Farklı kalınlıklardaki CAD/CAM seramiklerin rezin siman polimerizasyonuna olan etkisi
The effect of CAD/CAM ceramics of different thickness on resin cement polymerization
- Tez No: 538003
- Danışmanlar: PROF. DR. MÜNİR TOLGA YÜCEL
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: DönüĢüm derecesi, FTIR, rezin siman, tam seramik, Akrilik reçineler, CAD/CAM, Cam seramikler, Dental porselen, Dental çimentolar, Kompozit reçineler, Kızılötesi spektroskopi, Polimerleşme, All ceramic, degree of conversion, FTIR, resin cement, Acrylic resins, CAD/CAM, Glass ceramics, Dental porcelain, Dental cements, Composite resins, Infrared spectroscopy, Polymerization
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Selçuk Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmanın amacı, farklı kalınlıklardaki CAD/CAM seramik kesitlerinin iki farklı rezin simanın polimerizasyonuna olan etkisini değerlendirmektir. Üç farklı CAD/CAM ile işlenebilen tam seramik restorasyon materyali (IPS Empress, Vita Enamic, Vita Suprinity), dört farklı kalınlığa sahip olacak şekilde (0.5, 1, 1.5, 2 mm) düşük hızlı hassas kesme cihazında kesildi. Her seramik kesiti altında gerçekleştirilen polimerizasyon ile ışık ile polimerize olan rezin siman ve hem kimyasal hem de ışık ile polimerize olan rezin simandan toplam 240 örnek hazırlandı ve 24 saat boyunca 37 °C'de ışık almayacak şekilde saklandı. Tüm örnekler, dönüşüm derecelerinin belirlenebilmesi amacıyla FTIR analizi ile test edilerek 1608 ve 1637 cm-1 dalga boylarındaki absorbsiyon miktarları kaydedildi. Her iki rezin siman türünden 10 örnek polimerizasyon öncesi ve sonrası FTIR analiziyle incelendi ve kontrol grubu olarak görev gördü. Elde edilen veriler yardımıyla rezin siman örneklerin dönüşüm dereceleri (%) hesaplandı. Veriler tek yönlü ANOVA, bağımsız t testi ve Tukey testleri ile analiz edildi (p<0.05). Her iki rezin siman türünde de en yüksek dönüşüm derecesi değerleri kontrol grubunda görülürken en düşük değerler 2 mm kalınlığındaki Vita Enamic kesiti altındaki örneklerde saptanmıştır (p<0.05). Tüm seramik kesitlerin 0.5 ve 1 mm kalınlıkları altında gerçekleştirilen polimerizasyon diğer kalınlıklara göre istatistiksel olarak daha yüksek değerler ortaya çıkmasını sağlamıştır (p<0.05). Aynı seramik kesitler altında polimerizasyonu gerçekleştirilen ışık ile polimerize olan rezin siman ve hem kimyasal hem de ışık ile polimerize olan rezin simanın dönüşüm dereceleri karşılaştırıldığında hem kimyasal hem de ışık ile polimerize olan rezin simanda daha yüksek değerler elde edilmiştir. Işık ile polimerize olan rezin simanın aynı kalınlıktaki seramik kesitlerin altındaki dönüşüm derecesi incelendiğinde 0.5 ve 1 mm kalınlığa sahip IPS Empress kesitler aynı kalınlıktaki diğer seramiklere göre istatistiksel olarak daha yüksek değerler ortaya koymuştur (p<0.05). Aynı kalınlıkların hem kimyasal hem de ışık ile polimerize olan rezin simanın dönüşüm derecesine olan etkileri incelendiğinde ise IPS Empress ile Vita Enamic arasında belirgin bir fark gözlemlenmiştir (p<0.05). 1.5 ve 2 mm kalınlığa sahip kesitlerde ise iki rezin siman türünde de seramikler arasında herhangi bir fark bulunmamıştır (p>0.05)
Özet (Çeviri)
The aim of this study was to evaluate the effect of different thicknesses of CAD / CAM ceramic sections on the polymerization of two different resin cements. Three CAD/CAM all-ceramic restorative materials (IPS Empress, Vita Enamic, Vita Suprinity) were sectioned using a low speed diamond saw with four different thicknesses (0.5, 1, 1.5, 2 mm). A total of 240 resin cement specimens were prepared from light cured and dual cure resin cements by means of polymerization under each ceramic section and were stored for 24 hours at 37 ° C. Absorbtion peaks were recorded at 1608 and 1637 cm-1 by testing with FTIR analysis to determine the degree of conversion of all samples. 10 samples of each resin cement type were examined by FTIR analysis before and after polymerization and served as the control group. Data were analyzed using one way ANOVA, independent t and Tukey HSD tests (p<0.05). For both resin cement types, the control group showed the highest degree of conversion values while samples cured under Vita Enamic section with a thickness of 2 mm presented the lowest values (p<0.05). Polymerization performed under 0.5 and 1 mm thicknesses of all ceramic sections provided statistically higher values than other thicknesses (p<0.05). Dual cure resin cement samples cured under the same ceramic sections showed higher degree of conversion values compared to light cured resin cement samples. When the degree of conversion of light cured resin cement samples cured under the same ceramic thicknesses were examined, IPS Empress sections with 0.5 and 1 mm thickness exhibited statistically higher values than other ceramics of the same thickness (p<0.05). When the effects of the same thicknesses on the degree of conversion of dual cure resin cement samples were examined, a significant difference between IPS Empress and Vita Enamic was observed (p<0.05). There was no difference for both resin cement types for sections of 1.5 and 2 mm (p>0.05).
Benzer Tezler
- Farklı kalınlıklardaki CAD/CAM seramiklerin dual-cure ve light-cure rezin siman polimerizasyonlarına etkisi
Effect of CAD/CAM ceramics of different thicknesses on dual-cure and light-cure resin cement polymerizations
BURHAN ARSLAN
Doktora
Türkçe
2023
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. TUBA YILMAZ SAVAŞ
- Zirkonya ile güçlendirilmiş lityum silikat cam seramik kalınlığının ışıkla polimerize rezin simanın polimerizasyon dönüşüm derecesine etkisinin değerlendirilmesi
Evaluating the effect of zirconia reinforced lithium silicate glass ceramic thickness on the degree of conversion of LIGHT-cured resin cement
GÜLEN DAL
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiKütahya Sağlık Bilimleri ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ BANU ÇUKURLUÖZ BAYINDIR
- Farklı tip ve kalınlıklardaki monolitik zirkonya seramiklerin rezin simanların polimerizasyon ve mikrosertliğine etkisi
Effect of the different type and thickness of monolithic zirconia ceramics on the resin cement polymerization and microhardness
İPEK BALEVİ AKKESE
Doktora
Türkçe
2022
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DR. ÖĞR. ÜYESİ TUBA YILMAZ SAVAŞ
- Buğdayda farklı melezleme teknikleri kullanarak tohum tutma oranının saptanılması
Başlık çevirisi yok
İSMAİL TÜZÜN
Yüksek Lisans
Türkçe
1986
ZiraatUludağ ÜniversitesiTarla Bitkileri Ana Bilim Dalı
PROF. DR. HALİS RUHİ EKİNGEN
- İzmir'de bazı yolların kapatılarak yaya bölgeleri oluşturma da kent peyzajını geliştirme açısından yeniden planlanması üzerinde araştırmalar
Başlık çevirisi yok
BAHAR TÜRKYILMAZ
Yüksek Lisans
Türkçe
1985
Şehircilik ve Bölge PlanlamaEge ÜniversitesiŞehir ve Bölge Planlama Ana Bilim Dalı