Evaluation of PH and calcium release of novel calcium-based materials used in vital pulp therapies
Vital pulpa tedavilerinde kullanılan güncel kalsiyum bazlı materyallerin PH ve kalsiyum saliminin değerlendirilmesi
- Tez No: 673206
- Danışmanlar: PROF. DR. SENEM SELVİ KUVVETLİ
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: MTA Angelus, Biodentine, TheraCal, kalsiyum salınımı, Biodentin, Dental materyaller, Dental pulpa, Hidrojen iyon konsantrasyonu, Kalsiyum, TheraCal, MTA Angelus, Biodentine, Calcium release, Dental materials, Dental pulp, Hydrogen-ion concentration, Calcium
- Yıl: 2021
- Dil: İngilizce
- Üniversite: Yeditepe Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Çocuk Diş Hekimliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı; pulpa kaplamasında kullanılan kalsiyum esaslı materyallerin, pH ve kalsiyum salımı değerlerini in vitro koşullarda karşılaştırmalı olarak değerlendirmektir. Kalsiyum hidroksit esaslı materyaller; Dycal, Ultra-Blend plus ve kalsiyum silikat esaslı materyaller TheraCal LC, MTA Angelus ve Biodentine hazırlanıp, kalıplara yerleştirilmiş (çap: 8,0 ± 0,1 mm; kalınlık: 1,6 ± 0,1 mm) (n = 10) ve10 mL deiyonize suya konmuştur. 1, 3, 7, 14 ve 28. günde solüsyonlar, pH ve kalsiyum salımı ölçümü için toplanmış ve yenilenmiştir. pH ölçümleri pH-metre (pH 2100 serisi; pH / mV / Ion / ° C / ° F Metre ile RS232 ve kaydedici çıkışı; OAKTON Instruments, Vernon Hills, IL ABD) ve kalsiyum salımı, Atomik Absorbsiyon Spektrofotometresi (Zeenit 700 P, Analytik Jena AG, Almanya) ile yapılmıştır. Tüm materyaller 28 gün içinde, hidroksil ve kalsiyum iyonları salmış; ayrıca Dycal grubunda gözlenen kalsiyum salımındaki artış eğilimi dışında, bu salım zamanla azalmıştır. 1 ve 3. Gün, en yüksek pH, MTA Angelus ve Biodentine gruplarında gözlenirken (p<0,005); 28. Günde ise en yüksek değerler Dycal ve Biodentine gruplarında ölçülmüştür (p<0,05). Biodentine grubunun 1. Günde en yüksek kalsiyum salım değerlerine sahip olduğu (p=0,0001); 28. Günde de Dycal grubu dışındaki tüm materyal gruplarından anlamlı düzeyde yüksek olduğu görülmüştür (p<0,05). 28. Günde, tüm gruplar arasında en düşük miktarda kalsiyum iyon salımı, Ultra-Blend plus materyal grubunda ölçülmüştür (p=0,0001). 1. Günde MTA Angelus, Dycal ve Ultra-Blend plus grupları arasında anlamlı fark yokken; 28. Günde Dycal materyal grubu Biodentin dışındaki tüm materyal gruplarından daha yüksek miktarda kalsiyum iyon salımı göstermiştir (p<0,05). Sonuç olarak; bu in vitro çalışmada değerlendirilen kalsiyum hidroksit ve kalsiyum silikat esaslı mataryellerin, sert doku oluşumu için gerekli iyonların salınımında başarılı olduğu gözlenmiştir. Özellikle Biodentine materyal grubunun, kısa dönemde diğer gruplardan daha fazla hidroksil ve kalsiyum iyonu serbestlediği, uzun dönemde ise Dycal materyal grubu dışındaki tüm gruplardan istatistiksel olarak anlamlı düzeyde daha yüksek pH ve kalsiyum iyon salım değerlerine sahip olduğu görülmüştür.
Özet (Çeviri)
The aim of this study is to evaluate and compare the pH values and the calcium release of various pulp capping materials, in vitro. Calcium hydroxide-based materials; Dycal, Ultra-Blend plus and calcium silicate-based materials TheraCal LC, MTA Angelus, Biodentine and were prepared and placed into molds (diameter: 8.0±0.1 mm; thickness: 1.6±0.1 mm) (n=10). Set samples were immersed in the 10 mL of deionized water. On Day 1, 3, 7,14 and, 28 the storage media were collected for measurement of pH and calcium release and refreshed. The measurements of pH were carried out with a pH-meter (pH 2100 series; pH/mV/Ion/°C/°F Meter with RS232 and Recorder output; OAKTON Instruments, Vernon Hills, IL USA) and the amount of calcium release was determined using an Atomic Absorption Spectrophotometer (Zeenit 700 P, Analytik Jena AG, Germany). All the material groups released both hydroxyl and calcium ions over 28 days which decreased gradually. Exceptionally, the Dycal group showed a tendency to increase regarding calcium ion release. The mean pH was found significantly highest in the MTA Angelus and Biodentine groups in short term (Day 1 and 3) (p<0.005); and Dycal and Biodentine groups in long term (Day 28) (p<0.05). Biodentine group showed significantly the highest amount of calcium ion release among all the material groups in Day 1 (p=0.0001); also highest in Day 28 except Dycal group (p<0.05). On Day 28 the least amount of calcium ion release was measured in the Ultra-Blend plus group among all material groups (p=0.0001). There were no statistically significant differences between the mean amount of calcium ions in MTA Angelus, Dycal, and Ultra-Blend plus groups in Day 1; however, on Day 28, the Dycal material group showed significantly higher calcium ion release than the other material groups except Biodentine (p<0.05). As conclusion; both calcium silicate and calcium hydroxide-based materials tested in this in vitro study were found successful in the release of products required for hard tissue formation. Especially Biodentine group released significantly more calcium and hydroxyl ions in short term. In long term; Biodentine still showed statistically significantly the highest pH and calcium release among all material groups; except the Dycal material group.
Benzer Tezler
- Farklı güncel biyomateryaller ile doldurulan yapay rezorptif defektlere sahip kök kanallarında; ph değişiklikleri, kalsiyum iyon salınımı ve kırılma direncinin incelenmesi
Evaluation of ph changes, calcium ion release and fracture resistance of teeth with artificial root resorptions and filled using different contemporary biomaterials
SEBAHAT ÖZLER
- Farklı kalsiyum silikat esaslı materyallerin ortam pH'ına etkisi ve farklı pH değerlerinde çözünürlük, sıvı emilimi ve mikrosertliklerinin değerlendirilmesi
The effect of different calcium silicate-based materials on environmental pH and the evaluation of solubility, water sorption, and microhardness at different pH values
SEDA KILINÇ
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiNecmettin Erbakan ÜniversitesiEndodonti Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ŞEREF NUR MUTLU
- Fluorid bileşikleri ve linoleik asitle hazırlanan geçici simanın basma dayanımı, çözünürlük, fluorid salınımı, pH, radyo-opasite ve antimikrobiyal özelliklerinin araştırılması
Evaluation of compressive strength, disintegration, fluoride release, pH, radiopacity and antimicrobial properties of temporary cement prepared with fluoride compounds and linoleic acid
KERİME GÖZDE IŞIKSAL
- Doğal polimerler kullanılarak hazırlanan boncuk şeklindeki kontrollü salım sistemlerinin tasarımı ve gerçekleştirilmesi
Design and evaluation of controlled release bead dosage forms by using natural polymers
SEVGİ TAKKA
- Farklı kalsiyum silikat içerikli simanların fiziksel ve kimyasal özelliklerinin değerlendirilmesi
Evaluation of the physical and chemical properties of different calcium silicate-containing cements
KEMAL FURKAN GÜDÜL
Diş Hekimliği Uzmanlık
Türkçe
2025
Diş HekimliğiTokat Gaziosmanpaşa ÜniversitesiRestoratif Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ GÜLŞAH TONGA
DOÇ. DR. HÜSEYİN HATIRLI