Çelik parçaların elektroliz yöntemi ile nikel ve krom kaplanması
Başlık çevirisi mevcut değil.
- Tez No: 57721
- Danışmanlar: PROF. DR. TEMEL SAVAŞKAN
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Nikel ve krom kaplama, kaplama hızı, kaplama kalitesi. v, Elektroliz, Kaplama, Krom, Nikel, Çelik-metal, Nickel and chromium plating, plating rate, plating quality. VT, Electrolysis, Coating, Chromium, Nickel, Steel-metal
- Yıl: 1995
- Dil: Türkçe
- Üniversite: Karadeniz Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Bu çalışmada, çelik parçalar elektroliz yöntemiyle nikel ve krom kaplanarak, akım yoğunluğu ve banyo sıcaklığının kaplama hızına, kaplama tabakasının yapışma, sertliğine' ve yapışma kalitesine etkileri incelendi. Ayrıca, nikel ve krom kaplanmış numunelerle, hiç kaplanmamış numunelerin korozyon dirençleri karşılaştırıldı. Nikel ve krom kaplama işlemlerinde, kaplama hızının akım yoğunluğu ile doğru orantılı olarak arttığı görüldü. Ayrıca, banyo sıcaklığı ile nikel kaplama hızının doğru orantılı, krom kaplama hızının ise ters orantılı olarak değiştiği belirlendi. Banyo sıcaklığı arttıkça nikel kaplama tabakasının tane boyutunun azaldığı gözlendi. Yüksek akım yoğunluklarında iri taneli nikel kaplama tabakası elde edilirken, akım yoğunluğu düştükçe kaplama tabakasına ait tanelerin inceldiği görüldü. Düşük banyo sıcaklıklarında yapılan krom kaplamalarda mikro çatlakların oluştuğu, banyo sıcaklığı arttıkça çatlak miktarının azaldığı ve yüksek sıcaklıklarda yapılan kaplamalarda ise çatlak meydana gelmediği gözlendi, öte yandan, akım yoğunluğu arttıkça nikel kaplama tabakasının sertliğinin azaldığı, krom kaplama tabakasının serdiğinin ise arttığı görüldü. Banyo sıcaklığı arttıkça, hem nikel hem de krom kaplama tabakasının sertliğinin azaldığı belirlendi. Musluk suyu ve deniz suyu ortamlarında yapılan korozyon deneyleri sonucunda, nikel ve krom kaplamaların çelik parçaların korozyon direncini artırdığı ve krom kaplanmış numunelerin nikel kaplanmış numunelerden daha üstün korozyon direncine sahip olduğu belirlendi.
Özet (Çeviri)
SUMMARY Nickel and Chromium Plating of Steel Parts Using Electrodeposition Technique In this work, the effect of current density and bath temperature on the rate of plating, structure of electrodeposits, adhesion quality and the hardness of deposit were determined for nickel and chromium plating of steel parts. In addition, the corrosion behavior of the electroplated and unplated specimens were compared. Plating speed was found to be proportional to the current density in both nickel and chromium plating. In addition, the rate of nickel plating was found to be proportional, but the rate of chromium plating was found to be inversly proportional to the bath temperature. In nickel plating, the grain size of the deposit found to be decreased with increasing bath temperature. In addition, coarse grain structure of nickel deposit was obtained at high current densities and vice versa. Microcracks were observed in chromium plating at low bath temperatures. Howewer, as the bath temperature increased number of microcracks were decreased and at very high bath temperatures crack-free platings were obtained. As the current density increased the hardness of nickel deposit decreased, but the hardness of chromium deposit increased. It was also observed that, the hardness of both nickel and chromiun deposits was decreased with increasing bath temperature. As a result of corrosion tests carried out in tap water and sea water, it was observed that nickel or chromium plating greatly increased the corrosion resistance of the steel parts, and chromium plated specimens showed higher corrosion resistance than the nickel plated specimens.
Benzer Tezler
- Yüksek nikel alaşımlı malzemelerin vakum ortamında sert lehimlenmesine işlem parametrelerinin özelliklere etkisinin incelenmesi
The Investigation of brazing cycle, overlap distance and joint clearance parameters effect to mechanical properties for high nickel alloys during brazing under vacuum
HASAN KURŞUNGÖZ
Doktora
Türkçe
1996
Makine MühendisliğiEskişehir Osmangazi ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF.DR. ORHAN KOMAÇ
- Boru hatlarında katodik koruma akım ihtiyacının ölçülmesi
Current requirements for cathodic protection of pipe lines
SALİM AGLA
- Disturbance decoupling and disturbance decoupled estimation in regular and decomposed systems
Başlık çevirisi yok
MEHMET KAMİL KÜLMİZ ÇEVİK
Doktora
İngilizce
1990
Elektrik ve Elektronik Mühendisliğiİstanbul Teknik ÜniversitesiPROF.DR. İ. CEM GÖKNAR
- Çinko-alüminyum esaslı“zamak-5”alaşımının elektroliz yoluyla tek ve çok katlı kaplanmasında önemli parametrelerin incelenmesi
Investigation of important parameters in the mono andl multi layer eloctrolytic coating of based zinc-aluminum“zamak-5”alloy
RAMAZAN ÇITAK
Yüksek Lisans
Türkçe
1991
Metalurji MühendisliğiGazi ÜniversitesiMetal Eğitimi Ana Bilim Dalı
DOÇ.DR. RAFET ARIKAN
- Zemin üstü tam elektronik 40 tonluk kamyon kantarı tasarımı
The Project for over floor, electronic truck scale, for 40 tons
ABDULLAH UZUN