Monolitik zirkonyumun farklı dental materyaller ve mine karşısında meydana getirdiği aşınmanın değerlendirilmesi
Wear evaluation of different dental materials and enamel opposing monolithic zirconia
- Tez No: 516996
- Danışmanlar: DOÇ. DR. COŞKUN YILDIZ
- Tez Türü: Doktora
- Konular: Diş Hekimliği, Dentistry
- Anahtar Kelimeler: Benzetim, Dental materyaller, Dental mine, Dental mine erirliği, Diş aşınması, Zirkonyum, Çiğneme, Simulation, Dental materials, Dental enamel, Dental enamel solubility, Tooth abrasion, Zirconium, Mastication
- Yıl: 2018
- Dil: Türkçe
- Üniversite: Marmara Üniversitesi
- Enstitü: Sağlık Bilimleri Enstitüsü
- Ana Bilim Dalı: Protetik Diş Tedavisi Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Amaç: Dinamik yükleme sonrası monolitik zirkonya materyalinde ve karşıt arkında kullanılabilecek farklı dental restoratif materyallerde meydana gelecek aşınma miktarının belirlenmesidir. Gereç ve yöntem: Çalışmamızda 7 mm/7 mm boyutlarında ve 3 mm kalınlığında 90 adet LAVA monolitik zirkonya (50 adet glazelenmiş ve 40 adet cilalanmış), 20 adet premolar diş, hemisfer formunda çapı 5 mm yüksekliği 10 mm olacak şekilde 20 adet feldspatik porselen, 20 adet lityum disilikat seramik (IPS e.max Press), 20 adet kompozit (Herculite) ve 20 adet monolitik zirkonya (Lava Monolithic) örnekler hazırlandı. Üç boyutlu lazer tarayıcı ile çiğneme simülasyonu öncesi yüzey tarama işlemleri yapıldı. Örnekler dual akslı çiğneme simülatörü (50 N'luk yük, 5-55 °C ısı döngüsü) ile 1 yıllık klinik kullanıma eşdeğer olan 240 000 döngü çiğneme döngüsüne tabii tutuldu. Simülasyon sonrası yüzey tarama işlemleri tekrar yapılıp, elde edilen veriler çakıştırılarak meydana gelen aşınma miktarları belirlendi. İstatistiksel analiz için Independent Samples t, Kruskal Wallis ve Mann Whitney U testleri kullanılmıştır. Bulgular: Antagonist aşınması cilalanmış zirkonya örneklerde (0,071±0,061 mm3) glazelenmiş zirkonya örneklere (0,109±0,084 mm3) kıyasla daha düşük bulunmuştur. Antagonist materyaller arasında en az aşınma glazelenmiş zirkonya karşısındaki cilalanmış zirkonya örneklerde (0,015±0,015 mm3) ve en fazla aşınma ise glazelenmiş zirkonya karşısında mine örneklerinde (0,097±0,075 mm3) görülmüştür. Sonuçlar: Cilalanmış yüzeyli monolitik zirkonya restorasyonların kullanılması, karşıt arkda meydana gelebilecek aşınma miktarının azaltılması açısından önerilmektedir. Yaptığımız bu in vitro çalışma sonuçları, ileride yapılacak in vivo ve in vitro çalışmalara ışık tutacaktır.
Özet (Çeviri)
Purpose: Determination of the amount of wear that will occur in monolithic zirconia and different dental restorative materials that can be used against it after dynamic loading. Materials and Methods: In our study, 7mm/7mm in size and 3mm in thickness 90 LAVA monolithic zirconia (50 glazed, 40 polished), 20 premolars, in the form of hemisphere 5mm diameter and 10mm in height 20 feldspathic porcelain, 20 lithium disilicate ceramic (IPS e-max Press), 20 composite (Herculite) and 20 monolithic zirconia (Lava Monolithic) samples were prepared. A three-dimensional laser scanner was used to perform surface scanning before simulation. The samples were subjected to a 240 000 chewing cycle with dual-axis chewing simulator (load 50 N, heat cycle 5-55 °C), equivalent to 1 year of clinical use. After the simulation, the surface scans were repeated and the obtained data were superimposed to determine the amount of wear. Independent Samples t, Kruskal Wallis and Mann Whitney U tests were used for statistical analysis. Results: Antagonist wear was found in polished zirconia samples (0,071±0,061 mm3) lower than in glazed zirconia samples (0,109±0,084 mm3). Among the antagonist materials, polished zirconia (0,015±0,015 mm3) against glazed zirconia (0,015±0,015 mm3) shows the least wear and maximal wear was observed in enamel specimens (0,097±0,075 mm3) against glazed zirconia. Conclusion: The use of polished monolithic zirconia restorations is suggested for reducing the amount of wear that can occur in the opposite arc. We are thinking that the results of this in vitro study will illuminate future in vivo and in vitro studies.
Benzer Tezler
- Farklı dental porselen sistemlerinin aşınma ve renk değişimlerinin araştırılması
Investigation of the wear and color changes of different dental porcelain
MEHMET ÇAĞATAY ULUCAN
Diş Hekimliği Uzmanlık
Türkçe
2017
Diş HekimliğiCumhuriyet ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. GİRAY BOLAYIR
- Farklı yttrium içerikli monolitik zirkonya materyalinin mine ve dentin üzerindeki aşınma etkisinin incelenmesi
Wear evaluation of monolithic zirconia material with different Yttrium amounts on enamel and dentin
MİRAY KAYA ACAR
Diş Hekimliği Uzmanlık
Türkçe
2023
Diş HekimliğiKocaeli ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. AYŞE KOÇAK BÜYÜKDERE
- Aşırı harabiyete uğramış kanal tedavisi görmüş dişlerde geleneksel yöntemle hazırlanan ve güncel yöntemlerle zirkonyum dioksit içerikli hazırlanan; Sabit protezlerle restore edilmiş farklı mil-çekirdek sistemlerinin karşılaştırılması
Comparision between post and core systems restored with traditional and uptodate zirconium dioxide restorati̇on in endodontically treated teeth
MAHMUT ÖMER
Doktora
Türkçe
2017
Diş Hekimliğiİstanbul ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. GÜLÜMSER EVLİOĞLU
- Monolitik zirkonyuma uygulanan yüzey işlemleri ile yaşlandırmanın pürüzlülük ve dönüşümüne etkisinin incelenmesi
İnvestigation of the effect of surface treatment and aging on roughnessn and phase transformation of monolithic zirconium
FIRAS SULEYMAN
Doktora
Türkçe
2019
Diş HekimliğiAtatürk ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
PROF. DR. ZEYNEP YEŞİL DUYMUŞ
- Farklı translusenslikteki monolitik zirkonyumun renk ve translusensliğine kalınlığın ve rezin siman renginin etkisinin değerlendirilmesi
Evaluation of the effect of thickness and resin cement color on color and translucency of monolithic zirconium with different translucency
BERKAY BOZCA
Diş Hekimliği Uzmanlık
Türkçe
2021
Diş HekimliğiRecep Tayyip Erdoğan ÜniversitesiProtetik Diş Tedavisi Ana Bilim Dalı
DOÇ. DR. MURAT ALKURT