Farklı bitim ve suni yaşlandırma işlemlerinin monolitik zirkonyum restorasyonlarının değişik özellikleri üzerine etkisi
The effect of different finishing techniques and thermocycling of monolithic zirconium restorations on different properties
- Tez No: 567352
- Danışmanlar: PROF. DR. ZEYNEP YEŞİL DUYMUŞ, DOÇ. DR. İPEK ÇAĞLAR
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Monolitik zirkonyum, Farklı bitim işlemleri, Suni yaşlandırma, Yüzey pürüzlülüğü, Topografik analiz, Faz değişimi, Bükülme dayanımı, Dental materyaller, Dental restorasyon, Dental stres analizi, Yapay yaşlandırma, Yaşlandırma, Zirkonyum, Monolithic zirconium, Different finishing techniques, Artificial aging, Surface roughness, Topographic analysis, Phase transformation, Flexural strength, Dental materials, Dental restoration, Dental stress analysis, Ageing, Zirconium
- Yıl: 2019
- Dil: Türkçe
- Üniversite: Recep Tayyip Erdoğan Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Bu çalışmanın amacı, monolitik zirkonyum restorasyonlara uygulanan bitim ve suni yaşlandırma işlemlerinin yüzey pürüzlülüğü, topografik özellikler, faz değişimi ve bükülme dayanımına etkisinin incelenmesidir. Materyal ve Metot: Disk şeklinde 100 adet monolitik zirkonyum örnek, presinterize monolitik zirkonyum bloklardan (Ceramill; Amann Girrbach GmbH) sinterleme büzülmesini karşılayacak şekilde hazırlandı. Üretici firmanın talimatları doğrultusunda, 1450 °C'de 7 saat sinterlenme işlemine tabi tutulduktan sonra 15 mm çapında ve 1.2 mm kalınlığında örnekler elde edildi. Örnekler, glaze işlemi uygulandıktan sonra rastgele beş gruba (kontrol, A, AP, AG, APG grupları) ayrıldı. Kontrol grubundaki 20 adet örneğe herhangi bir işlem uygulanmadı. Grup A'daki 20 adet örneğe glaze işleminden sonra mavi bantlı elmas frezlerle aşındırma işlemi, Grup AP'deki örneklere grup A prosedürü sonrası zirkonyum polisaj seti ile polisaj işlemi yapıldı. AG grubundaki 20 adet örneğe aşındırma işlemi yapıldıktan sonra tekrar glaze işlemi uygulandı. Geriye kalan 20 adet örneğe (Grup APG) Grup AP prosedürü sonrası glaze işlemi uygulandı. Tüm gruplar iki alt gruba (n=10) ayrıldı. Bir gruptaki örnekler distile suda bekletilirken diğer alt gruptaki örneklere 5 ile 55 °C sıcaklık aralığında 5000 suni yaşlandırma ile hızlandırılmış yaşlandırma işlemi uygulandı. Tüm örnekler profilometre ile incelendi. Topografik değişimleri değerlendirmek için her gruptan birer adet örneğin Taramalı Elektron Mikroskobu (SEM) ile görüntüleri alındı ve Enerji Dağılımlı X Işını Spektroskopisi (EDS) testi yapıldı. Örneklerin faz değişim analizleri X-Ray Difraktometre (XRD) ile değerlendirildi. Örneklerin bükülme dayanımının değerlendirilmesi için Universal Test Cihazında üç top üzerinde bükülme dayanım testi uygulandı. Elde edilen veriler varyans analizi ve Tukey çoklu karşılaştırma testi ile istatistiksel olarak değerlendirildi (p<0.05). Bulgular: Aşındırma işlemi uygulanan örneklerin yüzey pürüzlülük ve bükülme dayanımının diğer gruplardan anlamlı derecede yüksek (p<0.05) olduğu, polisaj ve glaze grupları arasındaki farkın anlamlı olmadığı (p>0.05) saptandı. XRD analizinde; uygulanan yüzey ve ısıl işlemlerin göreceli monoklinik faz miktarına etkisinin olduğu ancak elde edilen farkların istatistiksel olarak anlamlı olmadığı görüldü (p>0.05). Sonuç: Bu çalışmada polisaj işlemleri uygulanan örneklerin glaze işlemleri uygulanan örneklerden daha iyi mekanik özellikler sergilediği tespit edildiğinden, monolitik zirkonyum restorasyonların bitim işlemlerinde yeterli bir şekilde polisaj uygulanmasının glaze işlemi yerine tercih edilebileceği kanaatine varıldı.
Özet (Çeviri)
Aim : The aim of this study was to evaluate the effect of different finishing procedures and artificial aging of monolithic zirconium restorations on the surface roughness, topographic properties, phase transformation and flexural strength. Material and Methods: 100 disc-shaped monolithic zirconium specimens were cut from presintered zirconium blanks (Ceramill; Amann Girrbach GmbH) which were oversized to compensate for sintering shrinkage. After sintering for 7 hours at 1450 °C according to the manufacturer's instruction, specimens of 15 mm diameter and 1.2 mm thickness were obtained. Glaze was applied to all specimens and randomly divided into 5 groups (control, A, AP, AG, APG groups). In the control group, no other procedure was applied to the 20 specimens. 20 specimens surfaces in the group A were ground with blue band diamond rotary instruments after glaze treatment. In the group AP, specimens were polished with zirconium polishing kit after group A. 20 specimens in the group AG were glazed again after group A procedures. The remaining 20 specimens (group APG) were treated with glaze after Group AP procedure. All groups were divided into 2 subgroups (n = 10). Specimens in one group were kept in distilled water while the specimens in the other subgroup were thermocycled for 5000 cycles, with a temperature range of 5 to 55 °C. To evaluate the topographic changes, one specimen of each group was subjected to scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS) test. Additionally, all specimens were measured with profilometer. Phase changes were assessed with X-ray diffraction (XRD). The biaxial flexural strength was determined by using a piston-on-3- balls technique in a Universal Testing Machine. Statistical analysis was performed by using variance analysis and Tukey multiple comparison test (p <0.05). Results: It was found that surface roughness and flexural strength were significantly higher in grinding group than other groups (p <0.05) and no significant difference was found between polished and glazed groups (p>0.05). In XRD analysis; it was observed that the applied surface and heat treatments had an effect on the relative monoclinical phase amount but the differences were not statistically significant (p> 0.05). Conclusions: In our study, it was determined that the polished specimens exhibited better mechanical properties than glazed specimens. For this reason, we think that an adequate polishing application can be preferred instead of glaze treatment in monolithic zirconium restorations.
Benzer Tezler
- Farklı bitirme işlemleri uygulanan CAD/CAM seramiklerin termal yaşlandırma sonrası renk stabilitelerinin değerlendirilmesi
The evaluation of the color stability of CAD / CAM ceramics after different finishing procedures and thermal aging
FUNDA SOYSAL
Diş Hekimliği Uzmanlık
Türkçe
2019
Diş HekimliğiGaziantep ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ NERMİN DEMİRKOL
- Akışla şekillendirme uygulanmış AA7075 kalite alüminyum alaşımının mekanik ve korozyon özelliklerine retrogresyon ve yeniden yaşlandırma işleminin etkisi
The effect of retrogression and reaging heat treatment on the mechanical and corrosion properties of a flow formed AA7075 aluminum alloy
EDA URAL
Yüksek Lisans
Türkçe
2024
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. MURAT BAYDOĞAN
- The effect of post weld heat treatment on the mechanical properties of TIG welded inconel 718 alloy
Kaynak sonrası ısıl işlemin TIG ile kaynak yapılmış inconel 718 alaşımının mekanik özelliklerine etkisi
ECE CANAN KOŞMAZ
Yüksek Lisans
İngilizce
2015
Bilim ve Teknolojiİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU
- Alaşımlı Al tozundan toz metalurjisi yöntemi ile malzeme üretimi ve yaşlandırma tavrının irdelenmesi
Production of alloy from pre-mixed powders by powder metallurgy technique and investigation of it's ageing behaviour
MEHMET ÇELİK
Yüksek Lisans
Türkçe
2003
Metalurji MühendisliğiGazi ÜniversitesiMetal Eğitimi Ana Bilim Dalı
PROF. DR. MEHMET TÜRKER
- Alümina takviyeli alüminyum matrisli sintaktik köpük malzemenin üretim karakterizasyonu ve mekanik özelliklerinin incelenmesi
The mechanical analysis and production properties of aluminium matrix syntactic foams with alumina particles
CEM BEKAR
Yüksek Lisans
Türkçe
2019
Makine Mühendisliğiİstanbul Teknik ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
DOÇ. DR. ALİ GÖKŞENLİ