Application of salt spray testing to the evaluation of corrosion performance of organic coatings
Boyaların korozyon direncinin belirlenmesinde tuz püskürtme testinin uygulanması
- Tez No: 5354
- Danışmanlar: PROF. DR. MUSTAFA DORUK
- Tez Türü: Yüksek Lisans
- Konular: Metalurji Mühendisliği, Metallurgical Engineering
- Anahtar Kelimeler: Tuz püskürtme deneyi, organik kaplamalar, boyalar, boya testleri. iv, Boya testleri, Endüstriyel boyalar, Tuz püskürtme testi, Salt spray test, organic coatings, paint tests, paints. iii, Industrial dyes, Organic coating, Salt spraying test
- Yıl: 1989
- Dil: İngilizce
- Üniversite: Orta Doğu Teknik Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Belirtilmemiş.
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
BOYALARIN KOROZYON DİRENCİNİN BELİRLENMESİNDE TÜZ PÜSKÜRTME TESTİNİN UYGULANMASI Yağmur Suat. Mühendislik Fakültesi Metalürji Mühendisliği Bolümü, Yüksek Lisans Tezi Tez Yöneticisi : Prof. Dr. Mustafa Doruk 106 Sayfa, Şubat 1989 ÖZET Bu -tez çalismasinda, çeşitli endüstriyel boyalarin korozyon davranişlari tuz püskürtme testi ile belirlendi. Deneylerde çeşitli endüstriyel kaynaklardan sağlanan 18 farkli boya kullanildi. Numuneler 30 gün boyunca sürekli olarak % 5'lik tuz çözeltisi kullanilarak -test edildi. Tüm deneyler ODTÜ Metalürji Mühendisliği Bölümünde geliştirilen tuz püskürtme testi sistemi kullanilarak gerçekleştirildi. ı Deney süresi sonunda numunelere 4 standard boya testi uygulanarak sürekli tuz sisine karşi dirençli boyalar belirlendi.
Özet (Çeviri)
APPLICATION OF SALT SPRAY TESTING TO THE EVALUATION OF CORROSION PERFORMANCE OF ORGANIC COATINGS Yağmur Suat Faculty of Engineering Department of Metallurgical Engineering, M.S. Thesis Supervisor : Prof. Dr. Mustafa Doruk 106 Pages, February 1989 ABSTRACT In this thesis, the corrosion characteristics of various types of industrial paints were determined by salt spray test. 18 different types of industrial paints supplied from industrial companies were used in the experiments. The specimens were tested for a period of 30 days using a 5 % salt water solution. All the experiments were carried out using the salt spray test system developed in Metallurgical Engineering Department at METU. After exposure period, 4 standard paint tests were applied to the specimens, and the paints resistant to continuous salt spray were determined.
Benzer Tezler
- Galvenizli çelik saçların ark kaynaklı bağlantılarının mekanik ve korozyon davranışlarının incelenmesi
Investigation of mechenical and corrosion behaviour of arc welded joints on galvanized steel sheets
C. BURAK ÖREN
Yüksek Lisans
Türkçe
1999
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMetalurji Mühendisliği Ana Bilim Dalı
PROF. DR. KUTSAL TÜLBENTÇİ
- Yapraklara püskürtülen Ca formlarının tuz stresinde yetiştirilen biber bitkisi (capsicum annuum L. ) 'nin gelişmesi, mineral bileşimi ve membran geçirgenliğine etkisi
The Effects of foliar sprayed Ca forms on the growth, mineral composition and membrane integrity of pepper (capsicum annuum L.) plants grown under salinity stress
AYŞE KUZAL