride release, surface roughness and surface hardness of the three different resin modified and conventional glass ionomer and a flowable composite resin materials
FATOŞ ALP
- Ozon uygulamasının pedodontide kullanılan rezin içerikli restoratif materyallerin farklı içeceklerle yaşlandırılması sonrası renk değişimi ve yüzey pürüzlülüğüne etkisinin değerlendirilmesi
Evaluation of the effect of ozone application ondiscolouration and surface roughness of resincontaining restorati̇f materials used in pedodonticsafter aging with different beveragesfaculty of dentistry
TUĞÇE ASLAN
Diş Hekimliği Uzmanlık
Türkçe
2024
Diş HekimliğiBolu Abant İzzet Baysal ÜniversitesiPedodonti Ana Bilim Dalı
DR. ÖĞR. ÜYESİ DENİZ SILA ÖZDEMİR ÇELİK
- CAD/CAM sistemlerinde kullanılan farklı içeriklere sahip seramik materyallerde gıda benzeri solüsyonların estetik, mekanik ve fiziksel etkilerinin değerlendirilmesi
Evaluation of aesthetic, mechanical and physical effects of food-like solutions on ceramic materials with different contents used in CAD/CAM systems
ÇAĞRI KOYAL
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiPamukkale ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. HATİCE LAMİA ELİF SAĞESEN
- Cam iyonomer esaslı restoratif materyallerin farklı içerikte diş macunları ile fırçalanması sonrası yüzey özelliklerinin incelenmesi
Investigation of the surface properties of glass ionomer-based restorative materials after brushing with different toothpastes
BERRAK MANGUT
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiMarmara ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ GÜLÇİN BİLGİN GÖÇMEN