Farklı içerikteki toz metal magnezyum alaşımları ile deniz suyundan hidrojen üretiminin incelenmesi
Investigation of hydrogen production from sea water with powder metal magnesium alloys with different content
- Tez No: 741164
- Danışmanlar: DR. ÖĞR. ÜYESİ MEHMET SALİH CELLEK, AR.GÖR. ALİ ERÇETİN
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Ağırlık kaybı, Hidrojen üretimi, Magnezyum alaşımları, Sinterleme, Sıcak presleme, Toz metalurjisi, Weight loss, Hydrogen production, Magnesium alloys, Sintering, Hot pressing, Powder metallurgy
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Bingöl Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, yüksek saflıkta ve mikron boyutlarında Mg, Sn, Si, Al, Mn, Zn, Cr ve Fe elementel tozları farklı oranlarda kullanılarak Mg alaşımları sıcak presleme tekniği ile üretilmiştir. Özellikle Mg gibi oksijene yüksek ilgisi olan tozların üretim aşamasında oksidasyonuna mahal vermemek için parafin kaplama tekniği uygulanmıştır. Belirli oranlarda karıştırılan tozlar önceden hazırlanan grafit kalıplara doldurulmak suretiyle sıcak presleme işlemi uygulanmak üzere fırın içerisine yerleştirilmiştir. 300 oC'de 40 dk bağlayıcı giderme işleminden sonra, sinterleme işlemleri yüksek saflıkta argon gazı kullanılarak 610 oC sinterleme sıcaklığında, 50 MPa basınç altında 90 dk süreyle gerçekleştirilmiştir. Sıcak presleme yöntemiyle üretilen numunelere sırasıyla zımparalama ve parlatma işlemleri uygulanmıştır. Numune yüzey incelemelerinde SEM-EDS analizleri uygulanmıştır. Sinterleme prosesinin başarısı üretilen numunelerin %98 üzerinde bağıl yoğunluğa sahip olmasıyla belirlenmiştir. Yoğunluk ölçümlerinde Arşimet prensibinden yararlanılmıştır. Farklı Mg alaşımlarının yapay ve doğal deniz suyunda 10 gün süreyle korozyona uğraması neticesinde açığa çıkan hidrojen gazı miktarları ölçülmüştür. Yapay ve doğal deniz suyuna üretilen Mg alaşımlarını daldırma işlemi neticesinde sürekli hidrojen gazı açığa çıktığı belirlenmiştir. Hidrojen gazı miktarının farklı kompozisyona sahip Mg alaşımlarıyla önemli ölçüde değiştiği tespit edilmiştir. Yüksek oranda Sn içeren alaşımların daldırılmasında en yüksek oranda hidrojen gazı açığa çıkmaktadır. Uygulamanın özellikle talaş veya hurda formunda atıl durumdaki Mg alaşımlarının hidrojen enerjisi olarak geri dönüştürülmesine ışık tutacağı öngörülmektedir.
Özet (Çeviri)
In this study, Mg alloys were prepared by hot pressing technique using Mg, Sn, Si, Al, Mn, Zn, Cr and Fe elemental powders of high purity and micron size in different proportions. In order to prevent oxidation of powders such as Mg, which have a high affinity for oxygen, during the manufacturing process, the paraffin coating technique was used. The powders mixed in certain proportions were filled into the pre-prepared graphite molds and placed in the furnace to apply the hot-pressing method. After 40 minutes binder removal at 300 oC, the sintering processes was carried out using high purity argon gas at a sintering temperature of 610 oC, and a pressure 50 MPa for 90 minutes. Sanding and polishing processes were applied to the samples produced by the hot-pressing method, respectively. SEM-EDS analyzes were applied for sample surface examinations. The success of the sintering process was determined by the relative density of the produced specimens exceeding 98%. Archimedes principle was used for the measurements. The amount of hydrogen gas released as a result of corrosion of various Mg alloys in artificial and natural sea water over 10 days was measured. It was found that, hydrogen gas is constantly released due to the immersion of Mg alloys in artificial and natural sea water. It was found that the amount of hydrogen gas varies Mg alloys with different compositions. The largest amount of hydrogen gas is released during immersion of alloys with high Sn content. It is expected that the application will shed light on the recycling of inert Mg alloys, especially in the form of sawdust or scrap, as hydrogen energy.
Benzer Tezler
- Darbeli elektrik alan tekniği ile arıtma tesisi çamurundan bütünleşik azot ve fosfor geri kazanımı ve anaerobik çürümenin iyileştirilmesi
Integrated nitrogen and phosphorus recovery from treatment plant waste sludge with pulsed electric field technique and anaerobic stabilization improvement
EKİN EKE
Doktora
Türkçe
2019
Çevre MühendisliğiSüleyman Demirel ÜniversitesiÇevre Mühendisliği Ana Bilim Dalı
DOÇ. DR. ÖZLEM SELÇUK KUŞÇU
- Farklı karbür fazı içeren partikül takviyeli al matrisli kompozitlerin toz metalurjisi yöntemiyle üretimi ve karakterizasyonu
Production and characterization of various carbide particulate reinforced aluminium matrix composites produced by powder metallurgy method
RİFAT ONUR ÜLKÜSEVEN
Yüksek Lisans
Türkçe
2019
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. BURAK ÖZKAL
- Samsun şehir tozlarında ağır metal ve türlerinin tayini
Determination of heavy metals and their species in the city dusts of Samsun
FİLİZ KABADAYI
- Midye kabuğu takviyesinin alüminyumun özelliklerine etkisi
The effect of mussel shell reinforcement on the properties of aluminium
ONUR VARSOYOĞLU
Yüksek Lisans
Türkçe
2022
Metalurji MühendisliğiEskişehir Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ GÜL İPEK SELİMOĞLU
- Rafine ve rafine edilmemiş yemeklik tuzların analizi
Analyses of refined and unrefined edible salt samples
DÖNDÜ SERPİL KAÇAR PEKER
Yüksek Lisans
Türkçe
2006
KimyaErciyes ÜniversitesiKimya Ana Bilim Dalı
DOÇ.DR. ORHAN TÜRKOĞLU
PROF.DR. MUSTAFA SOYLAK