Dijital ortamda 3 boyutlu yazıcılarda üretilen zirkonya örneklerin bazı mekanik özelliklerinin ve üstyapı seramiği ile olan bağlantı dayanımının incelenmesi

Investigation of some mechanical properties of zirconia samples produced in 3-dimensional printers in a digital environment and the strength of connection with veneer ceramics

PDF İndir

  1. Tez No: 687417
  2. Yazar: HALİL BAKIÇ
  3. Danışmanlar: PROF. DR. TURAN KORKMAZ
  4. Tez Türü: Doktora
  5. Konular: Diş Hekimliği, Dentistry
  6. Anahtar Kelimeler: Dental porselen, Dental protezler, Dental stres analizi, Diş kaplamaları, Mekanik özellikler, Sayısal yazıcılar, Yüzey sertliği, Zirkonyum oksit, Üç boyutlu yazıcı, Dental porcelain, Dental prosthesis, Dental stress analysis, Dental veneers, Mechanical properties, Digital printers, Surface hardness, Zirconium oxide, Three dimensional printer
  7. Yıl: 2021
  8. Dil: Türkçe
  9. Üniversite: Gazi Üniversitesi
  10. Enstitü: Sağlık Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
  12. Bilim Dalı: Protetik Diş Tedavisi Bilim Dalı
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

Bu çalışmada eklemeli üretim (üç boyutlu litografi) ile oluşturulmuş seramik örnekler ile eksiltmeli üretim (CAD-CAM) ile oluşturulmuş seramik örneklerin bazı mekanik özellikleri in-vitro olarak değerlendirildi. Çalışmada kullanılan zirkonya örneklerin oluşturulması amacıyla üç boyutlu litografi üretim tekniği ve CAD-CAM sistemler kullanılmıştır. Mekanik özelliklerin değerlendirilmesinde; bükülme dayanımı testi, çentik kırılma tokluğu testi, sertlik testi kullanılırken, üstyapı seramikleri ile olan bağlantının test edilmesi için de makaslama testi uygulandı. Ayrıca örneklere EDS ve tanecik analiz testleri uygulandı. EDS ve tanecik analizi FE-SEM cihazında testler uygulanmadan önce yapıldı. Bükülme dayanımı testinde kırılan parçaların kırık yüzeylerinin analizi hem FE-SEM cihazında hem de optik mikroskopta değerlendirildi. Makaslama testi sonrasında ise örneklerin yüzeyleri kopma türlerinin belirlenmesi amacıyla optik mikroskopta incelendi. Elde edilen sonuçlar doğrultusunda en yüksek bükülme dayanımı lithografi tekniği ile üretilen zirkonya örneklerde ortalama 1173±160.9 MPa olarak elde edilmiştir. En düşük bükülme dayanımı, eksiltmeli yöntemlerle üretilen zirkonya grubunda 818.5±265.8 MPa olarak bulundu. Her iki grubun bükülme dayanımları arasında istatistiksel olarak anlamlı bir fark gözlemlenmiştir (P<0001). Eksiltmeli ve eklemeli yöntemlerle hazırlanan zirkonya örnekler yüzey sertliği ve kırılma tokluğu değeri bakımından karşılaştırıldığında, istatistiksel olarak anlamlı bir fark bulunmadı (P>0.05). Makaslama bağlanma testi sonucunda ise zirkonya grupları arasında istatistiksel olarak anlamlı bir fark gözlemlenmemiştir (P=0.9862). Elde edilen bulgular doğrultusunda eklemeli üretim yöntemi (lithografi) ile üretilen zirkonyanın dayanımı göz önüne alındığında dental kullanım için yeterlidir. Her iki grubun üstyapı seramiği ile olan bağlanma dayanımları değerlendirildiğinde, eklemeli üretim yöntemi ile hazırlanan örneklerin bağlanma dayanımı eksiltmeli üretim (CAD-CAM) kadar iyi olduğu sonucuna varılmıştır.

Özet (Çeviri)

In this study, some mechanical properties of ceramic samples fabricated by additive manufacturing (three-dimensional lithography) and subtractive manufacturing (CAD-CAM) were evaluated in-vitro. Three-dimensional lithographic production techniques and CAD-CAM systems were used to create the zirconia samples used in the study. In evaluating mechanical properties; the bending strength test, indentation fracture toughness test, and hardness test were used. Moreover, the shear test was applied to test the connection with the superstructure ceramics. In addition, EDS and particle analysis tests were applied to the samples. EDS and particle analysis were performed on the FE-SEM device before the tests were performed. The analysis of the fracture surfaces of the broken parts in the flexural strength test was evaluated both in the FE-SEM device and in the optical microscope. After the shear test, the surfaces of the samples were examined under an optical microscope to determine the failure types. In line with the results obtained, the highest flexural strength was obtained as 1173±160.9 MPa in zirconia samples produced by the lithography technique. The lowest bending strength is 818.5±265.8 MPa in the zirconia group produced by subtractive methods. A statistically significant difference was observed between the bending strengths of both groups (P<0001). When the zirconia samples prepared by subtractive and additive methods were compared in terms of surface hardness and fracture toughness, no statistically significant difference was found (P>0.05). As a result of the shear bond test, no statistically significant difference was observed between zirconia groups in both production methods (P=0.9862). Considering the strength of the zirconia produced by the additive manufacturing method (lithography) in line with the findings obtained, it is sufficient for dental use. When the bond strength values with the superstructure ceramic are evaluated, the values obtained in the samples prepared by the additive manufacturing method are as good as the subtractive manufacturing (CAD-CAM).

Benzer Tezler

  1. Tez No

    841854

    Dijital tasarım araçları ile yeniden yorumlanan ve üretilen froebel blokları üzerinden 4-6 yaş çocukların mekan-hackleme süreçlerinin değerlendirilmesi

    Evaluation of space-hacking process of 4-6 year old children through froebel blocks reinterpreted and produced with digital design tools

    NİLHAN KAYA

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    Eğitim ve Öğretimİstanbul Teknik Üniversitesi

    İç Mimarlık Ana Bilim Dalı

    DOÇ. DR. ETHEM GÜRER

  2. Tez No

    780950

    Transdermal ilaç dağıtımı için mikropartikül kaplı mikroiğne iskelelerinin üretimi ve karakterizasyonu

    Fabrication and characterization of micriparticle coated microneedle scaffolds for transdermal drug delivery

    ESRA PİLAVCI

    Yüksek Lisans

    Türkçe

    Türkçe

    2023

    BiyomühendislikMarmara Üniversitesi

    Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı

    PROF. DR. OĞUZHAN GÜNDÜZ

    DR. SÜMEYYE CESUR

  3. Tez No

    497534

    Extracting auxetic patterns from meshes for 3d printing

    Eklemeli üretim için örgü yapılarından ogzetik desenlerin çıkarılması

    LEVEND MEHMET MERT

    Yüksek Lisans

    İngilizce

    İngilizce

    2018

    Bilgisayar Mühendisliği Bilimleri-Bilgisayar ve KontrolOrta Doğu Teknik Üniversitesi

    Bilgisayar Mühendisliği Ana Bilim Dalı

    DOÇ. DR. YUSUF SAHİLLİOĞLU

    YRD. DOÇ. DR. ULAŞ YAMAN

  4. Tez No

    620749

    Tool as design variant

    Tasarım değişkeni olarak gereçler

    BETÜL ORBEY

    Doktora

    İngilizce

    İngilizce

    2016

    Mimarlıkİstanbul Teknik Üniversitesi

    Bilişim Ana Bilim Dalı

    PROF. DR. SİNAN MERT ŞENER

  5. Tez No

    935291

    Üç farklı teknikle üretilen posterior adeziv restorasyonların mekanik özelliklerinin İn-vitro incelenmesi

    In-vitro evaluation of the mechanical properties of posterior adhesive restorations fabricated using three different techniques

    GÖZDE ACAR

    Diş Hekimliği Uzmanlık

    Türkçe

    Türkçe

    2025

    Diş HekimliğiEge Üniversitesi

    Restoratif Diş Tedavisi Ana Bilim Dalı

    DOÇ. DR. CEM PEŞKERSOY

Geri Dön