Düşükkarbonlu çeliğin sodyum klorürlü ortamlarda çukur oluşma ve kritik çukur oluşma potansiyellerinin potansiyostatik yöntemle belirlenmesi

The Determination of the values of breakdown and protection potentials of plain carbon steel in sodium chloride media by potentiostatic method

  1. Tez No: 5312
  2. Yazar: AHMET YAŞAR TURAN
  3. Danışmanlar: YRD. DOÇ. DR. MÜBECCEL ERGUN
  4. Tez Türü: Yüksek Lisans
  5. Konular: Kimya Mühendisliği, Chemical Engineering
  6. Anahtar Kelimeler: Belirtilmemiş.
  7. Yıl: 1988
  8. Dil: Türkçe
  9. Üniversite: Gazi Üniversitesi
  10. Enstitü: Fen Bilimleri Enstitüsü
  11. Ana Bilim Dalı: Kimya Mühendisliği Ana Bilim Dalı
  12. Bilim Dalı: Belirtilmemiş.
  13. Sayfa Sayısı: Belirtilmemiş.

Özet

DÜŞÜK KARBONLU ÇELÎ?ÎN SODYUM KLORÜRLÜ ORTAMLARDA ÇUKUR OLUŞMA VE KRÎTÎK ÇUKUR OLUŞMA POTANSİYELLERİNİN POTANSÎYOSTATİK YÖNTEMLE BELİRLENMESİ (Yüksek Lisans Tezi) Ahmet Yaşar TURAN GAZİ ÜNİVERSİTESİ FEN BİLİMLERİ ENSTİTÜSÜ Ekim 1988 OZ Çukur oluşma (E ) ve kritik çukur oluşma (E, ) ço JCÇO potansiyelleri, çukur korozyonunun tanımlanmasında çok önemlidir. Bu çalışmanın ilk bölümünde bu değerler, dü şük karbonlu çelikler için (Fe 99,30; C 0,10; Mn 0,50; P 0,04; S 0,05 %), sabit derişimdeki inhibitöre (0,1 M) - 3 değişen der isimlerde NaCİ (1x10 - 1,0 M) eklenerek in celendi. Daha sonraki deneyler ise, farklı derişimlerde NaCİ çözeltilerindeki çukur körozyonunu önlemede, inhi- bitörlerin etkisini ve etkinlik sırasını saptamak ama cıyla yapıldı. Potansiyostatik yöntemle anodik polari zasyon eğrilerinin elde edildiği çalışmaların ilk bölü münde 30 mV/dk; ikinci bölümünde ise, 60 mV/dk potansi yel tarama hızı kullanıldı ve ortam pH'sı, tüm çalışma boyunca, 9,0' da sabit tutuldu. Çalışmaların sonucunda, E ve E, değerlerinin, klorür derişimindeki artışla ÇO KÇO _ daha eksiye kaydıkları ve log (Cl ) ile doğrusal olarak değiştikleri; ayrıca, log (inhibitor) ile log(Cl ) deği şiminin de doğrusal olduğu bulundu ve inhibitor ler in etkinlik sırasının; fosfat > benzoat > asetat > karbonat > sitrat, şeklinde azaldığı belirlendi. II

Özet (Çeviri)

THE DETERMINATION OF THE VALUES OF BREAKDOWN AND PROTECTION POTENTIALS OF PLAIN CARBON STEEL IN SODIUM CHLORIDE MEDIA BY POTENTIOSTATIC METHOD (M.Sc. Thesis) Ahmet Yaşar TURAN GAZI UNIVERSITY INSTITUTE OF SCIENCE AND TECHNOLOGY October 1988 ABSTRACT The breakdown (E,) and the protection (E ) poten tials are very important in characterizing the pitting corrosion. These values were determined on plain carbon steels (Fe 99.30; C 0.10; Mn 0.50; P 0.04; S 0.05 %) in early experiments of this work, by addition of various - 3 concentrations of NaCl (1x10 - 1.0 M) to the constant concentration of inhibitors (0.1 M). Later experiments were carried out to determine the effects of inhibitors on preventing the pitting corrosion in various concentra tions of NaCl solutions. Anodic polarization curves were determined potentiostatically, using 30 mV/min and 60 mV/min potential scanning rates in the first and second series of experiments respectively, while the pH was kept constant at 9.0 all through that, E, and E were shifted to more active values by the increase in the chloride concentration, and the potential versus log(Cl ) curves obtained were linear. The results of second group of experiments revealed out that the log (Cl ) versus log (inhibitor) curves were linear and the most effective inhibitor was found to be phosphate followed by benzoate acetate, carbonate and citrate in the decreasing effecti veness order. Ill

Benzer Tezler

  1. Tez No

    17575

    Düşük karbonlu çeliğin derişik sülfürik asit çözeltileri içinde anodik koruma kriterlerinin belirlenmesi

    The Determination of anodic protection criterions of low carbon steel in concentrated sulfuric acid solutions

    TALİP ERALP ALTINTEN

    Yüksek Lisans

    Türkçe

    Türkçe

    1991

    KimyaGazi Üniversitesi

    DOÇ.DR. HAYRİ YALÇIN

  2. Tez No

    98120

    Bronz ve düşük karbonlu çeliğin sürtünme kaynağı ile birleştirilmesi ve parametrelerinin incelenmesi

    Investigation of joining parameters of bronze to cow carbon steel by friction welding

    ÜMİT PAYLAŞAN

    Yüksek Lisans

    Türkçe

    Türkçe

    2000

    Metalurji MühendisliğiAfyon Kocatepe Üniversitesi

    Metal Eğitimi Ana Bilim Dalı

    DOÇ. DR. ADEM KURT

  3. Tez No

    50930

    Küre grafitli dökme demir ile düşük karbonlu çeliğin difüzyon kaynağı

    Başlık çevirisi yok

    MUSTAFA TAŞKIN

    Yüksek Lisans

    Türkçe

    Türkçe

    1996

    Metalurji MühendisliğiFırat Üniversitesi

    Y.DOÇ.DR. MUSTAFA AKSOY

  4. Tez No

    96979

    Düşük karbon çeliğinin 0.1 M hidroklorik asit çözeltisindeki korozyonuna kuaternar amonyum grubu içeren bileşiklerin inhibitör etkisi

    Inhibition effect of some compounds; having quaternary ammonium groups, on low carbon steel in 0.1 M hydrochloric acid solution

    AYSEL YURT

    Doktora

    Türkçe

    Türkçe

    2000

    KimyaEskişehir Osmangazi Üniversitesi

    Kimya Ana Bilim Dalı

    PROF. DR. GÖZEN BEREKET

  5. Tez No

    7063

    The Corrosion behavior of low-alloy steels in oil well fluids

    Başlık çevirisi yok

    NASSER AHMED FAYAD

    Yüksek Lisans

    İngilizce

    İngilizce

    1989

    Metalurji MühendisliğiOrta Doğu Teknik Üniversitesi

    PROF. DR. MUSTAFA DORUK

Geri Dön