Arayüzey polimerizasyonu ile elde edilen antibakteriyel poli(N-metilpirol)/BN kompozitinin yapısal ve elektriksel karakterizasyonu
Structural and electrical characterization of antibacterial poly(N-methylpyrol)/BN composite obtained by interface polymerization
- Tez No: 716364
- Danışmanlar: DOÇ. DR. HATİCE ÖZKAZANÇ
- Tez Türü: Yüksek Lisans
- Konular: Polimer Bilim ve Teknolojisi, Polymer Science and Technology
- Anahtar Kelimeler: Bor Nitrür, Karakterizasyon, Kompozit Malzeme, Poli(N-metilpirol), Kompozit malzemeler, Metil pirol, Boron Nitride, Characterization, Composite Material, Poly(N-methylpyrrole), Composite materials, Methyl pyrrolle
- Yıl: 2022
- Dil: Türkçe
- Üniversite: Kocaeli Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Polimer Bilim ve Teknolojisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada ara yüzey polimerizasyon yöntemi ile elde edilen Poli(N-metilpirol) ve Poli(N-metilpirol)/Bor nitrür (PNMPy/BN) kompozitinin karakterizasyon ve morfolojik analizleri yapıldı. Bu analizler Fourier dönüşümü kızılötesi (FT-IR), X-ışını kırınımı (XRD), Floresans (FL) ölçümleri, Termogravimetrik (TG) ve Taramalı elektron mikroskobu (SEM) ile gerçekleştirildi. Örneklerin sıcaklığa bağlı dielektrik ölçümleri bir LCR metre ile yapıldı ve ardından örneklerin antimikrobiyal aktiviteleri incelendi. Analizler, BN nanopartiküllerinin polimer zincirlerinin - istiflenme mesafesini azalttığını ve FL sönümleme etkisine neden olduğunu gösterdi. PNMPy'nin bozunma süreci 318C'de gerçekleşirken, katkılama işlemi sonrası bozunma sıcaklığı 345C'ye çıktı. SEM analizinde katkılama işlemi ile yüzeydeki moleküler yapıların daha sıkı ve istif bir yapıda olduğu görüldü. Dielektrik analizler, PNMPy ve PNMPy/BN kompozitinin yük transfer mekanizmasının CBH (Correlated Barrier Hopping) modeli ile uyumlu olduğunu gösterdi. Ayrıca, katkılama işleminin, polimer matriste bulunan yük taşıyıcıların minimum sıçrama mesafesini azalttığı belirlendi. Antibakteriyel aktivite testleri, BN nanopartiküllerinin E.Coli ve S. Aureus bakterilerinin yasaklı bölge çapını yaklaşık 7 mm arttırdığını gösterdi. Elde edilen sonuçlara göre, PNMPy/BN kompozitinin önemli bir antibakteriyel ajan olmasının yanı sıra, orta frekans bölgesinde çalışan elektronik cihazlarda kullanılabilecek düşük maliyetli bir yarı iletken malzeme olduğu belirlenmiştir.
Özet (Çeviri)
In this study, characterization and morphological analyzes of Poly(N-methylpyrrole) and Poly(N-methylpyrrole)/Boron nitride (PNMPy/BN) composite obtained by interfacial polymerization method were performed. These analyzes were performed with Fourier transform infrared (FT-IR), X-ray diffraction (XRD), Fluorescence (FL) measurements, Thermogravimetric (TG) and Scanning electron microscope (SEM). The temperature-dependent dielectric measurements of the samples were made with an LCR meter, and then the antimicrobial activities of the samples were examined. The analyzes showed that the BN nanoparticles reduced the - stacking distance of the polymer chains and caused the FL damping effect. While the decomposition process of PNMPy occurred at 318C, the decomposition temperature increased to 345C after doping. In the SEM analysis, it was observed that the molecular structures on the surface were more compact and stacked with the doping process. Dielectric analyzes showed that the charge transfer mechanism of PNMPy and PNMPy/BN composite is compatible with the CBH (Correlated Barrier Hopping) model. In addition, it was determined that the doping process reduces the minimum spacing of the charge carriers in the polymer matrix. Antibacterial activity tests showed that BN nanoparticles increased the restricted zone diameter of E. Coli and S. Aureus bacteria by approximately 7 mm. According to the results obtained, it has been determined that PNMPy/BN composite is a low-cost semiconductor material that can be used in electronic devices operating in the mid-frequency region, as well as being an important antibacterial agent.
Benzer Tezler
- Production of antibacterial biobased blends for biomedical use
Biyomedikal alanlarda kullanılmak üzere antibakteriyel özellikli biyobazlı harmanların eldesi
METE DERVİŞCEMALOĞLU
Yüksek Lisans
İngilizce
2023
Biyoteknolojiİstanbul Teknik ÜniversitesiMoleküler Biyoloji-Genetik ve Biyoteknoloji Ana Bilim Dalı (disiplinlerarası)
PROF. DR. FATOŞ YÜKSEL GÜVENİLİR
- Biomedical application of an enzymatically synthesized biopolyester
Enzimatik olarak sentezlenmiş bir biyopoliesterin biyomedikal uygulaması
ŞENOL BEYAZ
Yüksek Lisans
İngilizce
2024
Biyoteknolojiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. FATOŞ YÜKSEL GÜVENİLİR
- Tıbbi nane (Mentha piperita) yağının mikrokapsüllenerek denim kumaşa aktarılması ile kumaşa antibakteriyel özellik kazandırılmasının araştırılması
Research of antibacterial properties of denim fabric treated with microencapsulation of medical mint oil (Mentha piperita)
MERVE DOĞAN
Yüksek Lisans
Türkçe
2019
Kimya Mühendisliğiİnönü ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. ADIGÜZEL MEHMET YÜCEER
- Synthesis of dendronized polymers by ring opening metathesis polymerization techniques and investigation of biological activities
Halka açılım metatez polimerizasyon tekniği ile dendrize polimerlerin sentezi ve biyolojik aktivitelerin incelenmesi
MUHAMMAD NAZRUL ISLAM
- Fabrication and characterization of reverse osmosis membranes having antibacterial properties
Antibakteriyel özellik kazandırılmış ters osmoz membranların üretimi ve karakterizasyonu
ŞEYMA YILMAZ
Yüksek Lisans
Türkçe
2015
Çevre Mühendisliğiİstanbul Teknik ÜniversitesiÇevre Mühendisliği Ana Bilim Dalı
DOÇ. DR. DERYA YÜKSEL İMER