Kullanılmış Co-Mo-/Al2O3 katalizörünün kompleksleştirici EDTA varlığında çözünme şartlarının ve kinetiğinin incelenmesi
Investigation of dissolution conditions and kinetics in the presence of complexing agents of spent Co-Mo-Ni/Al2O3 catalyst
- Tez No: 600860
- Danışmanlar: DR. ÖĞR. ÜYESİ ALİ YARAŞ, DR. ÖĞR. ÜYESİ HASAN ARSLANOĞLU
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Kimya Mühendisliği, Mühendislik Bilimleri, Metallurgical Engineering, Chemical Engineering, Engineering Sciences
- Anahtar Kelimeler: EDTA, Kimyasal kinetik, Kimyasal çözeltiler, Liç çözeltisi, Sulu çözeltiler, EDTA, Chemical kinetics, Chemical solution, Leach solutions, Aqueous solutions
- Yıl: 2019
- Dil: Türkçe
- Üniversite: Bartın Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Metalurji ve Malzeme Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tez çalışmasında; kompleks yapıcı ajan varlığında kullanılmış hidrodesülfürizasyon (HDS) katalizöründen molibden (Mo), nikel (Ni), kobalt (Co) ve alüminyum (Al) metallerinin geri kazanımına ait proses şartları incelenmiştir. Metal iyonları ile bağlanma kabiliyetinin yüksek olması nedeniyle etilendiamin tetra asetik asit (EDTA) liç prosesinde kompleksleştirici reaktif olarak kullanıldı. Deneylerde katalizör bünyesindeki metalleri daha kolay çözünebilir formlara dönüştürmek amacıyla kullanılmış katalizöre ilk olarak kavurma ön işlemi uygulandı. Sonrasında Mo, Ni ve Co metalleri sırasıyla pH:2, pH:6 ve pH:10 değerlerinde amonyum molibdat, nikel dimetilglisoksim ve kobalt hidroksit formlarında çökeltilerek liç işlemi seçimli olarak gerçekleştirildi. En yüksek metal ekstraksiyon verimlerine (% 90.22 Mo,% 96.71 Co,% 95.31 Ni ve % 19.98 Al) optimum deney şartlarında ulaşıldı. Prosese ait termodinamik verilere göre; Co, Mo ve Ni'in aktivasyon enerji değerleri (Ea) sırasıyla 14.36 kj/mol, 16.85 kj/mol ve 15.93 kj/mol olarak hesaplandı. Liç kinetiğinin yalancı birinci derece homojen kinetik modele uyduğu ve prosesin difüzyon kontrollü olarak gerçekleştiği belirlendi. Proses parametrelerinin bir fonksiyonu olarak prosese ait kinetik eşitlik aşağıdaki şekilde elde edildi. Sonuçlar, hem petrokimya endüstrisinin katı atık yükünün azaltılması hem de EDTA kullanılarak kullanılmış katalizörden metallerin etkin bir şekilde geri kazanımı açısından yeni bir yaklaşım sunmaktadır.
Özet (Çeviri)
In this thesis; the process conditions for the recovery of molybdenum (Mo), nickel (Ni) cobalt (Co) and aluminum (Al) metals from the spent hydrodesulfurization (HDS) catalyst in the presence of complexing agent were investigated. Ethylenediamine tetra acetic acid (EDTA) was used as a complexing reagent in the leaching process due to high ability to bind with metal ions. In the experiments, the roasting pre-treatment was firstly applied to the spent catalyst to convert metals in catalyst structure into more soluble forms. Then, the selective leaching was carried out by precipitating Mo, Ni and Co metals in the forms of ammonium molybdate, nickel dimethylglycoxime and cobalt hydroxide at pH: 2, pH: 6 and pH: 10 respectively. Highest metal extraction yields (90.22% Mo, 96.71% Co, 95.31% Ni and 19.98% Al) were achieved under optimum experiment conditions. According to the thermodynamic data of the process; activation energy values (Ea) of Co, Mo and Ni were calculated as 14.36 kJ/mol, 16.85 kJ/mol and 15.93 kJ/mol, respectively. It was determined that leaching kinetics fit to pseudo-first homogeneous kinetic model and the process was controlled by diffusion. Kinetic equation of the process as a function of the process parameters was obtained as follows. The results provide a new approach in terms of reducing the solid waste load of the petrochemical industry and efficient recovery of metals from the spent HDS catalyst using EDTA.
Benzer Tezler
- Kullanılmış Co-Mo hidrodesülfürizasyon katalizörünün sülfürik asit çözeltilerinde çözünme kinetiğinin incelenmesi
Investigation of dissolution kinetics of spent co-mo hydrodesulfurization catalyst in sulfuric acid solutions
HİLAL AYAN YARDIMCI
Yüksek Lisans
Türkçe
2025
Metalurji Mühendisliğiİstanbul Üniversitesi-CerrahpaşaMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. AHMET ORKUN KALPAKLI
- Kullanılmış kobalt-molibden hidrodesülfürizasyon (HDS) katalizörünün nitrik asitli çözeltilerde çözündürülmesi
Dissolution of used cobalt-molybdenum hydrodesulfurization (HDS) catalyst in nitric acid solutions
İLKNUR ŞUŞOĞLU
Yüksek Lisans
Türkçe
2019
Metalurji Mühendisliğiİstanbul Üniversitesi-CerrahpaşaMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ AHMET ORKUN KALPAKLI
- Kullanılmış Ni-Mo hidrodesülfürizasyon katalizörünün HCl çözeltilerindeki liç kinetiğinin incelenmesi
Investigation of leaching kinetics of spent Ni-Mo hydrodesulfurization catalyst in HCl solutions
BERNA GÜMÜŞ ASLAN
Yüksek Lisans
Türkçe
2022
Metalurji Mühendisliğiİstanbul Üniversitesi-CerrahpaşaMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. SEDAT İLHAN
- Borhidrür bileşiklerinden hidrojen eldesinde kullanılmak üzere manyetik katalizörlerin hazırlanması
Preparation of magnetic catalysts for hydrogen generation from borohydride compounds
HOUSSEM LAKHALI
Doktora
Türkçe
2025
Kimya MühendisliğiKonya Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. AYHAN ABDULLAH CEYHAN
PROF. DR. ÖMER ŞAHİN
- Toz ve metalik formdaki numunelerin temel parametreler yöntemi kullanılarak edxrf spektroskopisi ile kantitatif analizi
Application of fundamental paramaters method in edxrf spectroscopy to the quantitative analysis of some powder and metallic samples
OĞUZ AKDUMAN
Yüksek Lisans
Türkçe
2019
Nükleer MühendislikAnkara ÜniversitesiMedikal Fizik Ana Bilim Dalı
PROF. DR. HALUK YÜCEL