Polivinil alkol katkılı lifli betonların özellikleri ve kullanılabilirliğinin araştırılması
Başlık çevirisi mevcut değil.
- Tez No: 50906
- Danışmanlar: Y.DOÇ.DR. M. ŞÜKRÜ YILDIRIM
- Tez Türü: Yüksek Lisans
- Konular: İnşaat Mühendisliği, Civil Engineering
- Anahtar Kelimeler: Lifli beton, akrilik lifler, polMnil alkol, poliakrilonitril, çekme gerilmesi, eğilme gerilmesi (mukavemeti), çarpma direnci, lifli takviye, Beton, Polivinil alkol, Çimento, Fibre concrete, acrylic fibres, polyvinyl alcohol (PVAL), polyacrylonitrile, tensile strength, flexural strength, impact resistance, fibre reinforcement, Concrete, Polyvinyl alcohol, Cement
- Yıl: 1996
- Dil: Türkçe
- Üniversite: Fırat Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Belirtilmemiş.
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
ÖZET Yüksek Lisans Tezi POLİVİNİL ALKOL KATKILI LİFÜ BETONLARIN ÖZELLİKLERİ VE KULLANİLABİRLİ?İNİN ARAŞTIRILMASI Yüksel ESEN Fırat Üniversitesi Fen Bilimleri Enstitüsü İnşaat Mühendisliği Anabilim Dalı 1996, Sayfa:79 Bu çalışmada, çimento hamuru bileşiklerinin mekaniksel özelliklerinde, Poliakrilonitril liflerinin etkisi araştırılmaktadır. Poliakrilonitıil lifinin çimeno hamuru matrisine ilavesi, bileşiğin; eğilme, çekmeye çarpma özelliklerinde önemli bir düzelme meydana getirir, örneğin Portland Çimentosu hamurunda, bu öp lifin varlığı çarpma direncini 40-500 defaya kadar düzelttiği ayrıca lifin %4 ilavesi ile eğilme direncinin, saf hamura göre aynı şartlarda %386 civarında bir artmaya neden olduğu gözlendi. Tek ekenli çekme gerilmesi deneyleri Eksenel Çekme Tekniği kullanılarak yapıldı. Çfrnento matrisine Poliakrilonitril liflerinin % 1,2,3 ve 4 ilavesi, eksenel çekme gerilmesinde sırasıyla %21, 46, 85, ve 103'likbir artma meydana getirir. Bileşiğin epme mukavemetindeki artma, tek eksenli çekme mukavemet" ile karşılaştırıldığı zaman daha önemlidir. Çimento matrisinin eğilme gerilmesi, liflerin % 1,2,3 ve 4 ilavesiyle sırasına göre %157, 243, 334 ve 386 kadar arttı. Eğilmedeki güvenirliliğin lif ilavesi ile arttığı ve bileşiğin güvenirliliği ile % lif ilavesi arasında bir ilişki olmadığı görüldü. Bununla beraber, Poliakrilonitril lifleri ile güçlendirilmiş bileşiğin; eğilme, çekme ve çarpma özellikleri önemli bir şekilde düzeldi.
Özet (Çeviri)
u SUMMARY Masters Thesis Properties of Polyvinyl Alcohol - Fiber Reinforced Concretes and Research of Theirs Availability Yüksel ESEN Fırat University Graduate School Natural and Applied Science <t *j Department of Civil Engineering t<, 3 1996, Page: 79 ^c£r- in this study, the effect of Polyacrylonitrile filers on the mechanical properties of cement paste composites was studied. The addition of Polyacrylonitrile fiber to the cementitious paste matrix results in a significant improvement in the tensile, flexural and impact properties of the composites. For instance, in pastes of Portland cement, tt has been provided that the presence of this type of fibre improves their impact resistance up to around 40 - 500 times whereas flexural resistances for a 4% wt. of addition of long fibres have an increase, with respect to those obtained for pure paste, of around 386% in same cases. The uniaxial tensile strength results are obtained using the uniaxial tensile technique.The addition of 1, 2, 3 and 4% wt. of Polyacrylonitrile fiber to a cement matrix results in an increase in the uniaxial tensile strength of 21, 46, 85 and 103% respectively. The enhancement of the composite flexural strength was more significant, as compared to the uniaxial tensile strength. The flexural strength of cement matrix increased by 157, 243, 334 and 386% with the addition of 1, 2, 3 and 4% wt. of this fiber, respectively. it was seen that, reliability in flexural increased by fiber addition and there was no correlation between the percent fiber loading and the reliability of the composites. However, the Polyacrylonrtrile - fiber - reinforced composite in tension, flexural and impact properties was greatly improved.
Benzer Tezler
- Polivinil alkol membran kullanılarak asetik asit-su karışımlarının pervaporasyon ile ayrılması
Separation of acetic acid-water mixtures by pervaporation in which polyvinyl alcohol membranes are used
SELÇUK SAKAOĞLU
Yüksek Lisans
Türkçe
1999
Kimya Mühendisliğiİstanbul Teknik ÜniversitesiKimya Mühendisliği Ana Bilim Dalı
PROF. DR. SEMA TÜLBENTÇİ
- Surface modified polyvinyl alchol membranes for water ethanol seperation via pervaporation
Yüzeyi modifiye edilmiş polivinil alkol membranlarının pervaporasyon yöntemiyle su-etanol ayırımının kullanılması
PINAR AKÇORA
- Kaolinit dispersiyonunun reolojik ve dielektrik özelliklerine polivinil alkol (PVA) etkisi
The effect of polyvinyl alcohol (PVA) on rheological and dielectric properties of kaolinite dispersion
İDRİS SORAR
Yüksek Lisans
Türkçe
1999
Fizik ve Fizik MühendisliğiCelal Bayar ÜniversitesiFizik Ana Bilim Dalı
DOÇ. DR. NURDOĞAN CAN
- Poli (vinil alkol)-akrolik asit, poli(vinil alkol)-akrilamid aşı kopolimerlerinin sentezi, deriştirilme işlemlerinde kullanılması
Synthesis of poly (vinyl alcohol)-acrylic acid, poly (vinyl alcohol)-acrylamide copolymers and their use in concentrating processes
CEMAL ERTAŞ
- Sulu poli (vinil alkol) ve poli (n-vinil pirrolidon ) çözeltilerinde, potasyum klorür iletkenliğinin, iç (lokal) viskozitenin ve assosiyasyonun incelenmesi
The Study of potassium chloride conductivity and viscosity and association of solutions in aqueous PVA and PVP
AYSUN ÜNLÜ