Toz metalurjisi yöntemi ile üretilen L21 yapısındaki Fe-Al-Ti alaşımların yüksek sıcaklık mekanik özellikleri
High temperature mechanical properties of Fe-Al-Ti alloys in L21 structure produced by powder metallurgy method
- Tez No: 690578
- Danışmanlar: DOÇ. DR. İBRAHİM ÇELİKYÜREK
- Tez Türü: Doktora
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Sinterleme, Sintering
- Yıl: 2021
- Dil: Türkçe
- Üniversite: Eskişehir Osmangazi Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Malzeme Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada; Kıvılcımlı Plazma Sinterleme ile yapısında L21 Heusler fazı içeren 4 farklı bileşimde Fe-Al-Ti üçlü alaşımları sentezlenmiş ve bu alaşımların yüksek sıcaklık mekanik özellikleri incelenmiştir. Vakum ark ergitme yöntemi ile hazırlanan Fe50Al40Ti10, Fe50Al35Ti15, Fe50Al30Ti20 ve Fe50Al25Ti25 tipi üç bileşenli Demir Alüminat ön alaşımlar; mekanik öğütme işlemi ile toz hale getirilmiş ardından kıvılcımlı plazma sinterleme (SPS) ile sentezlenmiş ve sentezlenen alaşımların oda sıcaklığındaki ve yüksek sıcaklıklardaki mekanik özellikleri incelenmiştir. Uygun kimyasal bileşimi sağlamak üzere oranlarda hazırlanan şarj malzemesi, vakum ark fırınında homojenliği sağlamak için iki kez ergitilmiş, daha sonra bakır kalıba dökülmüştür. Daha sonra bu alaşımlar başlangıçta kaba kırma ve öğütme yapılarak 20 – 45 µm boyut aralığında alaşım tozları elde edilmiştir. SPS yöntemi ile 20 mm çaplı disk şeklinde alaşımlar sentezlenmiştir. Sentezlenen bu alaşımların mikroyapıları optik mikroskopi ve SEM ile incelenmiştir. Faz Malzeme karakterizasyonu için X-ışını Kırınımı (XRD) ve Enerji Dağılım Spektrometresi (EDS) kullanılmıştır. Alaşımların sertlik değerleri mikrosertlik cihazında ölçülmüştür. Bu alaşımlardan tel erozyon yöntemi ile basma testi numuneleri hazırlanmıştır. Alaşımların oda sıcaklığı oda sıcaklığındaki ve yüksek sıcaklıklardaki (600 - 900 °C) basma mukavemeti ve süneklik değerleri kıyaslanmıştır. Sonuç olarak alaşım içerisindeki Ti miktarının artmasıyla sertlik ve basma mukavemetinde artış gözlenmiştir.
Özet (Çeviri)
In this study;, Fe-Al-Ti ternary alloys in 4 different compositions containing L21 Heusler phase were synthesized by using Spark Plasma Sintering and the high temperature mechanical properties of these alloys were investigated. Ternary Iron Aluminate pre-alloys of Fe50Al40Ti10, Fe50Al35Ti15, Fe50Al30Ti20 and Fe50Al25Ti25 prepared by vacuum arc melting method. Pre-alloys were pulverized by mechanical milling, then synthesized by spark plasma sintering (SPS) and the mechanical properties of the synthesized alloys at room temperature and high temperatures were investigated. Charge material prepared in proportions to provide the appropriate chemical composition were melted twice in order to ensure homogeneity in the vacuum arc furnace, later casted in to copper mold. These cast parts were coarse crushed then milled to obtain alloy powders which particles size range in 20 - 45 µm. Sintered disc shaped alloys with 20 mm diameter were synthesized by SPS method. Microstructures of these synthesized alloys were examined by optical microscopy and SEM. Phase identification has been carried out by means of X-ray powder diffraction (XRD) and energy-dispersive spectrometry (EDS). Alloys hardness was determined on Microhardness tester. Compression test samples were prepared from these alloys by electrical discharge machining (EDM). Compressive strength and ductility values of the alloys at room temperature and elevated temperatures (600 - 900 °C) were compared. As a result, it was observed that the hardness and compressive strength increased with Ti addition.
Benzer Tezler
- Enerji depolama için grafen tabanlı üç boyutlu elektrot malzeme uygulamaları
Graphene-based three-dimensional electrode material applications for energy storage
DENİZ KURUAHMET
Doktora
Türkçe
2023
EnerjiSakarya ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. MEHMET OĞUZ GÜLER
- Toz metalurjisi yöntemi ile üretilen Cu-%25Cr elektrik kontak malzemesinin sinterlenme davranışlarının incelenmesi
An Investigation in the sintering behavior of the Cu-25wt%Cr electrical contact materials produced by powder metallurgy technique
HALİL İBRAHİM BAKAN
- Toz metalürjisi yöntemi ile üretilen Al matrisli Al2O3 takviyeli kompozitin sürtünme kaynağının araştırılması
The Investigation of friction welding of Al matrix-Al2O3 reinforced composite produced by powder metallurgy process
ERKAN ŞAHAN
Yüksek Lisans
Türkçe
2002
Makine MühendisliğiFırat ÜniversitesiMakine Eğitimi Ana Bilim Dalı
YRD. DOÇ. DR. AHMET HASÇALIK
- Toz metalurjisi yöntemi ile üretilen Cu-C-Al2SiO5 kompozitinin abrasiv aşınma dayanımının araştırılması
The investigation of abrasive wear of Cu-C-Al2SiO5 composite producted by powder metallurgy process
ÇETİN ÖZAY
Yüksek Lisans
Türkçe
2004
Makine MühendisliğiFırat ÜniversitesiMakine Eğitimi Ana Bilim Dalı
Y.DOÇ.DR. AHMET HASÇALIK
- Toz metalurjisi yöntemi ile üretilen AA7075 alüminyum alaşımına TI ve B4C ilavesinin aşınma davranışı üzerine etkisinin incelenmesi
An investigation of the effects of added TI and B4C on wear behaviour in AA7075 alloy produced by powder metallurgy route.
HARUN AY
Yüksek Lisans
Türkçe
2014
Mühendislik BilimleriKarabük Üniversitesiİmalat Mühendisliği Ana Bilim Dalı
DOÇ. DR. DURSUN ÖZYÜREK