Amorphous to crystalline transition of selenium thin films deposited onto aluminum substrates
Başlık çevirisi mevcut değil.
- Tez No: 5387
- Danışmanlar: DOÇ. DR. A. MACİT ÖZENBAŞ
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Kristalleşme, selenyum, ince film. -vı, Crystallization, selenium, thin film..iv
- Yıl: 1989
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Belirtilmemiş.
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ALOMÎNYUM ALTLIKLAR ÖZERİNE KAPLANAN SELENYUM İNCE FİLMLERİN AMORF-KRİSTAL DÜNOŞOMO PINARLI, H. Coşkun Mühendislik Fakültesi Metalürji Mühendisliği Bölümü, Y. Lisans Tezi Tez Yöneticisi: Doç. Dr. AiMacit ÖZENBAS 96 Sayfa, Şubat 1989 ÖZET Bu çalışmada, mekanik olarak, parlatılmış alüminyum altlıkla rın üzerine vakumda kaplanan a-Se filmlerin kristalleşmesi incelen- -5 mistir. Kaplama işlemi sırasındaki vakum basıncı <10 torr ve alt lık sıcaklığı 20°C olarak uygulanmıştır. Değişik tavlama sürelerinde ve 70°C-85°C arasındaki sıcaklıklarda amorf-kristal dönüşümü gözlen miştir. Oluşan kristallerin büyüme hızı ve yapıları Tarama Elektron Mikroskobu yardımıyla saptanmıştır. X-ışınları ve Transmisyon Elek tron Mikroskobu altındaki incelemeler bu kristallerin hexagonal yapı da olduğunu göstermiştir. o Bu çalışmada kaplanan a-Se filmlerin kalınlıkları 6250 A, o o 9250 A ve 18400 A'dür. Film kalınlıklarının, tavlama süre ve sıcak-lıklarıyla birlikte kristallerin büyüme hızım etkiledikleri görül müştür. Tavlamayı izleyen kristalleşme altlık-film ara-yüzeyinde başlamış ve dış yüzeye doğru ilerlemiştir. Kristal yarıçaplarının tavlama süresindeki artışla doğru orantılı olarak arttığı gözlen miştir. Kristalleşme için gerekli aktivasyon enerjileri» kristal büyüme hızı ile tavlama sıcaklıkları arasında Arrhenius tipi bir bağıntı olduğu varsayımına dayanarak hesaplanmıştır. Aktivasyon enerjilerinin film kalınlığına bağlı olarak arttığı anlaşılmıştır. Alınan sonuçlar daha önceki çalışmalar ile uyum göstermektedir.
Özet (Çeviri)
AMORPHOUS TO CRYSTALLINE TRANSITION OF SELENIUM THIN FILMS DEPOSITED ONTO ALUMINUM SUBSTRATES PINARLI, H. Coşkun Faculty of Engineering Department of Metallurgical Engineering, M.S. Thesis Supervisor: Assoc. Prof. Dr. A.Macit ÜZENBAŞ 96 Pages, February 1989 ABSTRACT In this work the crystallization behaviour of a-Se thin films prepared by vacuum deposition onto mechanically polished aluminum substrates was examined. The vacuum. pressure during deposition and -5 o the substrate-temperature were <10 torr and 20 C, respectively. The amorphous-to-crystalline transition was observed between 70°C- 85 C at different annealing times. Crystal growth rates and morphology of the crystals formed have been obtained by virtue of SEM observations. X-ray and TEM analyses revealed that these crystals were of hexagonal structure. The thicknesses of the deposited a-Se films studied in this on ° work were, 6250 A, 9250 A» and 18400 A. The thicknesses of the films ?111'were found to be an important property, as to affect the growth rates of the crystallites, in correlation with the annealing temperatures and times. Upon annealing, crystallization started at the substrate- film interface and proceeded towards the free surface. The radii of the crystallites were found to be increasing linearly with the increase in annealing time. The activation energies for crystallization, calculated under the presumption of the existence of an Arrhenius type of relation between crystallite growth rate and annealing temperature, were found to be increasing with increases in the thickness of the films. The results of this study are in good agreement with those of the previous ones.
Benzer Tezler
- Eritme-Döküm yöntemiyle üretilmiş Bi1-6 Pb0.4 Sr 2 Ca3 Cu4 012 (2234) süperiletkenin yapısal ve fiziksel özelliklerinin incelenmesi
Başlık çevirisi yok
TAYFUR KÜÇÜKÖMEROĞLU
Yüksek Lisans
Türkçe
1994
Fizik ve Fizik MühendisliğiKaradeniz Teknik ÜniversitesiFizik Ana Bilim Dalı
YRD. DOÇ. DR. EKREM YANMAZ
- Sıvı kristal blok ve graft kopoliner sentezinde yeni yöntemler
New synthetic approaches for the synthesis of liquid crystalline block and graft copolymers
YEŞİM HEPUZER
- Li2O - ZnO - Al2O3 camlarının kontrollü kristalizasyonu ve cam seramiklerin karakterizasyonu
The Controlled crystallization of Li2O - ZnO - Al2O3 - SiO2 glasses and the characterization of glass ceramics
ENGİN MAYTALMAN
Yüksek Lisans
Türkçe
1999
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
DOÇ. DR. ERDEM DEMİRKESEN
- Alümina ilavesinin Li2O-ZnOSi2 cam ve cam seramiklerinin kristalizasyon davranışı, mekaniksel ve kimyasal özellikleri üzerine etkisi
Başlık çevirisi yok
ELVAN BİLGE ÇUKUR
- Volkanik bazalt kayaçlarından cam-seramik malzeme üretim koşullarının araştırılması ve özelliklerinin incelenmesi
The investigation of production conditions and properties of glass-ceramic materials from the volcanic basalt rocks
ŞENOL YILMAZ
Doktora
Türkçe
1997
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
DOÇ. DR. VOLKAN GÜNAY