Kompozit levhaya nano partikül katkısının mekanik ve burkulma özelliklerine etkisinin deneysel olarak araştırılması
Experimental study on the effect of composite plastic nano particleine composition on mechanical and various characteristics
- Tez No: 521551
- Danışmanlar: DR. YASİN YILMAZ
- Tez Türü: Yüksek Lisans
- Konular: Makine Mühendisliği, Mechanical Engineering
- Anahtar Kelimeler: Cam elyaf kompozitler, Cam elyafı, Composite material, Carbon nanotube, Waste tyre char, Mechanical properties, Characterization, Glass fiber composites, Fiberglass
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Pamukkale Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Makine Mühendisliği Ana Bilim Dalı
- Bilim Dalı: Mekanik Bilim Dalı
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu tez çalıĢmasında katkısız, % 0,1;0,2;0,3;0,5;1;2 oranlarında karbon nanotüp (CNT) katkılı ve % 0,1;0,2;0,3;0,5;1;2 oranlarında atık lastiğin kimyasal bozundurmasıyla elde edilmiĢ olan karbon esaslı katkı maddesi(KEKM) eklenerek güçlendirilmiĢ cam elyaf takviyeli kompozit malzemelerin mekanik özellikleri ve burkulma davranıĢları araĢtırılmıĢtır. ÇalıĢma kompozit malzemelerin üretilmesi ve üretilen malzemelerin mekanik, morfolojik ve fonksiyonel özelliklerinin belirlenmesi olmak üzere iki aĢamadan oluĢmuĢtur. Mekanik özelliklerin belirlenmesi için çekme ve burkulma deneyleri gerçekleĢtirilmiĢtir ve elde edilen sonuçlar karĢılaĢtırılmıĢtır. Belirlenen en uygun katkı oranlı numunelere ve katkısız numuneye fonksiyonel yapısını belirlemek için FT-IR ve morfolojik yapısını belirlemek için SEM analizleri gerçekleĢtirilmiĢtir. Çekme deneyleri sonucunda çekme yükü, çekme gerilmesi ve elastisite modülü verileri incelendiğinde kompozit numune için %0,5 KNT oranının en uygun olduğu görülmüĢtür. Ancak KEKM'nin kullanıldığı kompozit numunelerde ise analiz değerlerinin katkısız numuneye göre arttığı belirlenmiĢtir, fakat belirgin bir değiĢiklik gözlenmemiĢtir. Burkulma deneyleri sonunda kritik burkulma kuvveti ve kritik burkulma gerilmesi sonuçları incelendiğinde kompozit numune için % 0,3 KNT oranının en uygun olduğu belirlenmiĢtir. Ancak KEKM içeren kompozit malzemelerin analiz sonuçlarının düzensiz olduğu gözlenmiĢtir. Sonuç olarak, her iki katkı maddesinin kompozit malzemenin mukavemetini artırdığı belirlenmiĢtir. Atık lastiğin kimyasal bozundurmasıyla elde edilmiĢ olan KEKM'in kompozit malzeme hazırlanma aĢamasında epoksi içersinde topaklanarak homojen dağılmamasından dolayı epoksi ile bağ kuramamaktadır ve bu sonuç FT-IR analizleri ile desteklenmiĢtir. ANAHTAR KELĠMELER: Kompozit malzeme, Karbon nanotüp, Atık lastik çarı, Mekanik özellikler, Karakterizasyon
Özet (Çeviri)
In this thesis the mechanical properties and buckling behavior of glass fiber reinforced composite materials was studied as add different ratios (0.1;0.2;0.3;0.5;1;2) of carbon based additive (CBA) obtained from chemical degradation of waste tyre and different ratios (0.1;0.2;0.3;0.5;1;2) carbon nanotube (CNT), additive-free. The study consisted of two stage; 1) production of composite materials and 2) determination of mechanical, morphological and functional properties of produced materials. Tension and buckling tests were carried out to determine the mechanical properties and the obtained results were compared. SEM and FT-IR analyses were characterized to determined morphological and functional of additive-free sample and the most appropriate additive ratio samples. It was determined to be the most appropriate ratio of 0.5 % CNT for composite sample when analyzed tensile load, tensile stress and elastic modulus datas according to tension test. However, it was determined increase of results in composite samples used of CBA to compared with the additive-free sample, but no significant change was observed. It was determined to be the most appropriate ratio of 0.3 % CNT for composite sample when analyzed critical buckling force and critical buckling stress according to buckling tests. Yet, it was observed be irregular of results of composite materials containing CBA. As a result, the both additives were found to increase the strength of the composite material. CBA obtained from chemical degradation of waste tyre couldn't chemical bond by epoxy because it is not homogenously dispersed within epoxy during the preparation of composite materials and this result was supported by FT-IR analyzes.
Benzer Tezler
- Design and implementation of origami inspired miniature parallel mechanisms
Origamiden esinlenilmiş minyatür paralel mekanizmaların tasarımı ve uygulaması
HASAN SEVİNÇ
Yüksek Lisans
İngilizce
2020
Makine Mühendisliğiİstanbul Teknik ÜniversitesiMekatronik Mühendisliği Ana Bilim Dalı
DR. ÖĞR. ÜYESİ ATAKAN ALTINKAYNAK
ÖĞR. GÖR. MERVE ACER KALAFAT
- Nanoteknolojik ürünlerle modifiye edilen FF ve MUF tutkallarının ahşap kompozit malzemelerin fiziksel ve mekanik özelliklerine etkisi
Effects of PF and MUF adhesive modified with nanotechnology products on physical and mechanical proporties of wood composites
MEHMET ERDAL KARA
Doktora
Türkçe
2018
Ağaç İşleriKarabük ÜniversitesiOrman Endüstri Mühendisliği Ana Bilim Dalı
PROF. DR. AYHAN ÖZÇİFÇİ
- Tabakalı kompozit levhalarda düşük hızlı darbe etkisinin sayısal analizi
Numerical analysis of effect of low velocity impact on laminated composite plates
MUSTAFA ALBAYRAK
Yüksek Lisans
Türkçe
2013
Makine MühendisliğiFırat ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
YRD. DOÇ. DR. MUSTAFA GÜR
- Katmanlı kompozit panellerin dövünme basınç yüküne cevabı
Response of laminated composite panels subjected to slamming load
ÖMER EKSİK
- Yeni bir yaklaşımla partikül takviyeli fonksiyonel derecelendirilmiş hibrit özellikli tabakalı kompozit üretimi ve sürtünme karıştırma kaynağı ile birleştirilmesinin incelenmesi
A new approach to particle-reinforced functional graduated hybrid characterized layer composite production and investigation of joining with friction stir welding
UĞUR AVCI
Doktora
Türkçe
2019
Makine Mühendisliğiİnönü ÜniversitesiMakine Mühendisliği Ana Bilim Dalı
PROF. DR. ŞEMSETTİN TEMİZ