Structural characterization, tensile strength, thermal and electrical conductivities of Al-0.25Zr and Al-0.25Zr-0.1Nb alloys
Al-0.25Zr ve Al-0.25Zr-0.1Nb alaşımlarının yapısal karakterizasyonu, çekme mukavemeti, ısısal ve elektriksel iletkenlikleri
- Tez No: 507342
- Danışmanlar: PROF. DR. MEHMET GÜNDÜZ
- Tez Türü: Yüksek Lisans
- Konular: Fizik ve Fizik Mühendisliği, Physics and Physics Engineering
- Anahtar Kelimeler: Mikroyapı, Al-Zr alaşımı, Al-Zr-Nb alaşımı, çekme mukavemeti, ısısal iletkenlik, elektriksel direnç, elektriksel iletkenlik, Microstructure, Al-Zr alloy, Al-Zr-Nb alloy, tensile strength, thermal conductivity, electrical resistivity, electrical conductivity
- Yıl: 2018
- Dil: İngilizce
- Üniversite: Erciyes Üniversitesi
- Enstitü: Fen Bilimleri Enstitüsü
- Ana Bilim Dalı: Fizik Ana Bilim Dalı
- Bilim Dalı: Belirtilmemiş.
- Sayfa Sayısı: Belirtilmemiş.
Özet
Bu çalışmada, doğrusal olarak katılaştırılmış Al-0.25%Zr ve Al-0.25%Zr-0.1%Nb alaşımlarının mikroyapıları ve ayrıca çekme mukavemeti, ısısal ve elektriksel iletkenlikleri incelenmiştir. Aşırısoğumalar, çekirdeklenmeler, katılaştırmalar, dendritic büyütmeler, çekme mukavemeti, ısısal ve elektriksel iletkenlikleri ile ilgili temel kavramlar birinci bölümdetartışılmıştır. Mikroyapı parametreleri ile katılaştırma parametreleri arasındaki ilişkikler, çekme mukavemeti, ısısal ve elektriksel iletkenlik ile ilgili önemli teorik ve deneysel çalışmalar ikinci bölümde irdelenmiştir. Al aşımlarında katılaştırma hızı, V, ile mikroyapı parametreleri arasındaki ilişkikleri incelemek için numuneler faklı hızlarda ve sabit sıcaklık gradyentinde Bridgman tipi deney sisteminde doğrusal olarak katılaştırılmıştır. Çekme mukavemeti test numuneleri ise sıcak döküm fırınında alaşımların alttan yukarı doğru serbest katılastırma tekniği ile katılaştırılarak elde edilmiştir. Al aşımlarının katı fazlarının ısısal iletkenlikleri, erime sıcaklıklarının 10 0C altına kadar radial ısı akış fırınında ölçülmüştür. Numunelerin cıcaklık dağılımı 0.5 mm'lik mineral yalıtımlı K- tipi 5 ısıl çift ile deney süresince, akım ve potansiyel farkları ise aralıklar ile kaydedilmiştir. Al aşımların elektriksel iletkenlikleri ise dört-nokta metodu ile oda sıcaklığı-3000C aralığında ölçülmüştür. Özetolarak; alaşımlarının mikroyapılarının (hücrelerin birincil kollar arası mesafelerinin) artan büyütme hızı ile azaldığı,Al-Zr alaşımına Nb elementini ilave edilmesi yeni alaşımın çekme mukavemetinin artmasına sebep olduğu, her iki alaşımın da ısısal ve elektiriksel iletkenliklerinin artan sıcaklık ile azaldığı görülmüştür.
Özet (Çeviri)
This work was undertaken to characterize microstructures of directly solidified Al-0.25wt%Zr and Al-0.25wt% Zr-0.10wt% Nb alloys and also to investigate the tensile strength, thermal conductivity and electrical conductivity of the alloys. Basic concepts about undercooling, nucleation, solidification, dendritic growth, tensile strength, thermal and electrical conductivity have been discussed in chapter one. Theoretical and experimental studies on the relationships between solidification processing parameters on microstructure parameters, tensile strength, thermal and electrical conductivity were presented in chapter two. In order to investigate the effect of growth rates, V, on microstructures, the alloys were directionally solidified with different V at a constant temperature gradient in a Bridgman type apparatus. The tensile strength samples were prepared by cooling the alloys from bottom to top with the free growth technique by using a hot filling furnace. The thermal conductivity of the alloys was measured with the radial heat flow apparatus for the solid phases up to 10 oC below the melting temperature of the alloys. Temperature distribution was recorded with five K-type 0.5 mm insulated thermocouples during the run, and also the current and potential differences were recorded with intervals. Electrical resistivity (i.e conductivity) of the alloys was also measured from room temperature to 300 oC by using a four- point probe method. In summary it was found that the microstructures, (primary cell spacing), of the alloys decrease with increasing growth rates. Addition of Nb element into the Al-Zr alloy causes to increase the tensile strength of the new alloy. The thermal and electrical conductivities of the alloys decreased with increasing temperatures.
Benzer Tezler
- Structural and mechanical characterization of hybrid nanocomposite material
Hibrit nanokompozit malzemenin yapısal ve mekanik karakterizasyonu
HALA MAHMOOD KADHIM AL-ZUBAIDI
Yüksek Lisans
İngilizce
2017
Makine MühendisliğiTürk Hava Kurumu ÜniversitesiMakine ve Uçak Mühendisliği Ana Bilim Dalı
DOÇ. DR. MURAT DEMİRAL
- Structural and mechanical characterization of scale-up FeCoCrNi, FeCoCrNiCux ve FeCoCrNiAlx high entropy alloys (HEAs)
Büyük ölçekli FeCoCrNi, FeCoCrNiCux ve FeCoCrNiAlx yüksek entropili alaşımların (Yea'ların) yapısal ve mekanik karakterizasyonu
ZİYA ANIL ERDAL
Yüksek Lisans
İngilizce
2020
Metalurji MühendisliğiOrta Doğu Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
DOÇ. DR. YUNUS EREN KALAY
- Development and characterization of thermal and structural properties of textile fibers
Tekstil elyafın termal ve yapısal özelliklerinin geliştirilmesi ve karakterize edilmesi
MD MAHBUBOR RAHMAN
Doktora
İngilizce
2021
Tekstil ve Tekstil MühendisliğiErciyes ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
PROF. DR. İSMAİL KARACAN
- Rüzgar türbini pervane göbeği üretimi ve yapısal özelliklerinin belirlenmesi
Production and structural characterization of wind turbine rotor hub
ÇAĞLAR YÜKSEL
Yüksek Lisans
Türkçe
2011
Metalurji MühendisliğiYıldız Teknik ÜniversitesiMetalurji ve Malzeme Mühendisliği Ana Bilim Dalı
PROF. DR. AHMET EKERİM
- Poli(hekzametilen adipamit) (Poliamid 66) esaslı karbon lifi üretimi sırasında antioksidan kullanımının termal stabilizasyon ve karbonizasyon aşamalarına etkilerinin araştırılması, yapısal ve mekanik özelliklerin karakterize edilmesi
The investigation of the effects of the use of antioxidant during the fabrication of poly(hexamethylene adipamide) (Polyamide 66) based-carbon fiber on the thermal stabilization and carbonization stages and characterization of structural and mechanical properties
LEVENT ERZURUMLUOĞLU
Yüksek Lisans
Türkçe
2015
Tekstil ve Tekstil MühendisliğiErciyes ÜniversitesiTekstil Mühendisliği Ana Bilim Dalı
PROF. DR. İSMAİL KARACAN