İki farklı tip peek materyalinin kompozitle bağlanma dayanımının değerlendirilmesi
Evaluation of bond strength Two different peek and indirect composite resin materials
- Tez No: 552642
- Danışmanlar: DOÇ. DR. SERKAN SARIDAĞ
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Dental bonding, Dental materyaller, Dental stres analizi, Kompozit malzemeler, Kompozit reçineler, Kumlama, Polietereterketon, Yüzey pürüzlülüğü, Dental bonding, Dental materials, Dental stress analysis, Composite materials, Composite resins, Sanding, Polyetheretherketone, Surface roughness
- Yıl: 2019
- Dil: Türkçe
- Üniversite: Kocaeli Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tez çalışmasının amacı, farklı yüzey pürüzlendirme yöntemleri ve adeziv sistemlerin iki farklı tip polietereterketon (PEEK) ile indirekt kompozit rezin materyalin makaslama bağlanma dayanımı üzerindeki etkilerinin incelenmesidir. Çalışmada doldurucusuz saf PEEK (Juvora) ve %20 nano-seramik doldurucu içeren PEEK (BioHPP) bloklardan her biri 160 adet olacak şekilde (toplam=320) 8×8×4 mm boyutlarında dikdörtgen örnekler hazırlandı. Örnekler 25 N basınçta otomatik cila makinesinde 10 sn. cilalandıktan sonra her biri kırk numuneden oluşan dört yüzey işlem grubuna (kontrol grubu, alüminyum oksit kumlama, piranha çözeltisi ile aşındırma, kumlama+piranha asitle aşındırma) rastgele olarak ayrıldı (n=40/grup). Tüm numunelerin yüzey pürüzlülüğü profilometre ile ölçüldükten sonra yüzey topografyası taramalı elektron mikroskobu ile incelendi. Daha sonra tüm gruplara iki farklı tip adeziv (Visio.Link ve Single Bond Universal) uygulandı (n=20/grup). Adeziv uygulanan gruplara iki farklı tip kompozit materyali (Crea.Lign ve SR Nexco) uygulandı (n=10/grup). Örnekler 24 saat boyunca 37°C'de damıtılmış su içinde bekletildikten sonra universal test cihazında 0,5 mm/dk hızla makaslama testine tabi tutuldu. Elde edilen veriler tek yönlü ANOVA, Kruskal-Wallis, Mann-Whitney ve Bonferroni çoklu karşılaştırma testleri kullanılarak istatistiksel olarak analiz edildi (p<0,05). Piranha asitle işlenmiş PEEK örneklerin yüzey pürüzlülüğü (3,46±0,75) diğer gruplara kıyasla anlamlı derecede yüksek bulundu (p<0,01). Bağlanma dayanımı ile yüzey pürüzlülük değerleri arasında %87,2 düzeyinde pozitif yönlü istatistiksel olarak anlamlı bir korelasyon bulundu (r:0,870; p<0,01). Visio.Link uygulanan örnekler Single Bond Universal uygulananlara oranla daha yüksek bağlanma değerleri gösterirken SR Nexco uygulanmış örnekler Crea.Lign uygulanmış örneklerden anlamlı olarak daha yüksek bağlanma değerleri göstermiştir (p<0,01).
Özet (Çeviri)
The aim of this study is to evaluate the influence of different surface treatment methods and adhesives on the shear bond strength of two different type indirect composite resin material and polyetheretherketone (PEEK). This study one type of unfilled PEEK (Juvora) and %20 nano-ceramic filled PEEK (BioHPP) compounds each were prepared 160 (total =320) rectangular specimens (8×8×4 mm). After the samples were polished for 10 seconds at 25 N pressure on automatic polishing machine, they were randomly separated into four surface treatment groups each consisting of forty samples (n= 40/group); (control group, air abrasion, etching with piranha solution, air abrasion and piranha acid etching). After measuring the surface roughness of all specimens with a profilometer, surface topography was examined by scanning electron microscope. Each group were divided into two primer subgroups Visio.Link and Single Bond Universal (n=20/group). Half of each group was veneered with Crea.Lign the other half with SR Nexco (n=10/group). The specimens were stored in distilled water at 37oC for 24 hours and and loaded in a universal testing device for shear bond stress with at a crosshead speed of 0,5 mm/min. Data were analyzed by one-way ANOVA, Kruskal-Wallis and Mann-Whitney and Bonferroni multiple comparison tests (p<0,05). PEEK specimens etched with piranha acid resulted in higher surface roughness (3,46±0,75) significantly higher than the other groups. PEEK specimens statistically significant correlation was found between the bond strength and surface roughness values at %87 (r:0,870; p<0,01). Visio.Link conditioned specimens showed higher SBS values than those treated with Single Bond Universal, whereas PEEK veneered with SR Nexco showed significantly higher SBS values than those veneered with Crea.Lign (p<0,01).
Benzer Tezler
- PEEK ve PEKK materyallerinin çeşitli lazerlerle yüzey özelliklerinin değiştirilmesinin kompozit ile bağlantı dayanımına etkisinin incelenmesi
Başlık çevirisi yok
BURCU AŞIK
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiBezm-İ Alem Vakıf ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. ÖZGÜN YUSUF ÖZYILMAZ
- Buğdayda farklı melezleme teknikleri kullanarak tohum tutma oranının saptanılması
Başlık çevirisi yok
İSMAİL TÜZÜN
Yüksek Lisans
Türkçe
1986
ZiraatUludağ ÜniversitesiTarla Bitkileri Ana Bilim Dalı
PROF. DR. HALİS RUHİ EKİNGEN
- İzmir'de bazı yolların kapatılarak yaya bölgeleri oluşturma da kent peyzajını geliştirme açısından yeniden planlanması üzerinde araştırmalar
Başlık çevirisi yok
BAHAR TÜRKYILMAZ
Yüksek Lisans
Türkçe
1985
Şehircilik ve Bölge PlanlamaEge ÜniversitesiŞehir ve Bölge Planlama Ana Bilim Dalı
- Bazı esterlerin kinetik incelenmesi ve termodinamik parametrelerin belirlenmesi
Kinetic study and detesmination of thermodnamic parameters of some esters
İBRAHİM TAŞ
Yüksek Lisans
Türkçe
1986
Kimya MühendisliğiUludağ ÜniversitesiKimya Ana Bilim Dalı
PROF. DR. MUSTAFA CEBE
- Çoklu amaçların çözümlemesinde amaç programlaması ile genelleştirilmiş ters yaklaşımı ve yem sanayiinde bir uygulama
Goal programming and generalieed inverse approaches in the multi-objective analysis and application in feed industry
HASAN BAL