Improving the flame retardancy using nanoparticles in cable insulation
Kablo izolasyonunda nanopartiküller kullanılarak alev geciktirici özelliğin geliştirilmesi
- Tez No: 676410
- Danışmanlar: DR. ÖĞR. ÜYESİ ALİ DURAN
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Makine Mühendisliği, Kimya Mühendisliği, Metallurgical Engineering, Mechanical Engineering, Chemical Engineering
- Anahtar Kelimeler: Alüminyum hidroksit, Etilen vinil asetat, Magnezyum hidroksit, Aluminum hydroxide, Ethylene vinyl acetate, Magnesium hydroxide
- Yıl: 2021
- Dil: İngilizce
- Üniversite: Abdullah Gül Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Malzeme Bilimi ve Nanoteknoloji Ana Bilim Dalı (disiplinlerarası)
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Al(OH)3 (ATH) ve Mg(OH)2 (MDH) gibi maddeler, ısı etkisi altında su ve oksit bazlı madde oluşturma kabiliyetleri nedeniyle alev geciktirici olarak yaygın bir şekilde kullanılmaktadırlar. Bu çalışmada, nano boyutta Mg(OH)2 sentezlenerek, bu maddenin EVA (etilen-vinil-asetat) kopolimeri ve mikro boyutta Al(OH)3 ve Mg(OH)2 ile birlikte kullanılması ile alev geciktirici özellikleri geliştirilmiş kablo izolasyonları üretilmesi amaçlanmıştır. Çalışma dört bölüme ayrılabilir. Birinci bölümde ATH ve MDH'nin alev geciktirici özellikleri karşılaştırılmıştır. İkinci bölümde, Mg(OH)2 nanopartikülleri farklı hammaddeler kullanılarak sentezlenmiştir. Üçüncü bölümde sentez, fabrika boyutunda yapılmış ve ticari ürün ile karşılaştırılmıştır. Örnekler, taramalı elektron mikroskobu (SEM), Fourier dönüşümü kızılötesi spektrometresi (FT-IR), X-Işını difraktometresi (XRD), X-Işını floresans spektrometresi (XRF) ve Termogravimetrik analiz (TGA) ile karakterize edilmiştir. Son bölümde, ATH ve MDH kullanılan formüllere farklı miktarlarda nano boyutlu Mg(OH)2 partikülleri eklenmiş; Limit Oksijen İndeksi (LOI) testi ve dikey yanma testi ile alev geciktirici performansları üzerindeki etkileri araştırılmıştır. Uzama ve çekme dayanımı gibi mekanik özellikler de incelenmiştir. ATH bazlı numunelerde maksimum %9, MDH bazlı numunelerde maksimum %10 oranında karıştırılan, 5-10 nm kalınlıkta ve yer yer uzunlukları 900 nm'ye ulaşan Mg(OH)2 partikülleri LOI değerleri; ATH bazlı numuneler için %26 ve MDH bazlı numuneler için %38 oranında artmıştır. Ancak nanopartikül katkısının artmasıyla mekanik özelliklerde yaşanan kayıplar dikkate alındığında, maksimum %5 oranda nano boyutlu Mg(OH)2 eklenebileceği görülmüştür. Bu durumda bile LOI değerleri ATH bazlı örneklerde %8,6 iken MDH bazlı örneklerde %26 oranında artmıştır.
Özet (Çeviri)
Al(OH)3 (ATH) and Mg(OH)2 (MDH) like materials are frequently used as flame retardants due to their ability to form water and oxide-based substances under the influence of heat. In this study, it is aimed to produce cable insulations with improved flame retardant properties by synthesizing nano-sized Mg(OH)2 and using this material together with EVA (ethylene-vinyl-acetate) copolymer and micro-sized Al(OH)3 and Mg(OH)2 . The study can be divided into four parts. In the first part, the flame retardant properties of ATH and MDH were compared. In the second part, different raw materials were used for the synthesis of Mg(OH)2 nanoparticles; in the third part, the synthesis was carried out at factory scale and compared with the commercial product. The samples were characterized by scanning electron microscopy (SEM), Fourier transform infrared spectrometer (FT-IR), X-Ray diffraction analysis (XRD), X-Ray fluorescence analysis (XRF) and Thermogravimetric analysis (TGA). In the last part, different amounts of nano-sized Mg(OH)2 particles were added to the formulas using both ATH and MDH; the effects on flame retardant performances were investigated by the Limiting Oxygen Index (LOI) test and the vertical burning test. Mechanical properties such as elongation and tensile strength were also studied. It has been observed that the synthesized Mg(OH)2 particles with a thickness of 5-10 nm and lengths reaching 900 nm, mixed in ATH based samples at a maximum rate of 9% and in MDH based samples at a maximum rate of 10%; LOI values increased by 26% for ATH based samples and 38% for MDH based samples. However, considering the losses in mechanical properties with the increase of nanoparticle additive, it has been seen that a maximum rate of 5% nano-sized Mg(OH)2 can be added. Even in this case, the LOI values increased by 8.6% in ATH based samples and 26% in MDH based samples.
Benzer Tezler
- POSS modifiye alev geciktirici doymamış polyester reçine sentezi ve karakterizasyonu
Synthesis and characterization of POSS modified flame retardant unsaturated polyester resin
SERPİL İPEK
Yüksek Lisans
Türkçe
2023
Polimer Bilim ve TeknolojisiMarmara ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. NİLHAN KAYAMAN APOHAN
- Development of novel biopolyamide compounds as a green and sustainable alternative to petroleum derived polymers and their applications in medical field
Petrolden elde edilen polimerlere yeşil ve sürdürülebilir bir alternatif olarak özgün biyopoliamit bileşiklerinin geliştirilmesi ve tıbbi alanda uygulamaları
ŞEBNEM GÜLEL
Doktora
İngilizce
2024
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. FATOŞ YÜKSEL GÜVENİLİR
- Styrene - butadiene rubber / halloysite nanotubes nanocomposites modified by itaconic acid
İtakonik asitle modifiye edilmiş stiren - bütadien kauçuk / haloysit nanotüp nanokompozitleri
GİZEM UZAN
Yüksek Lisans
İngilizce
2014
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
PROF. DR. NURSELİ UYANIK
YRD. DOÇ. DR. BAĞDAGÜL KARAAĞAÇ
- Borik asit katkısıyla su bazlı iç cephe boyalarının alev dayanımının iyileştirilmesi
Improving flame retardancy of water based indoor paints with addition of boric acid
BERK USLU
Yüksek Lisans
Türkçe
2019
Kimya MühendisliğiGazi ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. NURSEL DİLSİZ
- Improvement of flame retardancy and mechanical properties of biobased polylactic acid compounds
Biyo bazlı polilaktik asit harmanlarının mekanik mukavemet ve yanma dayanımı özelliklerinin iyileştirilmesi
CEREN YARGICI KOVANCI
Doktora
İngilizce
2023
Polimer Bilim ve Teknolojisiİstanbul Teknik ÜniversitesiPolimer Bilim ve Teknolojisi Ana Bilim Dalı
DOÇ. DR. MOHAMMADREZA NOFAR