Ultrasonik yöntemlerle küresel grafitli dökme demirlerde mikroyapı kontrolü

The Microstructure control by ultrasonic methods in ductile iron

  1. Tez No: 67728
  2. Yazar: A.KAMELYA DÖĞÜŞÇÜ
  3. Danışmanlar: PROF. DR. AHMET TOPUZ
  4. Tez Türü: Yüksek Lisans
  5. Konular: Metalurji Mühendisliği, Metallurgical Engineering
  6. Anahtar Kelimeler: Görüntü analizi, Küresel grafitli dökme demirler, Mikroyapı, Ostemperleme, Ultrasonografi, Image analysis, Nodular graphite cast irons, Microstructure, Austempering, Ultrasonography
  7. Yıl: 1997
  8. Dil: Türkçe
  9. Üniversite: Yıldız Teknik Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Metalurji Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Malzeme Bilim Dalı
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

ÖZET Küresel grafitli dökme demirlerin günümüzde çok önemli bir malzeme grubunu teşkil ettiği herkesçe kabul edilmektedir. Küresel grafitli dökme demirlere bu ayrıcalığı sağlayan mekanik özellikleri korozyon direncidir, bilhassa östemperleme ısıl işlemi ile mekanik özelliklerde bir artış sağlanmaktadır. Mekanik özelliklerini, matris yapısı yanında etkileyen en önemli etken yapıda küresel formda bulunan grafitlerin; küreselleşme yüzdesi, hacimsel miktar' ve boyutudur. Bunlara döküm işlemleri ve aşılama ile en optimum değerlere ulaşılması amaçlanmaktadır. Kaliteli bir üretim için mikroyapıdaki matris ve küresel grafit durumunun incelenmesi zorunludur. Bu inceleme ülkemizde genellikle metalografik yöntemle ve görüntü analiz sistemi ile yapılabilmektedir. Bu durum uygun olması ile birlikte zaman alması ve bölgesel inceleme yapma sağladığından daha hızlı ve kolay muayene yöntemleri araştırılmış olup bu konuda ultrasonik hız ölçme tekniği ile küresel grafitli dökme demirlerin matris yapısı, küreselleşme yüzdeleri ile küresel grafit miktarı bulunabilmektedir. Bu çalışmada DDK 40 (ferritik) ve DDK 60 (perlitik) rumuzlu ferritik ve perlitik matrisli küresel grafitli dökme demirlerde döküldükleri konumda görüntü analiz sistemi yardımı ile (Buehler-Omnimet Advantage), ferrit-perlit miktarları, grafit miktarı, grafit boyutu, küre sayısı ve küreselleşme yüzdeleri ölçülmüştür. Çekme testi ve sertlik ölçümleri ile çekme mukavemeti, uzama yüzdesi ve sertlik değerleri belirlenmiştir. Daha sonra aynı numuneler üzerinde ultrasonik hız ölçümleri yapılarak ultrasonik hız ölçümleri ile matris yapısındaki değişimi, küreselleşme, küre sayısı, perlit miktarı, grafit boyutu arasındaki bağlantıyı veren diyagramlar elde edilmiştir. IXand hardness tests. Then, by measuring ultrasonic velocity on the same samples, the diagrams that show the relationship between the change in matrix structure, nodularity, number of nodules, pearlite amount and graphite size are obtained. In these castings, the austempering heat treatment has an important role. So, for the other part of project, the effect of the bainitic microstructure has been searched by measuring the ultrasonic velocity on the ductile iron austempered at 370°C, 275°C and 235°C after austenizing at 900°C. xn

Özet (Çeviri)

SUMMARY Nowadays, it is accepted that the ductile cast iron constitutes very important part of material group. The corrosion resistance and the mechanical properties give this privilege to ductile cast iron. Especially, there is an increase in the mechanical properties by austempering heat treatment. Besides matrix structure, the most important factors that affect the mechanical properties are the nodularity percentage, volame fraction and the graphite size that exists in uıe spherical form in the structure. it is aimed to achieve the most optimum values of these parameiers by casting processes and the inoculation method. in order to obtain the quality in production, it is necessary to examine the matrix and the nodular graphite situation of the microstructure. in our country, this examination is usually performed by metallographic method and the image analysis system. Although these methods are appropriate, it takes too much time and only the regional examination is possible. So, more fast and easy inspection techniques have been searched and it is found that by ultrasonic velocity measuring technique, the matrix structure, the percentage of nodularity and the nodular graphite amount of ductile cast iron can be detected. in this study, two kinds of the ductile cast iron symbolized as DDK 40 (ferritic) and DDK 60 (pearlitic) are evaluated as cast condition by image analysis system (Buehler- Omnimet Advantage). By this method the volume fraction of pearlite, ferrite and graphite, percentage of nodularity, number of nodules, graphite sizes of these samples are measured. Also, the tensile strength, elongation and hardness values of these specimens are obtained by tensile XIand hardness tests. Then, by measuring ultrasonic velocity on the same samples, the diagrams that show the relationship between the change in matrix structure, nodularity, number of nodules, pearlite amount and graphite size are obtained. In these castings, the austempering heat treatment has an important role. So, for the other part of project, the effect of the bainitic microstructure has been searched by measuring the ultrasonic velocity on the ductile iron austempered at 370°C, 275°C and 235°C after austenizing at 900°C. xn

Benzer Tezler

  1. Tez No

    17924

    İstifli polivinilklorür (PVC) yapısının mekaniksel anizotropisinin ultrasonik teknikle incelenmesi

    Başlık çevirisi yok

    H.SİNAN ÖZKAN

    Doktora

    Türkçe

    Türkçe

    1991

    Fizik ve Fizik MühendisliğiKaradeniz Teknik Üniversitesi

    Fizik Ana Bilim Dalı

    YRD. DOÇ. DR. TANER OSKAY

  2. Tez No

    31195

    Çeşitli yöntemlerle detoksifiye edilen kök yüzeylerine fibroblast ataşmanının incelenmesi

    Başlık çevirisi yok

    NİHAL ALPDOĞAN

    Doktora

    Türkçe

    Türkçe

    1993

    Diş HekimliğiGazi Üniversitesi

    Periodontoloji Ana Bilim Dalı

    DOÇ. DR. COŞKUN BARAN

  3. Tez No

    35433

    Biomechanical aspects of osteoroposis effect of medication on biomechanical properties of robbit bones in heparin induced osteoporosis and ultrasonic properties of human Bones senile osteoporosis

    Osteoporozun biyomekanik yönleri: heparinle yaratılan osteoporozda ilaçların tavşan kemiklerinin biyomekanik özellikleri üzerindeki etkisi ve yaşlılık osteoporozunda insan kemiklerinin ultrasonik özellikleri

    YENER NAİL YENİ

    Yüksek Lisans

    İngilizce

    İngilizce

    1994

    BiyolojiOrta Doğu Teknik Üniversitesi

    Mühendislik Bilimleri Ana Bilim Dalı

    PROF. DR. CEVDET AKGÖZ

  4. Tez No

    47130

    Biomechanical evaluation of frodure healing in long bones: An Experimental study on intromedullary stabilized rabbit tibia

    Uzun kemiklerdeki transvers kırıklarda iyileşme sürecinin biyomekanik takibi: İntramodüller fiksasyon ile sabitleşmiş tavşan tibiası üzerinde deneysel çalışma

    OZAN AKKUŞ

    Yüksek Lisans

    İngilizce

    İngilizce

    1995

    Mühendislik BilimleriOrta Doğu Teknik Üniversitesi

    DOÇ.DR. UĞUR GÜNEL

    PROF.DR. NURİ AKKAŞ

  5. Tez No

    18154

    Smear tabakası"'nın varlığında ve yokluğunda doldurulan kök kanallarında apikal sızıntının incelenmesi

    Başlık çevirisi yok

    IŞIL KARAGÖZ KÜÇÜKAY

    Doktora

    Türkçe

    Türkçe

    1990

    Diş Hekimliğiİstanbul Üniversitesi

    Diş Hastalıkları ve Tedavisi Ana Bilim Dalı

    PROF.DR. GÜNDÜZ BAYIRLI

Geri Dön