Seramik oksit katkılı nano sentetik hidroksiapatit kompozitlerin üretimi ve karakterizasyonu
Production and characterization of ceramic oxide added nano synthetic hydroxyapatites composites
- Tez No: 629702
- Danışmanlar: DR. ÖĞR. ÜYESİ NERMİN DEMİRKOL
- Tez Türü: Yüksek Lisans
- Konular: Mühendislik Bilimleri, Engineering Sciences
- Anahtar Kelimeler: Hidroksiapatit, Mekanik Özellikler, Nano Biyokompozit, Nano Magnezyum Oksit, Nano Niyobyum Penta Oksit, Hydroxyapatite, Mechanical Properties, Nano Biocomposite, Nano Magnesium Oxide, Nano Niobium Penta Oxide
- Yıl: 2020
- Dil: Türkçe
- Üniversite: Kocaeli Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Biyomedikal Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Hidroksiapatit (HA) ideal biyoaktif malzemedir. Bir kalsiyum fosfat bileşiği olup, Ca10(PO4)6(OH)2 şeklinde gösterilir. Ayrıca, HA iyi biyouyumluluk ve mükemmel osteoiletkenlik göstermektedir. Kimyasal bileşimi ve yapısı, doğal kemik mineralli matrise çok benzemektedir. Nano hidroksiapatitin tane boyutunun kemikteki apatit minerallerine çok benzemesi nedeniyle nano hidroksiapatit üzerindeki araştırmalar büyük önem kazanmıştır. Bu çalışmada, ticari nano hidroksiapatitin mekanik özelliklerini arttırmak için nano magnezyum oksit (nMgO) ve nano niyobyum penta oksit (nNb2O5) takviye malzemesi olarak kullanılmıştır. Ağ. %80 nHA-ağ. %20 nMgO (nMH1), ağ. %70 nHA-ağ. %30 nMgO (nMH2) ve ağ. %80 nHA-ağ. %20 nNb2O5 (nNH1), ağ. %70 nHA-ağ. %30 nNb2O5 (nNH2) toksik olmayan bağlayıcı içeren kompozitler pres kullanılarak şekillendirildi. Kompozitler 1000 ve 1100 °C'de 2 saat süre ile sinterlendi, sonra nano kompozitlerin mikroyapıları mekanik özellikleri araştırıldı. Fiziksel ve mekanik özellikler yoğunluk, basma mukavemeti ve Vickers mikrosertlik (HV) ölçümleri ile tanımlandı. Yapısal karakterizasyon X-ışını kırınımı (XRD) ve taramalı elektron mikroskobu (SEM) ile ortaya kondu. Kompozitlerin biyoaktivite özellikleri simüle edilmiş vücut sıvısında numunelerin 1,2,3 ve 4 hafta bekletilmesinden sonra tanımlandı. Yoğunluk, basma mukavemeti ve Vickers mikrosertlik değerleri artan sinterleme sıcaklığı ile arttı. En iyi yoğunluk, basma mukavemeti ve Vickers mikrosertlik değerleri 1100C'de sinterlenen ağ.% 70 nHA + ağ.% 30 nMgO (nMH2) kompozit ile sırasıyla 3,16 g/cm3, 135 MPa ve 438 HV olarak elde edildi. (nMH2) ve (nNH2) kompozitler için simüle edilmiş vücut sıvısı (SBF) içinde 4 hafta bekletilen numunelerden elde edilen apatit tabakasının kalınlıkları sırasıyla 74 ve 80 m'dir. Her iki kompozitte biyoaktif özelliğe sahiptir.
Özet (Çeviri)
Hydroxyapatite (HA) is an ideal bioactive material. It is a calcium phosphate compound, indicated as Ca10(PO4)6(OH)2. Its chemical composition and structure are very similar to the mineralized matrix of natural bone. Due to the resemblance of grain sizes of nano hydroxyapatite to that of apatite minerals in bone, the researches of nano hydroxyapatite have become to gain great importance. In this study, in order to improve the mechanical properties of commercial nano hydroxyapatite (nHA), nano magnesium oxide (nMgO) and nano niobium pentaoxide (nNb2O5) was used as a reinforcement material. 80 wt% nHA-20 wt% nMgO (nMH1), 70 wt% nHA -30 wt% nMgO (nMH2) and 80 wt% nHA-20 wt% nNb2O5 (nNH1), 70 wt% nHA -30 wt% nNb2O5 (nNH2) nano composites including nontoxic binder were shaped by using press. The composites were sintered at 1000 and 1100°C for 2 hrs, then microstructures and mechanical properties of nano composites were investigated. The physical and mechanical properties were determined by measuring density, compression strength and Vickers microhardness (HV). Structural characterization was carried out with X-ray diffraction (XRD) and scanning electron microscopy (SEM). Density, compression strength and Vickers microhardness values increased with increasing sintering temperature. The best density, compression strength and Vickers microhardness values were obtained with 70 wt.% nHA-30 wt% MgO (nMH2) composite sintered at 1100C as 3.16 g/cm3, 135 MPa and 438 HV, respectively. The thickness of the apatite layer obtained from the samples soaked for 4 weeks in simulated body fluid for (nMH2) and (nNH2) composites were 74 and 80 m, respectively.
Benzer Tezler
- Nano boyutlu grafen oksit katkılı polimer kompozitlerin üretimi ve karakterizasyonu
Production and characterization of nanosize graphene oxide doped polymer composites
MERVE COŞKUN
Yüksek Lisans
Türkçe
2022
Mühendislik BilimleriAfyon Kocatepe ÜniversitesiNanobilim ve Nanoteknoloji Ana Bilim Dalı
PROF. DR. ATİLLA EVCİN
- Nano katkılı bizmut tabanlı süperiletken malzemelerin manyetik ve mekanik özelliklerinin incelenmesi
Investigation of the magnetic and mechanical properties of nano doped bismuth based superconductor materials
EMİNE BURCU CEVİZCİ
Doktora
Türkçe
2023
Fizik ve Fizik MühendisliğiDokuz Eylül ÜniversitesiFizik Ana Bilim Dalı
PROF. DR. KEMAL KOCABAŞ
- Elektrospinleme yöntemiyle grafen katkılı seramik nanolif üretimi ve karakterizasyonu
fabrication and characterization of ceramic nanofibers based graphene oxide by electrospinning
NESRİN KAYACI ÖZTÜRK
- Production and characterization of white light based on energy up conversion mechanisms in Yb+3,Nd+3,Tm+3 rare earth ions doped y2o3-sio2 nano-phosphor materials
Yb+3,Nd+3,Tm+3 nadir toprak iyon katkili Y2O3-SiO2 nanofosfor malzemelerde üst enerji̇ dönüşüm mekanizmasına dayalı beyaz ışık üretimi ve karakterizasyonu
HATUN ÇINKAYA YILMAZ
Doktora
İngilizce
2019
Fizik ve Fizik Mühendisliğiİstanbul Teknik ÜniversitesiFizik Mühendisliği Ana Bilim Dalı
PROF. DR. GÖNÜL ERYÜREK
- Grafen esaslı nano elektroseramiklerin üretilmesi ve karakterizasyonu
Production and characterization of graphene based nano electroceramics
CİHAT AYDIN
Doktora
Türkçe
2017
Metalurji MühendisliğiFırat ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MUSTAFA TAŞKIN
PROF. DR. FAHRETTİN YAKUPHANOĞLU