Termik santral ve metalurjik tesis artıklarından yapay zeolit ve geopolimer malzemelerin eldesi
Production of synthetic zeolite and geopolymer materials from the tailings derived from thermal power plants and metallurgical plants
- Tez No: 534829
- Danışmanlar: PROF. DR. HÜSEYİN VAPUR, DR. ÖĞR. ÜYESİ MİNE TAYKURT DADAY
- Tez Türü: Doktora
- Konular: Polimer Bilim ve Teknolojisi, Maden Mühendisliği ve Madencilik, Kimya Mühendisliği, Polymer Science and Technology, Mining Engineering and Mining, Chemical Engineering
- Anahtar Kelimeler: Atık beton, Jeosentetik malzemeler, Karışık malzeme, Kompozit malzemeler, Kompozit polimerler, Polimer beton, Yüksek dayanımlı beton, Waste concrete, Geosynthetical materials, Mixed material, Composite materials, Composite polymers, Polymer concrete, High strength concrete
- Yıl: 2019
- Dil: Türkçe
- Üniversite: Çukurova Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Maden Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışma termik santral ve metalurjik tesis artıklarından yapay zeolit ve geopolimer malzemelerin üretim olanaklarının araştırılması şeklinde 2 bölümden oluşmaktadır. Geopolimer yapı malzemelerinin üretiminde bazik aktivatör olarak sodyum hidroksit (NaOH) ve sodyum metasilikat (Na2SiO3) kullanılmıştır. Yates test tekniği ve Box Behnken deney dizaynı etkin parametreleri belirlemek için uygulanmıştır. Bazik ve asidik pomzalar ile kalsine perlit agregalar kullanılarak 11,69 ila 51,87 MPa tek eksenli basınç dayanımlarına sahip hafif (1263-1792 kg/m3) geopolimer betonlar elde edilebilmiştir. Ark fırın ve ferrokrom cürufları agrega olarak kullanıldığında daha yüksek dayanımlarda daha çok agrega içeren daha yüksek dayanım ve ağırlıklarda geopolimer betonlar elde edilmiştir. Beton örneklerin nokta yük dayanımları da belirlenmiştir. 28. günde beton örneklerin su emme, sonik hız ve Mohs sertlik değerleri saptanmıştır. Zeolit sentezi deneylerinde NaOH kullanılmıştır. Uçucu küllerden hidrotermal bazik liç işlemi ile yüksek katyon değiştirme kapasitesine (KDK) sahip Gismondin grubu zeolitler (zeolit Na-P1, Gismondin ve Garronit) elde edilirken, bazik füzyon tekniği uygulandığında Na-LSX ve Ca-Filipsit türü zeolitler üretilebilmiştir. Liç işlemi öncesi yüksek alan şiddetli yaş manyetik ayırma işlemi uygulanmış ve manyetik olmayan fraksiyon zeolit sentezlenmek üzere kullanılmıştır. Zeolitler XRD, XRF, SEM, EDS, DTA-TGA-DSC, M-H ve FTIR teknikleri kullanılarak karakterize edilmiş ve sonuçlar yorumlanmıştır.
Özet (Çeviri)
This study consists of 2 chapters to investigate the production possibilities of artificial zeolite and geopolymer materials from the thermal power plant and metallurgical plant tailings. Sodium hydroxide (NaOH) and sodium metasilicate (Na2SiO3) were used as basic activators in the production of geopolymer building materials. Yates and Box Behnken test design were used to determine the effective parameters. Using basic/acidic pumice and calcined perlite aggregates, lightweight (1263-1792 kg/m3) geopolymer concretes with uniaxial compressive strengths of 11,69 to 51,87 MPa could be obtained. Much more aggregate containing geopolymer concretes with higher strengths and weights were obtained when arc furnace and ferrochrome slag aggregates were used. In addition, point load strengths were determined. Water absorption, sonic velocity and Mohs hardness values of specimens were determined on the 28th day. NaOH was used in the zeolite synthesis experiments. Gismondine group zeolites (zeolite Na-P1, Gismondine and Garronite) with high cation exchange capacity (CEC) were obtained by hydrothermal alkali leaching. Na-LSX and Ca-Filipsite type zeolites were produced by basic fusion technique. Before the alkali leaching process, high intensity magnetic separation was applied and the non-magnetic materials were used to synthesize the zeolites. Zeolites were characterized and interpreted using XRD, XRF, SEM, EDS, DTA-TGA-DSC, M-H and FTIR techniques.
Benzer Tezler
- Spatial distribution of emissions from industrial and residential heating systems using geographical information systems for Turkey
Türkiye için endüstriyel ve konut ısınma kaynaklı emisyonların coğrafi bilgi sistemi ile mekansal dağılımı
GÖKÇE DURUKAN
Yüksek Lisans
İngilizce
2014
Çevre Mühendisliğiİstanbul Teknik ÜniversitesiÇevre Mühendisliği Ana Bilim Dalı
PROF. DR. KADİR ALP
- Compilation of an industrial emission inventory for Turkey
Türkiye için endüstriyel emisyon envanteri oluşturulması
ÜMMÜGÜLSÜM ALYÜZ
Yüksek Lisans
İngilizce
2012
Çevre Mühendisliğiİstanbul Teknik ÜniversitesiÇevre Mühendisliği Ana Bilim Dalı
PROF. DR. KADİR ALP
- Design of a high temperature erosion apparatus for testing of boiler tubes
Termik santral kazan borularının testi için bir yüksek sıcaklık aşınma testi düzeneği tasarımı
HÜSEYİN ERGÜN
Yüksek Lisans
İngilizce
2010
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Bölümü
PROF. DR. MUSTAFA DORUK
PROF. DR. TAYFUR ÖZTÜRK
- SA 387 grade 91 malzemenin çok pasolu alın kaynağında farklı ön ısı sıcaklıklarının kalıntı gerilmelere ve mekanik özelliklere etkisinin deneysel incelenmesi
Experimental investigation of the effects of various preheat temperatures on residual stresses and mechanical properties in multi-pass butt welding of SA 387 grade 91 material
CİHAN ÇELİK
Yüksek Lisans
Türkçe
2023
Metalurji MühendisliğiDokuz Eylül ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ BAHADIR UYULGAN
- Termik santrallerin döner tip hava ısıtıcılarında kullanılan ısı değiştirici plakalar için emaye kaplama optimizasyonu
Optimization of enamel coatings on heat exchanger plates used in rotary air preheaters of thermal power plants
ERDEM GÜNGÖR
Yüksek Lisans
Türkçe
2015
Metalurji Mühendisliğiİstanbul Teknik ÜniversitesiMalzeme Bilimi ve Mühendisliği Ana Bilim Dalı
PROF. DR. HÜSEYİN ÇİMENOĞLU
DOÇ. DR. ERDEM ATAR