Farklı dental implant abutment materyallerine değişik simanların bağlanma dayanımının incelenmesi
Evaluation of the bonding strengths of different cements for different dental implant abutment materials
- Tez No: 522130
- Danışmanlar: YRD. DOÇ. DR. BİLAL HOLOĞLU
- Tez Türü: Diş Hekimliği Uzmanlık
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Titanyum, zirkonyum, yüzey pürüzlendirme, simantasyon, Dental bonding, Dental implantasyon, Dental implantlar, Dental materyaller, Dental stres analizi, Dental çimentolar, Yüzey pürüzlülüğü, Titanium, zirconium, surface processing, cementation, shear test, Dental bonding, Dental implantation, Dental implants, Dental materials, Dental stress analysis, Dental cements, Surface roughness
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Gaziosmanpaşa Üniversitesi
- Enstitü: Diş Hekimliği Fakültesi
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Farklı Dental İmplant Abutment Materyallerine Değişik Simanların Bağlanma Dayanımının İncelenmesi Amaç: Bu çalışmanın amacı farklı yüzey pürüzlendirme işlemi uygulanan farklı dental implant abutment materyallerine çeşitli simanların bağlanma dayanımının karşılaştırılmasıdır. Gerekçe: Çalışmamızda, Grade 4, Grade 5, zirkonyum materyallerinin her birinden 72 adet olmakla birlikte toplam 216 adet örnekle çalışılmıştır. Her 72 örnek içeren dental implant abutment materyali grubunda 24'er örnek içerecek şekilde pürüzlendirme, kumlama ve kontrol grubu olmak üzere üç yüzey işlemi uygulanmıştır. Yüzey işlemleri uygulandıktan sonra örneklerin SEM görüntüleri alınmıştır. Simantasyon öncesi çalışma modelleri bir kalıp aracılığıyla akril blok içerisine gömülmüş ve sonrasında ultrasonik temizleme işlemi uygulanmıştır. Hazırlanan kompozit örnekler 500 gr' lık sabit kuvvet altında bir düzenek aracılığıyla örneklere simante edilmiştir. Simantasyonun ardından, oda sıcaklığında 24 saat distile su içerisinde bekletilmiştir. Bağlanma dayanımının ölçülmesinde; örneklere kesme kuvveti deneyi uygulanmıştır. Test düzeneğine yerleştirilen örneklere kesme kuvveti başlık hızı 0,5 mm/dk olacak şekilde arayüzden uygulanmıştır ve ayrılmanın gerçekleştiği andaki Newton değeri yüzey alanına bölünerek MPa cinsinden kaydedilmiştir. İstatistiksel değerlendirme; veriler IBM SPSS V23 ile analiz edildi. Verilerin normal dağılıma uygunluğu Shapiro Wilk testi ile incelendi. Normallik koşulu sağlandıktan sonra materyal, yüzey işlemi ve siman faktörlerine göre bağlanma dayanımı üzerindeki etkileri univariate ANOVA ile incelendi. Analiz sonuçları ortalama ± standart sapma olarak sunuldu. Anlamlılık düzeyi p<0,05 olarak alındı. Bulgular: Materyal ana etkisi bağlanma dayanımı üzerinde istatistiksel olarak anlamlı bulunmuştur (p=0,027). Grade 4 ve Grade 5 titanyumlar arasında istatistiksel olarak bir fark bulundu( Grade 4 Titanyum için 5,81 ± 3,39 ve Grade 5 Titanyum içinde 5,60 ± 3,38), zirkonyumun ortalama değeri ise diğerlerinden farklı değildir(5,67 ± 3,39). Simanların ana etkileri bağlanma değerleri üzerinde anlamlı bir etkiye sahiptir (p<0,001). En düşük ortalama değer implant simanda(4,42 ± 2,97) elde edilirken en yüksek ortalama değer rezin simanda(7,78 ± 3,17) elde edilmiştir. Materyal ve yüzey işlemi etkileşimi istatistiksel olarak anlamlı bulunmamıştır (p=1,00). Benzer şekilde materyal*siman ve yüzey işlemi*siman etkileşimleri de istatistiksel olarak anlamlı değildir (p değerleri sırasıyla 0,999 ve 0,297). Materyal, yüzey işlemi ve siman'a ait 3'lü etkileşimlerde bağlanma dayanımları üzerinde anlamlı bir etkiye sahip değillerdir (p=1,000). iv Sonuçlar: En yüksek bağlanma dayanımının rezin simana ait olduğu görüldü, bunu polikarboksilat siman takip etti, en zayıf bağlanma dayanımının ise implant simanında olduğu görüldü. En düşük bağlanma dayanımı tüm örneklerde yüzey işlemi uygulanmayan kontrol gruplarında saptanmıştır, en yüksek bağlanmanın frezle pürüzlendirilen grupta olduğu görüldü. SEM görüntüleri incelendiğinde en pürüzlü yüzeylerin frezle pürüzlendirilen örneklere ait olduğu görüldü ve bunu kumlama ile pürüzlendirilen örnekler takip etti. Geçici simantasyon amacıyla kullanılan implant simanlarının bağlanma dayanımı, abutment yüzeylerine uygulanan pürüzlendirme işlemlerinden etkilenmektedir. Farklı abutment materyalleri kullanılması bu sonucu değiştirmemektedir.
Özet (Çeviri)
Evaluation Of The Bonding Strengths Of Different Cements For Different Dental Implant Abutment Materials Aim: The purpose of this study is to compare the bonding strengths of various cements on different dental implant abutment materials which were subjected to different surface treatment processes. Method: In our study, Grade 4, Grade 5 titanium materials and zirconium materials, 72 pieces of each, totally 216 samples were studied. Each abutment material group which consisted of 72 samples, were divided into three subgroups (24 samples each) according to used surface treatment techniques; roughing group, sand blasting group and non-treated group. After the surfaces of the samples were treated, scanning electron microscopic (SEM) views of abutment materials were obtained. Before luting, the abutment samples were embedded in acrylic blocks via using a mould and then the cleaning process was carried out with ultrasonic method. The prepared composite samples were cemented to surface treated abutment samples by a device which using 500 gr press force. After cementation, the samples were kept at room temperature, in distilled water for 24 hours. For bonding strength measurement, shear force test was applied to the samples. For the samples placed in the test set, the shear force was applied at the interface such that the head speed was 0.5 mm/minute, and the Newton value, which was obtained at the time of separation, was divided by surface area and was recorded in MPa. For statistical evaluation, obtained data were analysed by IBM SPSS V23 Programme. Normal distribution of the data was examined by Shapiro Wilk test. After the condition of normality was established, the effects on bond strength according to material, surface treatment and cementing factors were examined by univariate ANOVA test. Analysis results were presented as mean ± standard deviation. The significance level was p<0.05. Results: Material's main effect on bonding strength was statistically significant. (p=0.027) There was a statistically significant difference between Grade 4 and Grade 5 titanium abutment materials (for Grade 4 titanium material 5.81±3.39 and for Grade 5 titanium material 5.60± 3.38), but the average value of zirconium material did not differ from the others (5.67±3.39). Cements' main effects had a significant impact on bonding strengths (p<0.001). The dental implant cement had the lowest average value (4.42± 2.97) but the resin cement had the highest average value (7.78± 3.17). There was no significant relation between the abutment materials and the surface treatment techniques (p=1.00). Similarly, the interactions between the abutment materials and cements, vi surface treatment techniques and cements were not statistically significant. (p values were 0.999 and 0.297, respectively) The triple interactions between the abutment materials, the surface treatment techniques and the cement materials had not significant impacts on the bonding strengths. (p=1.000) Conclusion: As concluded, according to our study's findings the highest bonding strength was detected with resin cement material which was followed by the polycarboxylate cement material and the lowest bonding strength was detected with the implant cement material. By the surface treatment techniques' perspective, the highest bonding strength values were detected with roughened abutment surfaces (roughened by drills) and the lowest bonding strength values were detected in control (non-treated) abutment surfaces. When SEM views were evaluated, the most roughened surfaces were seen on abutment samples which were roughened by drills and drill-roughened abutment samples were followed by sand blasted abutment samples' surfaces. The bonding strength of implant cement, the cement materials which are used for provisional cementation, is affected by the roughening treatments applied to the abutment surfaces. The use of different abutment materials does not alter this result.
Benzer Tezler
- Dental implantlarda internal bağlantı sistemlerinin ölçüsel ve açısal değerlerinin, değişik yönlü kuvvetler altındaki kırılma dirençlerinin karşılaştırmalı olarak ölçülmesi
Comparative measurement of the fracture resistance of the measuremental and angular values of the internal junction systems in dental implants under forces of different directions
ÖZGE ÖZDAL ZİNCİR
Doktora
Türkçe
2015
Diş Hekimliğiİstanbul ÜniversitesiAğız, Diş ve Çene Cerrahisi Ana Bilim Dalı
PROF. MERAL ÜNÜR
- Maksiller anterior tek diş implant destekli protezlerde farklı abutment materyallerinin değişik açılarda kullanımının oluşturduğu streslerin sonlu elemanlar analizi metoduyla incelenmesi
Investigation of the stress caused on implant, on surrounding tissues, on abutment and on prothesis by the use of different abutment materials in different angles in single maxillary anteryor implant supported prosthesis with finite elements analysis.
SAİD MİRZA KIZMAZ
Doktora
Türkçe
2019
Diş HekimliğiDicle ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. KÖKSAL BEYDEMİR
- Ön bölge tek diş implantlarında farklı abutmant materyallerinin estetiğe etkisinin karşılaştırılması
An esthetic comparison of different abutment materials in anterior single-tooth areas
ARZU ARZUMAN
Doktora
Türkçe
2009
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
YRD. DOÇ. DR. BİLGE GÖKÇEN RÖHLİG
- Maksiller anterior tek diş implant destekli protezlerde değişik açı ve bağlantı tipleri ile kullanılan platform açılı implant ve farklı abutment materyallerinin oluşturduğu stres dağılımının üç boyutlu sonlu elemanlar analizi ile değerlendirilmesi
Evaluation of the stress distribution in maxillary anterior single unit implant supported prosthetics with different angle and connection types using platform angled implants and different abutment materials by three dimensional finite element analysis
GİZEM ŞAHİN
Diş Hekimliği Uzmanlık
Türkçe
2022
Diş HekimliğiSelçuk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. MÜNİR TOLGA YÜCEL
- Farklı implant desteklerinde değişik teknik ve materyallerle hazırlanan alt yapıların kenar uyumunun karşılaştırmalı olarak incelenmesi
A comparative study of marginal fit of copings which was prepared with various techniques and materials' on different abutments
ESRA KOÇ