Atık döküm poliamid 6 (PA6G) katkılı odun plastik kompozitlerden üretilen mobilya bağlantı elemanlarının özelliklerinin incelenmesi
Investigation of the properties of furniture fasteners produced from waste casting polyamide 6 (PA6G) added wood plastic composites
- Tez No: 723018
- Danışmanlar: DOÇ. DR. HÜSEYİN YÖRÜR, PROF. DR. FATİH MENGELOĞLU
- Tez Türü: Doktora
- Konular: Ağaç İşleri, Mühendislik Bilimleri, Ormancılık ve Orman Mühendisliği, Wood Products, Engineering Sciences, Forestry and Forest Engineering
- Anahtar Kelimeler: Ahşap mobilya, Büro mobilyaları, Lifli kompozitler, Mutfak mobilyaları, Plastik kompozitler, Polietilen kompozitleri, Polimer kompozitler, Wood furniture, Office furniture, Fiber composites, Kitchen furniture, Plastic composites, Polyethylene composites, Polymer composites
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Karabük Üniversitesi
- Enstitü: Lisansüstü Eğitim Enstitüsü
- Ana Bilim Dalı: Orman Endüstri Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Orman Endüstri Mühendisliği Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tez çalışması iki aşama olarak planlanmıştır. İlk aşamada, göknar odun unu, pirinç kabuğu, döküm poliamid 6 (PA6G), yüksek yoğunluklu polietilen (HDPE), N-bütil benzen sülfonamid ve lityum klorür tuzu kullanılarak odun plastik kompozitlerin (OPK) ekstrüzyon ve enjeksiyon kalıplama yöntemi ile üretimi gerçekleştirilmiştir. Farklı varyanslarda üretilen OPK' ların fiziksel (özgül ağırlık, yoğunluk, suda bekletme), mekanik (çekme direnci, çekmede elastikiyet modülü, kopmada uzama, eğilme direnci, eğilmede elastikiyet modülü, darbe direnci), termal (diferansiyel taramalı kalorimetre (DSC), termogravimetrik analiz (TGA)) ve morfolojik özellikleri belirlenmiştir. İkinci aşamada; ekstrüzyon ve enjeksiyon kalıplama yöntemiyle göknar odun unu dolgulu PA6G-HDPE esaslı kompozitlerden endüstride en yaygın kullanıma sahip L bağlantı elemanlarının üretimi gerçekleştirilmiştir. Üretilen ve piyasadan temin edilen (polipropilen ve yüksek yoğunluklu polietilen esaslı) L bağlantı elemanları ile L köşe birleştirmelerin üretimi gerçekleştirilmiştir. L köşe birleştirmelerin üretiminde melamin emprenyeli kâğıt ile kaplanmış yonga levha (YL-lam) ve orta yoğunluklu lif levha (MDFlam) kullanılmıştır. Göknar odun unu dolgulu PA6G-HDPE esaslı kompozitlerden üretilen ve piyasadan temin edilen L bağlantı elemanlarının farklı sıcaklıklardaki (20 ºC ve 50 ºC) ve su buharında bekletme sonrası diyagonal çekme yükleri altındaki moment taşıma kapasiteleri ve yorulma direnç özellikleri belirlenmiştir. Ayrıca bu bağlantı elemanları ile üretilen L köşe birleştirmelerin farklı sıcaklıklardaki (20 ºC ve 50 ºC) ve su buharında bekletme sonrası moment taşıma kapasiteleri ve yorulma direnç özellikleri tespit edilmiştir. Elde edilen sonuçlar incelendiğinde, %20 göknar odun unu dolgulu PA6G ve PA6G-HDPE esaslı kompozit test örneklerinin en yüksek mukavemet ve elastikiyet özelliği gösterdiği belirlenmiştir. Lignoselülozik dolgu maddesi ilavesi PA6G esaslı kompozitlerde erime sıcaklığını azaltırken, PA6G-HDPE esaslı kompozitlerde ise erime sıcaklığına etki etmediği gözlemlenmiştir. Göknar odun unu dolgulu PA6G-HDPE esaslı kompozitlerden üretilen ve piyasadan temin edilen L bağlantı elemanları ile bu bağlantı elemanları kullanılarak üretilen L köşe birleştirmelerine ait moment taşıma kapasitesitelerinin sıcaklık artışı ile azaldığı tespit edilmiştir. 20 ºC' de MDF-lam kullanılan L köşe birleştirmelerin moment taşıma kapasitesinin YL-lam kullanılan L köşe birleştirmelerinden daha yüksek olduğu tespit edilmiştir. 50 °C sıcaklıkta ise YL-lam'dan üretilen L köşe birleştirmelerin moment taşıma kapasitelerinin MDF-lam ile üretilenlerden daha yüksek olduğu belirlenmiştir. Göknar odun unu dolgulu PA6G-HDPE esaslı kompozitlerden üretilen bağlantı elemanları ile oluşturulan L köşe birleştirmelerin su buharında bekletilmesi sonucu moment taşıma kapasitelerinde artış meydana gelmiştir. L köşe birleştirmelerin yorulma dirençleri incelendiğinde, sıcaklık artışı ile toplam deformasyon miktarlarının azaldığı tespit edilmiştir. Lignoselülozik dolgu maddesi kullanılan deney örneklerinin su buharında bekletilmesi sonucu toplam deformasyon miktarında artış meydana gelmiştir.
Özet (Çeviri)
This thesis is planned as two stages. In the first stage, wood plastic composites (WPC) were produced by extrusion and injection molding using fir wood flour, rice husks, cast polyamide 6 (PA6G), high density polyethylene (HDPE), N-butyl benzene sulfonamide and lithium chloride salt. Physical (specific gravity, density, water soaking), mechanical (tensile strength, elasticity modulus in tensile, elongation at break, bending strength, elasticity modulus in bending, impact strength), thermal (differential scanning calorimetry (DSC), thermogravimetric analysis (TGA)) and morphological characteristics of OPKs produced in different variances were determined. In the second stage; L fasteners, which are the most widely used in the industry, were produced from fir wood flour filled PA6G-HDPE based composites by extrusion and injection molding method. L corner joints were produced with L fasteners produced and supplied from the market (polypropylene and high density polyethylene based). Melamine plate-coated particle board (YL-lam) and medium density fiberboard (MDFlam) were used in the production of L corner joints. The moment carrying capacities and fatigue strength of L corner joints produced using these fasteners and L fasteners produced from fir wood flour filled PA6G-HDPE composites and supplied from the market under diagonal tensile loads at different temperatures (20 ºC and 50 ºC) and water vapor were determined. In addition, the moment carrying capacities and fatigue strength properties of L corner joints produced with these fasteners at different temperatures (20 ºC and 50 ºC) and water vapor were determined. When the results obtained were examined, it was determined that PA6G and PA6G-HDPE based composite test samples filled with %20 fir wood flour showed the highest strength and elasticity. While the addition of lignocellulosic filler decreases the melting temperature in PA6G-based composites, it has been observed that it does not affect the melting temperature in PA6G-HDPE-based composites. It has been determined that the moment carrying capacity of the L corner joints produced from these fasteners with L fasteners supplied from the market and manufactured from fir wood flour filled PA6G-HDPE based composites decreases with increasing temperature. At 20 ºC, it was determined that the moment carrying capacity of L corner joints using MDF-lam is higher than L corner joints using YL-lam. At 50 °C, it was determined that the moment carrying capacities of L corner joints produced from YL-lam were higher than those produced with MDF-lam. The moment carrying capacity of the L corner joints formed with fasteners made of fir wood flour filled PA6G-HDPE based composites increased with holding in water vapor. When the fatigue strength of the L corner joints was examined, it was determined that the total deformation amount decreased with the increase in temperature. As a result of keeping in water vapor the test samples used lignocellulosic filler, an increase in the total deformation amount occurred.
Benzer Tezler
- Zeytinyağı üretimi atıklarının tekstil boyacılığında kullanım olanaklarının araştırılması
The investigation of possible use of olive oil production wastes in textile dyeing
BERRAK BUKET AVCI
Yüksek Lisans
Türkçe
2016
Tekstil ve Tekstil MühendisliğiDokuz Eylül ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. GÖKHAN ERKAN
- Reaction of acetophenone-formaldehyde resin with s-triazone compounds for fire resistance polyurethane
Poliüretan yanmazlık dayanımı için asetofenon formaldehit reçinesinin s-triazon bileşiği ile reaksiyonu
MİNE MUTLU
Yüksek Lisans
İngilizce
2017
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. NİLGÜN KIZILCAN
- Development of polyamideimide based nanofiltration membranes for separation of dyes and salts in textile wastewater treatment
Tekstil atıksuyunun arıtımında boya ve tuzların ayrıştırılması için polamidimid bazlı nanofiltrasyon membranlarının geliştirilmesi
AYŞE METECAN
Yüksek Lisans
İngilizce
2019
Kimya Mühendisliğiİzmir Yüksek Teknoloji EnstitüsüKimya Mühendisliği Ana Bilim Dalı
PROF. DR. SACİDE ALSOY ALTINKAYA
- Atık yün nonwoven ve nano bakır/PA kumaş takviyeli hibrit kompozit yapılarda elektromanyetik koruma etkinliğinin deneysel incelenmesi
Experimental investigation of electromagnetic shieldingeffectiveness in hybrid composite structures reinforced with wastewool nonwoven and nano copper/PA fabrics
MURAT ÇOBAN
Yüksek Lisans
Türkçe
2025
Bilim ve TeknolojiMersin ÜniversitesiNanoteknoloji ve İleri Malzemeler Ana Bilim Dalı
DR. ÖĞR. ÜYESİ BANU YILMAZ AKYÜREK
- Büyük ölçekli tekstil sektörleri için yeşil üretim ve atık yönetimi
Green production and waste managemetfor large scale textile industries
ERCİH KARACA
Yüksek Lisans
Türkçe
2024
Çevre MühendisliğiSakarya ÜniversitesiÇevre Mühendisliği Ana Bilim Dalı
DOÇ. DR. AHMET ÇELEBİ